Dual metallocene catalyst for producing film resins with good machine direction (MD) elmendorf tear strength

ABSTRACT

This invention relates to catalyst compositions comprising a first metallocene compound, a second metallocene compound, at least one chemically-treated solid oxide, and at least one organoaluminum compound. This invention also relates to methods to prepare and use the catalyst compositions and new polyolefins. The compositions and methods disclosed herein provide ethylene polymers and copolymers with lower MI, increased melt strength, and good MD tear properties.

TECHNICAL FIELD OF THE INVENTION

This invention relates to the field of olefin polymerization catalysis,catalyst compositions, methods for the polymerization andcopolymerization of olefins, polyolefins, and film resins, particularlyusing a supported catalyst composition.

BACKGROUND OF THE INVENTION

It is known that mono-1-olefins (α-olefins), including ethylene, can bepolymerized with catalyst compositions employing titanium, zirconium,vanadium, chromium, or other metals, often combined with a solid oxideand in the presence of cocatalysts. These catalyst compositions may beuseful for both homopolymerization of ethylene, as well ascopolymerization of ethylene with comonomers such as propylene,1-butene, 1-hexene, or other higher α-olefins. Therefore, there exists aconstant search to develop new olefin polymerization catalysts, catalystactivation processes, and methods of making and using catalysts, thatwill provide enhanced catalytic activities and polymeric materialstailored to specific end uses.

One type of transition metal-based catalyst system comprises metallocenecompounds, which have shown promise in tailoring polymer properties.However, there remain significant challenges in developing catalyststhat can provide custom-made polymers with a specific set of desiredproperties. Further, it is of interest to develop metallocene-basedcatalytic systems that can be activated with activating agents that donot require relatively expensive methylaluminoxane, yet still providerelatively high polymerization activities.

What are needed are new catalyst compositions and methods of making thecatalyst compositions that afford high polymerization activities, andwill allow polymer properties to be maintained within the desiredspecification ranges.

SUMMARY OF THE INVENTION

This invention encompasses catalyst compositions, methods for preparingcatalyst compositions, methods for polymerizing olefins, ethylenepolymers and copolymers, and films. In the course of examiningmetallocene-based olefin polymerization catalysts, it was discoveredthat a dual metallocene catalyst system provided a useful combination ofpolyolefin properties, such as melt index, haze, MD tear, and the like,while maintaining sufficient melt strength so the resin is suitable forblowing film.

In one aspect, the present invention encompasses a composition of mattercomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. In another aspect, this invention encompasses acatalyst composition, a catalyst composition for polymerizing olefins, amethod of preparing a catalyst composition, a method of using a catalystcomposition, and the like, in each case encompassing a first metallocenecompound, a second metallocene compound, at least one chemically-treatedsolid oxide, and at least one organoaluminum compound.

In one aspect, the present invention comprises a dual metallocenecatalyst composition, wherein the first metallocene compound cancomprise a bis(monosubstituted cycloalkadienyl) zirconium complex; thesecond metallocene can comprise a bis(disubstituted cycloalkadienyl)zirconium complex or a similar metallocene compound more highlysubstituted than the first metallocene compound, a chemically-treatedsolid oxide component; and an organoaluminum compound. In still anotheraspect of this invention, the second metallocene compound can comprise aloosely-bridged ansa-metallocene, wherein the two cyclopentadienyl-typeligands are connected by a substituted or unsubstituted bridging groupcomprising from 3 to 5 contiguous ansa carbon atoms in a chain, one endof which is bonded to one of the cyclopentadienyl-type ligands, and theother end of which is bonded to the other cyclopentadienyl-type ligand.In still another aspect of the invention, the second metallocenecompound can comprise a bis(monosubstituted cycloalkadienyl) hafniumcompound, similar in structure to the first metallocene compound ofzirconium. In yet another aspect, the dual metallocene catalystcomposition can comprise a first metallocene compound and anycombination of second metallocene compounds, including any combinationof more than one of the same type or different types of secondmetallocene compounds.

In one aspect, the catalyst composition of this invention comprises afirst metallocene compound, a second metallocene compound, at least onechemically-treated solid oxide, and at least one organoaluminumcompound, wherein:

a) the first metallocene compound has the following formula:(X¹)(X²)(X³)(X⁴)Zr;

wherein (X¹) and (X²) are independently selected from a monosubstitutedcyclopentadienyl, a monosubstituted indenyl, a monosubstitutedfluorenyl, or a monosubstituted, partially saturated analog thereof;

wherein each substituent on (X¹) and (X²) is independently selected froma linear or branched aliphatic group, wherein the aliphatic group isunsubstituted or substituted, any one of which having from 1 to about 20carbon atoms;

wherein (X³), (X⁴), and any substituent on the substituted aliphaticgroup on (X¹) and (X²) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen;

b) wherein the second metallocene compound has the following formula:(X⁵)(X⁶)(X⁷)(X⁸)M;wherein

-   -   1) M is Zr;        -   (X⁵) and (X⁶) are independently selected from a substituted            cyclopentadienyl, a substituted indenyl, a substituted            fluorenyl, or a substituted, partially saturated analog            thereof, wherein at least one of (X⁵) and (X⁶) is at least            disubstituted; and        -   each substituent on (X⁵) and (X⁶) is independently selected            from a linear or branched aliphatic group, wherein the            aliphatic group is unsubstituted or substituted, any one of            which having from 1 to about 20 carbon atoms;    -   2) M is Zr;        -   (X⁵) and (X⁶) are independently selected from a            cyclopentadienyl, an indenyl, a fluorenyl, a partially            saturated analog thereof, or a substituted analog thereof;            and        -   (X⁵) and (X⁶) are connected by a substituted or            unsubstituted bridging group comprising from 3 to 5            contiguous ansa carbon atoms in a chain, one end of which is            bonded to (X⁵) and the other end of which is bonded to (X⁶);            or    -   3) M is Hf;        -   (X⁵) and (X⁶) are independently selected from a            monosubstituted cyclopentadienyl, a monosubstituted indenyl,            a monosubstituted fluorenyl, or a monosubstituted, partially            saturated analog thereof; and        -   each substituent on (X⁵) and (X⁶) is independently selected            from a linear or branched aliphatic group, wherein the            aliphatic group is unsubstituted or substituted, any one of            which having from 1 to about 20 carbon atoms; and            wherein (X⁷), (X⁸), any substituent on (X⁵), any substituent            on (X⁶), any substituent on the substituted aliphatic group            on (X⁵) and (X⁶), and any substituent on the substituted            bridging group connecting (X⁵) and (X⁶) are independently            selected from an aliphatic group, an aromatic group, a            cyclic group, a combination of aliphatic and cyclic groups,            an oxygen group, a sulfur group, a nitrogen group, a            phosphorus group, an arsenic group, a carbon group, a            silicon group, a germanium group, a tin group, a lead group,            a boron group, an aluminum group, an inorganic group, an            organometallic group, or a substituted derivative thereof,            any one of which having from 1 to about 20 carbon atoms; a            halide; or hydrogen; and

c) the chemically-treated solid oxide comprises a solid oxide treatedwith an electron-withdrawing anion.

In another aspect of this invention, the organoaluminum compound canhave the following formula:Al(X⁹)_(n)(X¹⁰)_(3-n);wherein (X⁹) is a hydrocarbyl having from 1 to about 20 carbon atoms;(X¹⁰) is selected from alkoxide or aryloxide having from 1 to about 20carbon atoms, halide, or hydride; and n is a number from 1 to 3,inclusive.

In another aspect of this invention, the second metallocene compound canhave the following formula:(X⁵)(X⁶)(X⁷)(X⁸)Zr;

wherein (X⁵) and (X⁶) are independently selected from a substitutedcyclopentadienyl, a substituted indenyl, a substituted fluorenyl, or asubstituted, partially saturated analog thereof, wherein at least one of(X⁵) and (X⁶) is at least disubstituted;

wherein each substituent on (X⁵) and (X⁶) is independently selected froma linear or branched aliphatic group, wherein the aliphatic group isunsubstituted or substituted, any one of which having from 1 to about 20carbon atoms;

wherein (X⁷), (X⁸), and any substituent on the substituted aliphaticgroup on (X⁵) and (X⁶) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen. In another aspect, when the secondmetallocene compound has this formula, both (X⁵) and (X⁶) may be atleast disubstituted.

In yet another aspect, the second metallocene compound can be anansa-metallocene having the following formula:(X⁵)(X⁶)(X⁷)(X⁸)Zr;

wherein (X⁵) and (X⁶) are independently selected from acyclopentadienyl, an indenyl, a fluorenyl, a partially saturated analogthereof, or a substituted analog thereof; wherein (X⁵) and (X⁶) areconnected by a substituted or unsubstituted bridging group comprisingfrom 3 to 5 contiguous ansa carbon atoms in a chain, one end of which isbonded to (X⁵) and the other end of which is bonded to (X⁶);

wherein (X⁷), (X⁸), any substituent on the substituted bridging groupconnecting (X⁵) and (X⁶), any substituent on (X⁵), and any substituenton (X⁶) are independently selected from an aliphatic group, an aromaticgroup, a cyclic group, a combination of aliphatic and cyclic groups, anoxygen group, a sulfur group, a nitrogen group, a phosphorus group, anarsenic group, a carbon group, a silicon group, a germanium group, a tingroup, a lead group, a boron group, an aluminum group, an inorganicgroup, an organometallic group, or a substituted derivative thereof, anyone of which having from 1 to about 20 carbon atoms; a halide; orhydrogen.

In still another aspect, the second metallocene compound can have thefollowing formula:(X⁵)(X⁶)(X⁷)(X⁸)Hf;

wherein (X⁵) and (X⁶) are independently selected from a monosubstitutedcyclopentadienyl, a monosubstituted indenyl, a monosubstitutedfluorenyl, or a monosubstituted, partially saturated analog thereof;

wherein each substituent on (X⁵ ) and (X⁶) is independently selectedfrom a linear or branched aliphatic group, wherein the aliphatic groupis unsubstituted or substituted, any one of which having from 1 to about20 carbon atoms;

wherein (X⁷), (X⁸), and any substituent on the substituted aliphaticgroup on (X⁵) and (X⁶) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen.

In one aspect of this invention, the chemically-treated solid oxidecomprises a solid oxide treated with an electron-withdrawing anion,wherein

the solid oxide is selected from silica, alumina, silica-alumina,aluminum phosphate, heteropolytungstates, titania, zirconia, magnesia,boria, zinc oxide, mixed oxides thereof, or mixtures thereof; and

the electron-withdrawing anion is selected from fluoride, chloride,bromide, phosphate, triflate, bisulfate, sulfate, or any combinationthereof. In another aspect, the chemically-treated solid oxide can beselected from fluorided alumina, chlorided alumina, bromided alumina,sulfated alumina, fluorided silica-alumina, chlorided silica-alumina,bromided silica-alumina, sulfated silica-alumina, fluoridedsilica-zirconia, chlorided silica-zirconia, bromided silica-zirconia,sulfated silica-zirconia, or any combination thereof. Further, and inyet another aspect, the chemically-treated solid oxide can furthercomprise a metal or metal ion selected from zinc, nickel, vanadium,silver, copper, gallium, tin, tungsten, molybdenum, or any combinationthereof.

Yet another aspect of this invention is a catalyst composition furthercomprising an optional cocatalyst selected from at least onealuminoxane, at least one organozinc compound, at least one organoboroncompound, at least one ionizing ionic compound, or any combinationthereof.

Still another aspect of this invention is a catalyst compositionconsisting essentially of a first metallocene compound, a secondmetallocene compound, at least one chemically-treated solid oxide, andat least one organoaluminum compound.

In another aspect, this invention provides a process to produce orprepare a catalyst composition comprising contacting a first metallocenecompound, a second metallocene compound, at least one chemically-treatedsolid oxide, and at least one organoaluminum compound.

In still another aspect, this invention provides a process forpolymerizing olefins in the presence of a catalyst composition,comprising contacting the catalyst composition with at least one type ofolefin monomer, wherein the catalyst composition comprises a firstmetallocene compound, a second metallocene compound, at least onechemically-treated solid oxide, and at least one organoaluminumcompound. Thus, this invention comprises methods for polymerizingolefins using the catalyst compositions prepared as described herein.

The present invention also encompasses new polyolefins and new films.

In one aspect, this invention provides a polymer or copolymer ofethylene wherein the resin is characterized by a melt index (MI) of fromabout 0.3 to about 2.0 g/10 min, determined using a 2.16 kg load at 190°C. In another aspect, the polymer resin of this invention ischaracterized by a high load melt index (HLMI) of from about 10 to about30 g/10 min, determined with a 21.6 kg load at 190° C.

In another aspect, this invention provides a polymer or copolymer ofethylene wherein the resin is characterized by a density from about 0.94to about 0.91 g/cm³.

In still another aspect, this invention provides a polymer or copolymerof ethylene wherein the resin is characterized by a Carreau-Yasuda “a”breadth parameter (CY-a) from about 0.45 to about 0.70.

Another aspect of this invention is a polymer or copolymer of ethylenewherein the resin is characterized by a polydispersity (Mw/Mn) of fromabout 2 to about 6.

Yet a different aspect of this invention is a polymer or copolymer ofethylene wherein the resin is characterized by an Elmendorf MD tearresistance of greater than or equal to about 150 g/mil. In anotheraspect of the invention, a polymer or copolymer of ethylene is providedwherein the resin is characterized by an Elmendorf TD tear resistance ofgreater than or equal to about 300 g/mil.

Still a different aspect of this invention is a polymer of copolymer ofethylene wherein the Dart impact strength is greater than or equal toabout 600 g/mil. In another aspect, a polymer or copolymer of ethyleneis provided wherein the Spencer impact strength is greater than or equalto about 0.25 J/mil.

In yet another aspect, this invention provides a polymer or copolymer ofethylene wherein the resin is characterized by a haze of less than about25%.

This invention also provides, in another aspect, an article thatcomprises the polymer produced with the catalyst composition of thisinvention.

These and other features, aspects, embodiments, and advantages of thepresent invention will become apparent after a review of the followingdetailed description of the disclosed features.

DETAILED DESCRIPTION OF THE INVENTION

The present invention provides new catalyst compositions, methods forpreparing catalyst compositions, methods for using the catalystcompositions to polymerize olefins, and olefin polymers, copolymers, andpolymer films. In the course of examining metallocene-based olefinpolymerization catalysts, it was discovered that a dual metallocenecatalyst system provided a useful combination of polyolefin properties,such as melt index, haze, MD tear, and the like, while maintainingsufficient melt strength so the resin is suitable for blowing film.

In one aspect, the present invention encompasses a composition of mattercomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. In another aspect, this invention encompasses acatalyst composition, a catalyst composition for polymerizing olefins, amethod of preparing a catalyst composition, a method of using a catalystcomposition, and the like, in each case encompassing a first metallocenecompound, a second metallocene compound, at least one chemically-treatedsolid oxide, and at least one organoaluminum compound. In anotheraspect, this invention comprises new polyolefins and films.

Catalyst Composition and Components

The Metallocene Compounds

In one aspect, the present invention provides a catalyst compositioncomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. Thus, in one aspect, for example, two differentmetallocene compounds are used simultaneously in a polymerizationprocess to produce a polyethylene resin with good properties for linearlow density (LLDPE) film applications.

In one aspect, for example, when a first metallocene compound isemployed in a catalyst composition without a second metallocenecompound, a polyethylene may be obtained with insufficient molecularweight, melt strength, and optical properties, for use in LLDPE filmapplications. Using a second metallocene compound which makes highermolecular weight polyethylene when used alone, in conjunction with thefirst metallocene compound, may provide improved film performance insuch parameters as melt strength, activity, MD tear, and opticalproperties, as compared to a catalyst composition comprising eithersingle metallocene compound without the other.

In one aspect of this invention, for example, the first metallocene is azirconium metallocene compound wherein the two η⁵-cycloalkadienylligands are typically monosubstituted with an aliphatic group. Inanother aspect, for example, the second metallocene may be differentfrom the first by further substitution of the η⁵-cycloalkadienyl rings,by being unbridged or loosely bridged, or by comprising the hafniumanalog of the zirconium first metallocene. In another aspect, anycombination of more than one second metallocene compound may be used inthe catalyst compositions of this invention.

In one aspect, this invention encompasses a catalyst compositioncomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound, wherein:

a) the first metallocene compound has the following formula:(X¹)(X²)(X³)(X⁴)Zr;

wherein (X¹) and (X²) are independently selected from a monosubstitutedcyclopentadienyl, a monosubstituted indenyl, a monosubstitutedfluorenyl, or a monosubstituted, partially saturated analog thereof;

wherein each substituent on (X¹) and (X²) is independently selected froma linear or branched aliphatic group, wherein the aliphatic group isunsubstituted or substituted, any one of which having from 1 to about 20carbon atoms;

wherein (X³), (X⁴), and any substituent on the substituted aliphaticgroup on (X¹) and (X²) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen;

b) wherein the second metallocene compound has the following formula:(X⁵)(X⁶)(X⁷)(X⁸)M;wherein

1) M is Zr;

-   -   -   (X⁵) and (X⁶) are independently selected from a substituted            cyclopentadienyl, a substituted indenyl, a substituted            fluorenyl, or a substituted, partially saturated analog            thereof, wherein at least one of (X⁵) and (X⁶) is at least            disubstituted; and        -   each substituent on (X⁵) and (X⁶) is independently selected            from a linear or branched aliphatic group, wherein the            aliphatic group is unsubstituted or substituted, any one of            which having from 1 to about 20 carbon atoms;

    -   2) M is Zr;        -   (X⁵) and (X⁶) are independently selected from a            cyclopentadienyl, an indenyl, a fluorenyl, a partially            saturated analog thereof, or a substituted analog thereof;            and        -   (X⁵) and (X⁶) are connected by a substituted or            unsubstituted bridging group comprising from 3 to 5            contiguous ansa carbon atoms in a chain, one end of which is            bonded to (X⁵) and the other end of which is bonded to (X⁶);            or

    -   3) M is Hf;        -   (X⁵) and (X⁶) are independently selected from a            monosubstituted cyclopentadienyl, a monosubstituted indenyl,            a monosubstituted fluorenyl, or a monosubstituted, partially            saturated analog thereof; and        -   each substituent on (X⁵) and (X⁶) is independently selected            from a linear or branched aliphatic group, wherein the            aliphatic group is unsubstituted or substituted, any one of            which having from 1 to about 20 carbon atoms; and            wherein (X⁷), (X⁸), any substituent on (X⁵), any substituent            on (X⁶), any substituent on the substituted aliphatic group            on (X⁵) and (X⁶), and any substituent on the substituted            bridging group connecting (X⁵) and (X⁶) are independently            selected from an aliphatic group, an aromatic group, a            cyclic group, a combination of aliphatic and cyclic groups,            an oxygen group, a sulfur group, a nitrogen group, a            phosphorus group, an arsenic group, a carbon group, a            silicon group, a germanium group, a tin group, a lead group,            a boron group, an aluminum group, an inorganic group, an            organometallic group, or a substituted derivative thereof,            any one of which having from 1 to about 20 carbon atoms; a            halide; or hydrogen; and

c) the chemically-treated solid oxide comprises a solid oxide treatedwith an electron-withdrawing anion.

In another aspect of this invention, the organoaluminum compound canhave the following formula:Al(X⁹)_(n)(X¹⁰)_(3-n);wherein (X⁹) is a hydrocarbyl having from 1 to about 20 carbon atoms;(X¹⁰) is selected from alkoxide or aryloxide having from 1 to about 20carbon atoms, halide, or hydride; and n is a number from 1 to 3,inclusive.

Catalyst compositions comprising various combinations of thesemetallocenes including, but not limited to, at least one firstmetallocene compound and at least one second metallocene compound, anycombination of more than one first metallocene compound and anycombination of more than one second metallocene compound, are alsoencompassed by this invention.

The First Metallocene Compound

In one aspect of this invention, the first metallocene compound has thefollowing formula:(X¹)(X²)(X³)(X⁴)Zr;

wherein (X¹) and (X²) are independently selected from a monosubstitutedcyclopentadienyl, a monosubstituted indenyl, a monosubstitutedfluorenyl, or a monosubstituted, partially saturated analog thereof;

wherein each substituent on (X¹) and (X²) is independently selected froma linear or branched aliphatic group, wherein the aliphatic group isunsubstituted or substituted, any one of which having from 1 to about 20carbon atoms; and

wherein (X³), (X⁴), and any substituent on the substituted aliphaticgroup on (X¹) and (X²) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen.

In another aspect, the first metallocene compound has the formula:(η⁵-C₅H₄R¹)₂ZrX¹¹ ₂,

wherein R¹ in each instance is independently selected from a linear orbranched aliphatic group having from 1 to about 20 carbon atoms, andwherein X¹¹ in each instance is independently selected from F, Cl, Br,I, OMe, OEt, O-n-Pr, O-i-Pr, O-n-Bu, O-t-Bu, NMe₂, or NEt₂.

Still another aspect of this invention is a catalyst compositioncomprising a first metallocene compound having the formula(η⁵-C₅H₄R¹)₂ZrCl₂, wherein R¹ in each instance is independently selectedfrom a linear or branched aliphatic group having from 1 to about 20carbon atoms.

In yet another aspect, the catalyst composition of this inventioncomprises a first metallocene compound selected from (η⁵-C₅H₄Me)₂ZrCl₂,(η⁵-C₅H₄Et)₂ZrCl₂, (η⁵-C₅H₄ ^(n)Pr)₂ZrCl₂, (η⁵-C₅H₄ ^(i)Pr)₂ZrCl₂,(η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂, (η⁵-C₅H₄ ^(i)Bu)₂ZrCl₂, (η⁵-C₅H₄ ^(s)Bu)₂ZrCl₂,(η⁵-C₅H₄ ^(t)Bu)₂ZrCl₂, and the like.

Yet another aspect of this invention is the first metallocene compoundhaving the formula (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂.

It is not necessary that both η⁵-cyclopentadienyl-type ligands be thesame in the first metallocene compound. Thus, the first metallocenecompound can comprise any combination of two η⁵-cyclopentadienyl-typeligands selected from a monosubstituted cyclopentadienyl, amonosubstituted indenyl, a monosubstituted fluorenyl, or amonosubstituted, partially saturated analog thereof. The term partiallysaturated analog refers to ligands such as partially saturated indenylsand fluorenyls including, but not limited to, tetrahydroindenyls,tetrahydrofluorenyls, and octahydrofluorenyls. Thus, the firstmetallocene compound can comprise a monosubstituted tetrahydroindenyl, amonosubstituted tetrahydrofluorenyl, or a monosubstitutedoctahydrofluorenyl.

Further, it is not necessary that both η⁵-cyclopentadienyl-type ligandsbe monosubstituted with the same aliphatic group, even when theη⁵-cyclopentadienyl-type ligands both are monosubstitutedcyclopentadienyl, both are monosubstituted indenyl, both aremonosubstituted fluorenyl, and the like. Thus, even when (X¹) and (X²)of the first metallocene compound (X¹)(X²)(X³)(X⁴)Zr are bothmonosubstituted cyclopentadienyl, it is not necessary that the aliphaticgroup substituents be the same. In this aspect, for example, (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ and (η⁵-C₅H₄ ^(n)Bu)(η⁵-C₅H₄Me)ZrCl₂ constitute examplesof a compound that may be used as a first metallocene compound.

The Second Metallocene Compound

In one aspect of this invention, the second metallocene compound has thefollowing formula:(X⁵)(X⁶)(X⁷)(X⁸)M;wherein

1) M is Zr;

-   -   (X⁵) and (X⁶) are independently selected from a substituted        cyclopentadienyl, a substituted indenyl, a substituted        fluorenyl, or a substituted, partially saturated analog thereof,        wherein at least one of (X⁵) and (X⁶) is at least disubstituted;        and    -   each substituent on (X⁵) and (X⁶) is independently selected from        a linear or branched aliphatic group, wherein the aliphatic        group is unsubstituted or substituted, any one of which having        from 1 to about 20 carbon atoms;

2) M is Zr;

-   -   (X⁵) and (X⁶) are independently selected from a        cyclopentadienyl, an indenyl, a fluorenyl, a partially saturated        analog thereof, or a substituted analog thereof; and    -   (X⁵) and (X⁶) are connected by a substituted or unsubstituted        bridging group comprising from 3 to 5 contiguous ansa carbon        atoms in a chain, one end of which is bonded to (X⁵) and the        other end of which is bonded to (X⁶); or

3) M is Hf;

-   -   (X⁵) and (X⁶) are independently selected from a monosubstituted        cyclopentadienyl, a monosubstituted indenyl, a monosubstituted        fluorenyl, or a monosubstituted, partially saturated analog        thereof; and    -   each substituent on (X⁵) and (X⁶) is independently selected from        a linear or branched aliphatic group, wherein the aliphatic        group is unsubstituted or substituted, any one of which having        from 1 to about 20 carbon atoms; and

wherein (X⁷), (X⁸), any substituent on (X⁵), any substituent on (X⁶),any substituent on the substituted aliphatic group on (X⁵) and (X⁶), andany substituent on the substituted bridging group connecting (X⁵) and(X⁶) are independently selected from an aliphatic group, an aromaticgroup, a cyclic group, a combination of aliphatic and cyclic groups, anoxygen group, a sulfur group, a nitrogen group, a phosphorus group, anarsenic group, a carbon group, a silicon group, a germanium group, a tingroup, a lead group, a boron group, an aluminum group, an inorganicgroup, an organometallic group, or a substituted derivative thereof, anyone of which having from 1 to about 20 carbon atoms; a halide; orhydrogen.

Type I Second Metallocene Compound

In one aspect of this invention, the second metallocene compound canhave the following formula:(X⁵)(X⁶)(X⁷)(X⁸)Zr;

wherein (X⁵) and (X⁶) are independently selected from a substitutedcyclopentadienyl, a substituted indenyl, a substituted fluorenyl, or asubstituted, partially saturated analog thereof, wherein at least one of(X⁵) and (X⁶) is at least disubstituted;

wherein each substituent on (X⁵) and (X⁶) is independently selected froma linear or branched aliphatic group, wherein the aliphatic group isunsubstituted or substituted, any one of which having from 1 to about 20carbon atoms;

wherein (X⁷), (X⁸), and any substituent on the substituted aliphaticgroup on (X⁵) and (X⁶) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen. In another aspect, when the secondmetallocene compound has this formula, both (X⁵) and (X⁶) may be atleast disubstituted.

In this aspect of the invention, the second metallocene compoundcomprises a more highly substituted zirconium metallocene compound thanthe first metallocene compound, in which the η⁵-cyclopentadienyl-typeligands are monosubstituted. Thus, in this aspect of the invention, theη⁵-cyclopentadienyl-type ligands of the second metallocene compound maybe disubstituted, trisubstituted, tetrasubstituted, or pentasubstituted.In another aspect, the η⁵-cyclopentadienyl-type ligands of the secondmetallocene compound may be disubstituted or trisubstituted.

In still another aspect, the second metallocene compound can have theformula (η⁵-C₅H₃R¹ ₂)₂ZrX¹¹ ₂, wherein R¹ in each instance isindependently selected from a linear or branched aliphatic group havingfrom 1 to about 20 carbon atoms, and X¹¹ in each instance isindependently selected from F, Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr,O-n-Bu, O-t-Bu, NMe₂, or NEt₂.

In another aspect, the second metallocene compound can have the formula(η⁵-C₅H₃ ^(n)BuR²)₂ZrCl₂, wherein R² is selected from Me, Et, n-Pr,i-Pr, n-Bu, s-Bu, i-Bu, or t-Bu.

Yet another aspect of this invention is a catalyst compositioncomprising a second metallocene compound of the formula (η⁵-C₅H₃^(n)BuMe)₂ZrCl₂.

Type II Second Metallocene Compound

In yet another aspect, the second metallocene compound can be anansa-metallocene having the following formula:(X⁵)(X⁶)(X⁷)(X⁸)Zr;

wherein (X⁵) and (X⁶) are independently selected from acyclopentadienyl, an indenyl, a fluorenyl, a partially saturated analogthereof, or a substituted analog thereof;

wherein (X⁵) and (X⁶) are connected by a substituted or unsubstitutedbridging group comprising from 3 to 5 contiguous ansa carbon atoms in achain, one end of which is bonded to (X⁵) and the other end of which isbonded to (X⁶);

wherein (X⁷), (X⁸), any substituent on the substituted bridging groupconnecting (X⁵) and (X⁶), any substituent on (X⁵), and any substituenton (X⁶) are independently selected from an aliphatic group, an aromaticgroup, a cyclic group, a combination of aliphatic and cyclic groups, anoxygen group, a sulfur group, a nitrogen group, a phosphorus group, anarsenic group, a carbon group, a silicon group, a germanium group, a tingroup, a lead group, a boron group, an aluminum group, an inorganicgroup, an organometallic group, or a substituted derivative thereof, anyone of which having from 1 to about 20 carbon atoms; a halide; orhydrogen.

As used herein, the term ansa-metallocene refers simply to a metallocenecompound in which the two η⁵-cycloalkadienyl-type ligands in themolecule are linked by a bridging moiety. Useful ansa-metallocenes aretypically “loosely-bridged”, meaning that the twoη⁵-cycloalkadienyl-type ligands are connected by a bridging groupwherein the shortest link of the bridging moiety between theη⁵-cycloalkadienyl-type ligands is at least 3 atoms and up to about 5atoms. Thus, the length of the bridge or the chain between the twoη⁵-cycloalkadienyl-type ligands is from 3 to about 5 atoms. Further, thebridge that connects the two η⁵-cycloalkadienyl-type ligands may besubstituted or unsubstituted.

In one aspect, the second metallocene compound may be selected from[μ-CH₂(CH₂)_(n)CH₂](η⁵-9-C₁₃H₈)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-9-C₁₃H₁₆)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-1-C₉H₆)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-1-C₉H₁₀)₂ZrX¹² ₂, or any combination thereof,wherein n is from 1 to 3, and wherein X¹², in each occurrence, isindependently selected from an aliphatic group, an aromatic group, analkoxide group, an aryloxide group, an alkylamide group, an arylamidegroup, a dialkylamide group, a diarylamide group, an alkyl arylamidegroup, an alkylthiolate group, an arylthiolate group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen.

In another aspect, the present invention encompasses a catalystcomposition comprising a second metallocene compound selected from[μ-CH₂(CH₂)_(n)CH₂](η⁵-9-C₁₃H₈)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-9-C₁₃H₁₆)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-1-C₉H₆)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-1-C₉H₁₀)₂ZrX¹² ₂, or any combination thereof,wherein n is from 1 to 3, and wherein X¹² is independently selected fromF, Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr, O-n-Bu, O-t-Bu, NMe₂, or NEt₂.

Still another aspect of this invention, for example, is a secondmetallocene compound selected from:

-   1,3-propanediylbis(η⁵-9-fluorenyl)zirconium dichloride;-   1,4-butanediylbis(η⁵-9-fluorenyl)zirconium dichloride;-   1,5-pentanediylbis(η⁵-9-fluorenyl)zirconium dichloride;-   1,3-propanediylbis(η⁵-1-indenyl)zirconium dichloride;-   1,4-butanediylbis(η⁵-1-indenyl)zirconium dichloride;-   1,5-pentanediylbis(η⁵-1-indenyl)zirconium dichloride;-   1,3-propanediylbis(η⁵-9-fluorenyl)di-n-butoxyzirconium;-   1,4-butanediylbis(η⁵-9-fluorenyl)di-n-butoxyzirconium;-   1,5-pentanediylbis(η⁵-9-fluorenyl)di-n-butoxyzirconium;-   1,3-propanediylbis(η⁵-1-indenyl)di-n-butoxyzirconium;-   1,4-butanediylbis(η⁵-1-indenyl)di-n-butoxyzirconium;-   1,5-pentanediylbis(η⁵-1-indenyl)di-n-butoxyzirconium;-   1,3-propanediylbis(η⁵-9-fluorenyl)zirconium dimethyl;-   1,4-butanediylbis(η⁵-9-fluorenyl)zirconium dimethyl;-   1,5-pentanediylbis(η⁵-9-fluorenyl)zirconium dimethyl;-   1,3-propanediylbis(η⁵-1-indenyl)zirconium dimethyl;-   1,4-butanediylbis(η⁵-1-indenyl)zirconium dimethyl;-   1,5-pentanediylbis(η⁵-1-indenyl)zirconium dimethyl;    or any combination thereof.

Type III Second Metallocene Compound

In still another aspect, the second metallocene compound can have thefollowing formula:(X⁵)(X⁶)(X⁷)(X⁸)Hf;

wherein (X⁵) and (X⁶) are independently selected from a monosubstitutedcyclopentadienyl, a monosubstituted indenyl, a monosubstitutedfluorenyl, or a monosubstituted, partially saturated analog thereof;

wherein each substituent on (X⁵) and (X⁶) is independently selected froma linear or branched aliphatic group, wherein the aliphatic group isunsubstituted or substituted, any one of which having from 1 to about 20carbon atoms; and

wherein (X⁷), (X⁸), and any substituent on the substituted aliphaticgroup on (X⁵) and (X⁶) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen.

In this aspect, the second metallocene compound is the hafnium analog ofthe first metallocene zirconium compound.

In another aspect, the second metallocene compound has the followingformula:(η⁵-C₅H₄R¹)₂HfX¹¹ ₂,

wherein R¹ in each instance is independently selected from a linear orbranched aliphatic group having from 1 to about 20 carbon atoms, and X¹¹is independently selected from F, Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr,O-n-Bu, O-t-Bu, NMe₂, or NEt₂;

Still another aspect of this invention is a catalyst compositioncomprising a second metallocene compound having the formula(η⁵-C₅H₄R¹)₂HfCl₂, wherein R¹ in each instance is independently selectedfrom a linear or branched aliphatic group having from 1 to about 20carbon atoms.

In yet another aspect, for example, the catalyst composition of thisinvention comprises a second metallocene compound selected from(η⁵-C₅H₄Me)₂HfCl₂, (η⁵-C₅H₄Et)₂HfCl₂, (η⁵-C₅H₄ ^(n)Pr)₂HfCl₂, (η⁵-C₅H₄^(i)Pr)₂HfCl₂, (η⁵-C₅H₄ ^(n)Bu)₂HfCl₂, (η⁵-C₅H₄ ^(i)Bu)₂HfCl₂, (η⁵-C₅H₄^(s)Bu)₂HfCl₂, (η⁵-C₅H₄ ^(t)Bu)₂HfCl₂, and the like.

Yet another aspect of this invention, for example, is the secondmetallocene compound having the formula (η⁵-C₅H₄ ^(n)Bu)₂HfCl₂.

It is not necessary that both η⁵-cyclopentadienyl-type ligands be thesame in this type of second metallocene compound. Thus, this type ofsecond metallocene compound can comprise any combination of twoη⁵-cyclopentadienyl-type ligands selected from a monosubstitutedcyclopentadienyl, a monosubstituted indenyl, a monosubstitutedfluorenyl, or a monosubstituted, partially saturated analog thereof. Theterm partially saturated analog refers to ligands such as partiallysaturated indenyls and fluorenyls including, but not limited to,tetrahydroindenyls, tetrahydrofluorenyls, and octahydrofluorenyls. Thus,the first metallocene compound can comprise a monosubstitutedtetrahydroindenyl, a monosubstituted tetrahydrofluorenyl, or amonosubstituted octahydrofluorenyl.

Further, it is not necessary that both η⁵-cyclopentadienyl-type ligandsbe monosubstituted with the same aliphatic group, even when theη⁵-cyclopentadienyl-type ligands both are monosubstitutedcyclopentadienyl, both are monosubstituted indenyl, both aremonosubstituted fluorenyl, and the like. Thus, even when (X⁵) and (X⁶)of the second metallocene compound (X⁵)(X⁶)(X⁷)(X⁸)Hf are bothmonosubstituted cyclopentadienyl, it is not necessary that the aliphaticgroup substituents be the same. In this aspect, for example, (η⁵-C₅H₄^(n)Bu)₂HfCl₂ and (η⁵-C₅H₄ ^(n)Bu)(η⁵-C₅H₄Me)HfCl₂ constitute examplesof a compound that may be used as a second metallocene compound.

Substituents

In one aspect of this invention, the metallocene compounds can comprisea variety of substituents, comprising chemical moieties bonded either tothe metal itself as an (X³), (X⁴), (X⁷), or (X⁸) ligand, or bonded toanother portion of the molecule, such as a substituent on an aliphaticmoiety bonded to a η⁵-cyclopentadienyl-type ligand, a substituent on abridging group linking two a η⁵-cyclopentadienyl-type ligand, or thelike.

In this aspect, for example, (X³); (X⁴); (X⁷); (X⁸); any substituent onthe substituted aliphatic group on (X¹), (X²), (X⁵), and (X⁶); anysubstituent on (X⁵) and (X⁶); and any substituent on the substitutedbridging group connecting (X⁵) and (X⁶); are typically independentlyselected from an aliphatic group, an aromatic group, a cyclic group, acombination of aliphatic and cyclic groups, an oxygen group, a sulfurgroup, a nitrogen group, a phosphorus group, an arsenic group, a carbongroup, a silicon group, a germanium group, a tin group, a lead group, aboron group, an aluminum group, an inorganic group, an organometallicgroup, or a substituted derivative thereof, any one of which having from1 to about 20 carbon atoms; a halide; or hydrogen; as long as thesegroups do not terminate the activity of the catalyst composition.Further, this description can include substituted, unsubstituted,branched, linear, or heteroatom-substituted analogs of these moieties.

Further, this list of possible substituents includes substituents thatmay be characterized in more than one of these categories such asbenzyl. This list also includes hydrogen, therefore the notion of asubstituted indenyl and substituted fluorenyl includes partiallysaturated indenyls and fluorenyls including, but not limited to,tetrahydroindenyls, tetrahydrofluorenyls, and octahydrofluorenyls.

Examples of each of these substituent groups include, but are notlimited to, the following groups. In each example presented below,unless otherwise specified, R is independently selected from: analiphatic group; an aromatic group; a cyclic group; any combinationthereof; any substituted derivative thereof, including but not limitedto, a halide-, an alkoxide-, or an amide-substituted derivative thereof;any one of which has from 1 to about 20 carbon atoms; or hydrogen. Alsoincluded in these groups are any unsubstituted, branched, or linearanalogs thereof.

Examples of aliphatic groups, in each instance, include, but are notlimited to, an alkyl group, a cycloalkyl group, an alkenyl group, acycloalkenyl group, an alkynyl group, an alkadienyl group, a cyclicgroup, and the like, and includes all substituted, unsubstituted,branched, and linear analogs or derivatives thereof, in each instancehaving from one to about 20 carbon atoms. Thus, aliphatic groupsinclude, but are not limited to, hydrocarbyls such as paraffins andalkenyls. For example, aliphatic groups as used herein include methyl,ethyl, propyl, n-butyl, tert-butyl, sec-butyl, isobutyl, amyl, isoamyl,hexyl, cyclohexyl, heptyl, octyl, nonyl, decyl, dodecyl, 2-ethylhexyl,pentenyl, butenyl, and the like.

Examples of aromatic groups, in each instance, include, but are notlimited to, phenyl, naphthyl, anthacenyl, and the like, includingsubstituted derivatives thereof, in each instance having from 6 to about25 carbons. Substituted derivatives of aromatic compounds include, butare not limited to, tolyl, xylyl, mesityl, and the like, including anyheteroatom substituted derivative thereof.

Examples of cyclic groups, in each instance, include, but are notlimited to, cycloparaffins, cycloolefins, cycloacetylenes, arenes suchas phenyl, bicyclic groups and the like, including substitutedderivatives thereof, in each instance having from about 3 to about 20carbon atoms. Thus heteroatom-substituted cyclic groups such as furanylare included herein.

In each instance, aliphatic and cyclic groups are groups comprising analiphatic portion and a cyclic portion, examples of which include, butare not limited to, groups such as: —(CH₂)_(m)C₆H_(q)R_(5-q) wherein mis an integer from 1 to about 10, q is an integer from 1 to 5,inclusive; —(CH₂)_(m)C₆H_(q)R_(11-q) wherein m is an integer from 1 toabout 10, q is an integer from 1 to 11, inclusive; and—(CH₂)_(m)C₅H_(q)R_(9-q), wherein m is an integer from 1 to about 10, qis an integer from 1 to 9, inclusive. In each instance and as definedabove, R is independently selected from: an aliphatic group; an aromaticgroup; a cyclic group; any combination thereof; any substitutedderivative thereof, including but not limited to, a halide-, analkoxide-, or an amide-substituted derivative thereof; any one of whichhas from 1 to about 20 carbon atoms; or hydrogen. In one aspect,aliphatic and cyclic groups include, but are not limited to: —CH₂C₆H₅;—CH₂C₆H₄F; —CH₂C₆H₄Cl; —CH₂C₆H₄Br; —CH₂C₆H₄I; —CH₂C₆H₄OMe; —CH₂C₆H₄OEt;—CH₂C₆H₄NH₂; —CH₂C₆H₄NMe₂; —CH₂C₆H₄NEt₂; —CH₂CH₂C₆H₅; —CH₂CH₂C₆H₄F;—CH₂CH₂C₆H₄Cl; —CH₂CH₂C₆H₄Br; —CH₂CH₂C₆H₄I; —CH₂CH₂C₆H₄OMe;—CH₂CH₂C₆H₄OEt; —CH₂CH₂C₆H₄NH₂; —CH₂CH₂C₆H₄NMe₂; —CH₂CH₂C₆H₄NEt₂; anyregioisomer thereof, and any substituted derivative thereof.

Examples of halides, in each instance, include fluoride, chloride,bromide, and iodide.

In each instance, oxygen groups are oxygen-containing groups, examplesof which include, but are not limited to, alkoxy or aryloxy groups(—OR), —OC(O)R, —OC(O)H, —OSiR₃, —OPR₂, —OAlR₂, and the like, includingsubstituted derivatives thereof, wherein R in each instance is selectedfrom alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl, substitutedaryl, or substituted aralkyl having from 1 to about 20 carbon atoms.Examples of alkoxy or aryloxy groups (—OR) groups include, but are notlimited to, methoxy, ethoxy, propoxy, butoxy, phenoxy, substitutedphenoxy, and the like.

In each instance, sulfur groups are sulfur-containing groups, examplesof which include, but are not limited to, —SR, —OSO₂R, —OSO₂OR, —SCN,—SO₂R, and the like, including substituted derivatives thereof, whereinR in each instance is selected from alkyl, cycloalkyl, aryl, aralkyl,substituted alkyl, substituted aryl, or substituted aralkyl having from1 to about 20 carbon atoms.

In each instance, nitrogen groups are nitrogen-containing groups, whichinclude, but are not limited to, —NH₂, —NHR, —NR₂, —NO₂, —N₃, and thelike, including substituted derivatives thereof, wherein R in eachinstance is selected from alkyl, cycloalkyl, aryl, aralkyl, substitutedalkyl, substituted aryl, or substituted aralkyl having from 1 to about20 carbon atoms.

In each instance, phosphorus groups are phosphorus-containing groups,which include, but are not limited to, —PH₂, —PHR, —PR₂, —P(O)R₂,—P(OR)₂, —P(O)(OR)₂, and the like, including substituted derivativesthereof, wherein R in each instance is selected from alkyl, cycloalkyl,aryl, aralkyl, substituted alkyl, substituted aryl, or substitutedaralkyl having from 1 to about 20 carbon atoms.

In each instance, arsenic groups are arsenic-containing groups, whichinclude, but are not limited to, —AsHR, —AsR₂, —As(O)R₂, —As(OR)₂,—As(O)(OR)₂, and the like, including substituted derivatives thereof,wherein R in each instance is selected from alkyl, cycloalkyl, aryl,aralkyl, substituted alkyl, substituted aryl, or substituted aralkylhaving from 1 to about 20 carbon atoms.

In each instance, carbon groups are carbon-containing groups, whichinclude, but are not limited to, alkyl halide groups that comprisehalide-substituted alkyl groups with 1 to about 20 carbon atoms, aralkylgroups with 1 to about 20 carbon atoms, —C(O)H, —C(O)R, —C(O)OR, cyano,—C(NR)H, —C(NR)R, —C(NR)OR, and the like, including substitutedderivatives thereof, wherein R in each instance is selected from alkyl,cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, orsubstituted aralkyl having from 1 to about 20 carbon atoms.

In each instance, silicon groups are silicon-containing groups, whichinclude, but are not limited to, silyl groups such alkylsilyl groups,arylsilyl groups, arylalkylsilyl groups, siloxy groups, and the like,which in each instance have from 1 to about 20 carbon atoms. Forexample, silicon groups include trimethylsilyl and phenyloctylsilylgroups.

In each instance, germanium groups are germanium-containing groups,which include, but are not limited to, germyl groups such alkylgermylgroups, arylgermyl groups, arylalkylgermyl groups, germyloxy groups, andthe like, which in each instance have from 1 to about 20 carbon atoms.

In each instance, tin groups are tin-containing groups, which include,but are not limited to, stannyl groups such alkylstannyl groups,arylstannyl groups, arylalkylstannyl groups, stannoxy (or “stannyloxy”)groups, and the like, which in each instance have from 1 to about 20carbon atoms. Thus, tin groups include, but are not limited to, stannoxygroups.

In each instance, lead groups are lead-containing groups, which include,but are not limited to, alkyllead groups, aryllead groups, arylalkylleadgroups, and the like, which in each instance, have from 1 to about 20carbon atoms.

In each instance, boron groups are boron-containing groups, whichinclude, but are not limited to, —BR₂, —BX₂, —BRX, wherein X is amonoanionic group such as halide, hydride, alkoxide, alkyl thiolate, andthe like, and wherein R in each instance is selected from alkyl,cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, orsubstituted aralkyl having from 1 to about 20 carbon atoms.

In each instance, aluminum groups are aluminum-containing groups, whichinclude, but are not limited to, —AlR₂, —AlX₂, —AlRX, wherein X is amonoanionic group such as halide, hydride, alkoxide, alkyl thiolate, andthe like, and wherein R in each instance is selected from alkyl,cycloalkyl, aryl, aralkyl, substituted alkyl, substituted aryl, orsubstituted aralkyl having from 1 to about 20 carbon atoms.

Examples of inorganic groups that may be used as substituents forsubstituted cyclopentadienyls, substituted indenyls, substitutedfluorenyls, and substituted boratabenzenes, in each instance, include,but are not limited to, —SO₂X, —OAlX₂, —OSiX₃, —OPX₂, —SX, —OSO₂X,—AsX₂, —As(O)X₂, —PX₂, and the like, wherein X is a monoanionic groupsuch as halide, hydride, amide, alkoxide, alkyl thiolate, and the like,and wherein any alkyl, cycloalkyl, aryl, aralkyl, substituted alkyl,substituted aryl, or substituted aralkyl group or substituent on theseligands has from 1 to about 20 carbon atoms.

Examples of organometallic groups that may be used as substituents forsubstituted cyclopentadienyls, substituted indenyls, and substitutedfluorenyls, in each instance, include, but are not limited to,organoboron groups, organoaluminum groups, organogallium groups,organosilicon groups, organogermanium groups, organotin groups,organolead groups, organo-transition metal groups, and the like, havingfrom 1 to about 20 carbon atoms.

Numerous processes to prepare metallocene compounds that can be employedin this invention have been reported. For example, U.S. Pat. Nos.4,939,217, 5,191,132, 5,210,352, 5,347,026, 5,399,636, 5,401,817,5,420,320, 5,436,305, 5,451,649, 5,480,848, 5,496,781, 5,498,581,5,541,272, 5,554,795, 5,563,284, 5,565,592, 5,571,880, 5,594,078,5,631,203, 5,631,335, 5,654,454, 5,668,230, 5,705,579, and 6,509,427describe such methods, each of which is incorporated by referenceherein, in its entirety. In addition, the following treatises alsodescribe methods to prepare the metallocene compounds of the presentinvention: Wailes, P. C.; Coutts, R. S. P.; Weigold, H. inOrganometallic Chemistry of Titanium, Zironium, and Hafnium, Academic;New York, 1974; Cardin, D. J.; Lappert, M. F.; and Raston, C. L.;Chemistry of Organo-Zirconium and -Hafnium Compounds; Halstead Press;New York, 1986.

The Chemically Treated Solid Oxide

In one aspect, this invention encompasses a catalyst compositioncomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. In another aspect, the present inventionencompasses catalyst compositions comprising a chemically-treated solidoxide which serves as an acidic activator-support, and which istypically used in combination with an organoaluminum compound.

In one aspect of this invention, the catalyst composition can compriseat least one chemically-treated solid oxide comprising at least onesolid oxide treated with at least one electron-withdrawing anion,wherein the solid oxide can comprise any oxide that is characterized bya high surface area, and the electron-withdrawing anion can comprise anyanion that increases the acidity of the solid oxide as compared to thesolid oxide that is not treated with at least one electron-withdrawinganion.

In another aspect of this invention, the catalyst composition comprisesa chemically-treated solid oxide comprising a solid oxide treated withan electron-withdrawing anion, wherein:

the solid oxide is selected from silica, alumina, silica-alumina,aluminum phosphate, heteropolytungstates, titania, zirconia, magnesia,boria, zinc oxide, mixed oxides thereof, or mixtures thereof; and

the electron-withdrawing anion is selected from fluoride, chloride,bromide, phosphate, triflate, bisulfate, sulfate, fluorophosphate,fluorosulfate, or any combination thereof. In another aspect, forexample, the chemically-treated solid oxide can be selected fromfluorided alumina, chlorided alumina, bromided alumina, sulfatedalumina, fluorided silica-alumina, chlorided silica-alumina, bromidedsilica-alumina, sulfated silica-alumina, fluorided silica-zirconia,chlorided silica-zirconia, bromided silica-zirconia, sulfatedsilica-zirconia, or any combination thereof. Further, and in yet anotheraspect, the chemically-treated solid oxide can further comprise a metalor metal ion selected from zinc, nickel, vanadium, silver, copper,gallium, tin, tungsten, molybdenum, or any combination thereof.

The chemically-treated solid oxide typically comprises the contactproduct of at least one solid oxide compound and at least oneelectron-withdrawing anion source. In one aspect, the solid oxidecompound comprises an inorganic oxide. It is not required that the solidoxide compound be calcined prior to contacting the electron-withdrawinganion source. The contact product may be calcined either during or afterthe solid oxide compound is contacted with the electron-withdrawinganion source. In this aspect, the solid oxide compound may be calcinedor uncalcined. In another aspect, the activator-support may comprise thecontact product of at least one calcined solid oxide compound and atleast one electron-withdrawing anion source.

The chemically-treated solid oxide, also termed the activator-support,exhibits enhanced acidity as compared to the corresponding untreatedsolid oxide compound. The chemically-treated solid oxide also functionsas a catalyst activator as compared to the corresponding untreated solidoxide. While the chemically-treated solid oxide activates themetallocene in the absence of cocatalysts, it is not necessary toeliminate cocatalysts from the catalyst composition. The activationfunction of the activator-support is evident in the enhanced activity ofcatalyst composition as a whole, as compared to a catalyst compositioncontaining the corresponding untreated solid oxide. However, it isbelieved that the chemically-treated solid oxide can function as anactivator, even in the absence of an organoaluminum compound,aluminoxanes, organoboron compounds, or ionizing ionic compounds.

In one aspect, the chemically-treated solid oxide of this inventioncomprises a solid inorganic oxide material, a mixed oxide material, or acombination of inorganic oxide materials, that is chemically-treatedwith an electron-withdrawing component, and optionally treated with ametal. Thus, the solid oxide of this invention encompasses oxidematerials such as alumina, “mixed oxide” compounds thereof such assilica-alumina, and combinations and mixtures thereof. The mixed oxidecompounds such as silica-alumina can be single or multiple chemicalphases with more than one metal combined with oxygen to form a solidoxide compound, and are encompassed by this invention.

In one aspect of this invention, the chemically-treated solid oxidefurther comprises a metal or metal ion selected from zinc, nickel,vanadium, titanium, silver, copper, gallium, tin, tungsten, molybdenum,or any combination thereof. Examples of chemically-treated solid oxidesthat further comprise a metal or metal ion include, but are not limitedto, zinc-impregnated chlorided alumina, titanium-impregnated fluoridedalumina, zinc-impregnated fluorided alumina, zinc-impregnated chloridedsilica-alumina, zinc-impregnated fluorided silica-alumina,zinc-impregnated sulfated alumina, chlorided zinc aluminate, fluoridedzinc aluminate, sulfated zinc aluminate, or any combination thereof.

In another aspect, the chemically-treated solid oxide of this inventioncomprises a solid oxide of relatively high porosity, which exhibitsLewis acidic or Brønsted acidic behavior. The solid oxide ischemically-treated with an electron-withdrawing component, typically anelectron-withdrawing anion, to form an activator-support. While notintending to be bound by the following statement, it is believed thattreatment of the inorganic oxide with an electron-withdrawing componentaugments or enhances the acidity of the oxide. Thus in one aspect, theactivator-support exhibits Lewis or Brønsted acidity which is typicallygreater than the Lewis or Brønsted acid strength than the untreatedsolid oxide, or the activator-support has a greater number of acid sitesthan the untreated solid oxide, or both. One method to quantify theacidity of the chemically-treated and untreated solid oxide materials isby comparing the polymerization activities of the treated and untreatedoxides under acid catalyzed reactions.

In one aspect, the chemically-treated solid oxide comprises a solidinorganic oxide comprising oxygen and at least one element selected fromGroup 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, or 15 of the periodictable, or comprising oxygen and at least one element selected from thelanthanide or actinide elements. (See: Hawley's Condensed ChemicalDictionary, 11^(th) Ed., John Wiley & Sons; 1995; Cotton, F. A.;Wilkinson, G.; Murillo; C. A.; and Bochmann; M. Advanced InorganicChemistry, 6^(th) Ed., Wiley-Interscience, 1999.) In another aspect, forexample, the inorganic oxide comprises oxygen and at least one elementselected from Al, B, Be, Bi, Cd, Co, Cr, Cu, Fe, Ga, La, Mn, Mo, Ni, Sb,Si, Sn, Sr, Th, Ti, V, W, P, Y, Zn or Zr.

Suitable examples of solid oxide materials or compounds that can be usedin the chemically-treated solid oxide of the present invention include,but are not limited to, Al₂O₃, B₂O₃, BeO, Bi₂O₃, CdO, Co₃O₄, Cr₂O₃, CuO,Fe₂O₃, Ga₂O₃, La₂O₃, Mn₂O₃, MoO₃, NiO, P₂O₅, Sb₂O₅, SiO₂, SnO₂, SrO,ThO₂, TiO₂, V₂O₅, WO₃, Y₂O₃, ZnO, ZrO₂, and the like, including mixedoxides thereof, and combinations thereof. Examples of mixed oxides thatcan be used in the activator-support of the present invention include,but are not limited to, silica-alumina, silica-titania, silica-zirconia,zeolites, many clay minerals, alumina-titania, alumina-zirconia,zinc-aluminate and the like.

In one aspect of this invention, the solid oxide material ischemically-treated by contacting it with at least oneelectron-withdrawing component, typically an electron-withdrawing anionsource. Further, the solid oxide material is optionallychemically-treated with a metal ion, then calcining to form ametal-containing or metal-impregnated chemically-treated solid oxide.Alternatively, a solid oxide material and an electron-withdrawing anionsource are contacted and calcined simultaneously. The method by whichthe oxide is contacted with an electron-withdrawing component, typicallya salt or an acid of an electron-withdrawing anion, includes, but is notlimited to, gelling, co-gelling, impregnation of one compound ontoanother, and the like. In one aspect, for example, following anycontacting method, the contacted mixture of oxide compound,electron-withdrawing anion, and optionally the metal ion is calcined.

The electron-withdrawing component used to treat the oxide is anycomponent that increases the Lewis or Brønsted acidity of the solidoxide upon treatment. In one aspect, the electron-withdrawing componentis an electron-withdrawing anion derived from a salt, an acid, or othercompound such as a volatile organic compound that may serve as a sourceor precursor for that anion. Examples of electron-withdrawing anionsinclude, but are not limited to, sulfate, bisulfate, fluoride, chloride,bromide, iodide, fluorosulfate, fluoroborate, phosphate,fluorophosphate, trifluoroacetate, triflate, fluorozirconate,fluorotitanate, trifluoroacetate, triflate, and the like, includingmixtures and combinations thereof. In addition, other ionic or non-ioniccompounds that serve as sources for these electron-withdrawing anionsmay also be employed in the present invention.

When the electron-withdrawing component comprises a salt of anelectron-withdrawing anion, the counterion or cation of that salt may beselected from any cation that allows the salt to revert or decomposeback to the acid during calcining. Factors that dictate the suitabilityof the particular salt to serve as a source for the electron-withdrawinganion include, but are not limited to, the solubility of the salt in thedesired solvent, the lack of adverse reactivity of the cation,ion-pairing effects between the cation and anion, hygroscopic propertiesimparted to the salt by the cation, and the like, and thermal stabilityof the anion. Examples of suitable cations in the salt of theelectron-withdrawing anion include, but are not limited to, ammonium,trialkyl ammonium, tetraalkyl ammonium, tetraalkyl phosphonium, H⁺,[H(OEt₂)₂]⁺, and the like.

Further, combinations of one or more different electron-withdrawinganions, in varying proportions, can be used to tailor the specificacidity of the activator-support to the desired level. Combinations ofelectron-withdrawing components may be contacted with the oxide materialsimultaneously or individually, and any order that affords the desiredchemically-treated solid oxide acidity. For example, one aspect of thisinvention is employing two or more electron-withdrawing anion sourcecompounds in two or more separate contacting steps. Thus, one example ofsuch a process by which an chemically-treated solid oxide is prepared isas follows: a selected solid oxide compound, or combination of oxidecompounds, is contacted with a first electron-withdrawing anion sourcecompound to form a first mixture, this first mixture is then calcined,the calcined first mixture is then contacted with a secondelectron-withdrawing anion source compound to form a second mixture,followed by calcining said second mixture to form a treated solid oxidecompound. In such a process, the first and second electron-withdrawinganion source compounds are typically different compounds, although theymay be the same compound.

In one aspect of the invention, the solid oxide activator-support(chemically-treated solid oxide) may be produced by a processcomprising:

1 ) contacting a solid oxide compound with at least oneelectron-withdrawing anion source compound to form a first mixture; and

2) calcining the first mixture to form the solid oxideactivator-support.

In another aspect of this invention, the solid oxide activator-support(chemically-treated solid oxide) is produced by a process comprising:

1) contacting at least one solid oxide compound with a firstelectron-withdrawing anion source compound to form a first mixture; and

2) calcining the first mixture to produce a calcined first mixture;

3) contacting the calcined first mixture with a secondelectron-withdrawing anion source compound to form a second mixture; and

4) calcining the second mixture to form the solid oxideactivator-support.

Thus, the solid oxide activator-support is sometimes referred to simplyas a treated solid oxide compound.

Another aspect of this invention is producing or forming thechemically-treated solid oxide by contacting at least one solid oxidewith at least one electron-withdrawing anion source compound, whereinthe at least one solid oxide compound is calcined before, during orafter contacting the electron-withdrawing anion source, and whereinthere is a substantial absence of aluminoxanes and organoborates.

In one aspect of this invention, once the solid oxide has been treatedand dried, it may be subsequently calcined. Calcining of the treatedsolid oxide is generally conducted in an ambient atmosphere, typicallyin a dry ambient atmosphere, at a temperature from about 200° C. toabout 900° C., and for a time of about 1 minute to about 100 hours. Inanother aspect, calcining is conducted at a temperature from about 300°C. to about 800° C. and in another aspect, calcining is conducted at atemperature from about 400° C. to about 700° C. In yet another aspect,calcining is conducted from about 1 hour to about 50 hours, and inanother aspect calcining is conducted, from about 3 hours to about 20hours. In still another aspect, calcining may be carried out from about1 to about 10 hours at a temperature from about 350° C. to about 550° C.

Further, any type of suitable ambient can be used during calcining.Generally, calcining is conducted in an oxidizing atmosphere, such asair. Alternatively, an inert atmosphere, such as nitrogen or argon, or areducing atmosphere such as hydrogen or carbon monoxide, may be used.

In another aspect of the invention, the solid oxide component used toprepare the chemically-treated solid oxide has a pore volume greaterthan about 0.1 cc/g. In another aspect, the solid oxide component has apore volume greater than about 0.5 cc/g, and in yet another aspect,greater than about 1.0 cc/g. In still another aspect, the solid oxidecomponent has a surface area from about 100 to about 1000 m²/g. Inanother aspect, solid oxide component has a surface area from about 200to about 800 m²/g, and in still another aspect, from about 250 to about600 m²/g.

The solid oxide material may be treated with a source of halide ion orsulfate ion, or a combination of anions, and optionally treated with ametal ion, then calcined to provide the chemically-treated solid oxidein the form of a particulate solid. In one aspect, the solid oxidematerial is treated with a source of sulfate, termed a sulfating agent,a source of chloride ion, termed a chloriding agent, a source offluoride ion, termed a fluoriding agent, or a combination thereof, andcalcined to provide the solid oxide activator. In another aspect, usefulacidic activator-supports include, but are not limited to: bromidedalumina; chlorided alumina; fluorided alumina; sulfated alumina;bromided silica-alumina, chlorided silica-alumina; fluoridedsilica-alumina; sulfated silica-alumina; bromided silica-zirconia,chlorided silica-zirconia; fluorided silica-zirconia; sulfatedsilica-zirconia; a pillared clay such as a pillared montmorillonite,optionally treated with fluoride, chloride, or sulfate; phosphatedalumina, or other aluminophosphates, optionally treated with sulfate,fluoride, or chloride; or any combination thereof. Further, any of theactivator-supports may optionally be treated with a metal ion.

In one aspect of this invention, the chemically-treated solid oxidecomprises a fluorided solid oxide in the form of a particulate solid,thus a source of fluoride ion is added to the oxide by treatment with afluoriding agent. In still another aspect, fluoride ion may be added tothe oxide by forming a slurry of the oxide in a suitable solvent such asalcohol or water, including, but are not limited to, the one to threecarbon alcohols because of their volatility and low surface tension.Examples of fluoriding agents that can be used in this inventioninclude, but are not limited to, hydrofluoric acid (HF), ammoniumfluoride (NH₄F), ammonium bifluoride (NH₄HF₂), ammoniumtetrafluoroborate (NH₄BF₄), ammonium silicofluoride (hexafluorosilicate)((NH₄)₂SiF₆), ammonium hexafluorophosphate (NH₄PF₆), analogs thereof,and combinations thereof. For example, ammonium bifluoride NH₄HF₂ may beused as the fluoriding agent, due to its ease of use and readyavailability.

In another aspect of the present invention, the solid oxide can betreated with a fluoriding agent during the calcining step. Anyfluoriding agent capable of thoroughly contacting the solid oxide duringthe calcining step can be used. For example, in addition to thosefluoriding agents described previously, volatile organic fluoridingagents may be used. Examples of volatile organic fluoriding agentsuseful in this aspect of the invention include, but are not limited to,freons, perfluorohexane, perfluorobenzene, fluoromethane,trifluoroethanol, and combinations thereof. Gaseous hydrogen fluoride orfluorine itself can also be used with the solid oxide is fluoridedduring calcining. One convenient method of contacting the solid oxidewith the fluoriding agent is to vaporize a fluoriding agent into a gasstream used to fluidize the solid oxide during calcination.

Similarly, in another aspect of this invention, the chemically-treatedsolid oxide can comprise a chlorided solid oxide in the form of aparticulate solid, thus a source of chloride ion is added to the oxideby treatment with a chloriding agent. The chloride ion may be added tothe oxide by forming a slurry of the oxide in a suitable solvent. Inanother aspect of the present invention, the solid oxide can be treatedwith a chloriding agent during the calcining step. Any chloriding agentcapable of serving as a source of chloride and thoroughly contacting theoxide during the calcining step can be used. For example, volatileorganic chloriding agents may be used. Examples of volatile organicchloriding agents useful in this aspect of the invention include, butare not limited to, certain freons, perchlorobenzene, chloromethane,dichloromethane, chloroform, carbon tetrachloride, trichloroethanol, orany combination thereof. Gaseous hydrogen chloride or chlorine itselfcan also be used with the solid oxide during calcining. One convenientmethod of contacting the oxide with the chloriding agent is to vaporizea chloriding agent into a gas stream used to fluidize the solid oxideduring calcination.

In one aspect, the amount of fluoride or chloride ion present beforecalcining the solid oxide is generally from about 2 to about 50% byweight, where the weight percents are based on the weight of the solidoxide, for example silica-alumina, before calcining. In another aspect,the amount of fluoride or chloride ion present before calcining thesolid oxide is from about 3 to about 25% by weight, and in anotheraspect, from about 4 to about 20% by weight. Once impregnated withhalide, the halided oxide may be dried by any method known in the artincluding, but not limited to, suction filtration followed byevaporation, drying under vacuum, spray drying, and the like, althoughit is also possible to initiate the calcining step immediately withoutdrying the impregnated solid oxide.

The silica-alumina used to prepare the treated silica-alumina can have apore volume greater than about 0.5 cc/g. In one aspect, the pore volumemay be greater than about 0.8 cc/g, and in another aspect, the porevolume may be greater than about 1.0 cc/g. Further, the silica-aluminamay have a surface area greater than about 100 m²/g. In one aspect, thesurface area is greater than about 250 m²/g, and in another aspect, thesurface area may be greater than about 350 m²/g. Generally, thesilica-alumina of this invention has an alumina content from about 5 toabout 95%. In one aspect, the alumina content of the silica-alumina maybe from about 5 to about 50%, and in another aspect, the alumina contentof the silica-alumina may be from about 8% to about 30% alumina byweight. In yet another aspect, the solid oxide component can comprisealumina without silica and in another aspect, the solid oxide componentcan comprise silica without alumina.

The sulfated solid oxide comprises sulfate and a solid oxide componentsuch as alumina or silica-alumina, in the form of a particulate solid.Optionally, the sulfated oxide is further treated with a metal ion suchthat the calcined sulfated oxide comprises a metal. In one aspect, thesulfated solid oxide comprises sulfate and alumina. In one aspect ofthis invention, the sulfated alumina is formed by a process wherein thealumina is treated with a sulfate source, for example selected from, butnot limited to, sulfuric acid or a sulfate salt such as ammoniumsulfate. In one aspect, this process may be performed by forming aslurry of the alumina in a suitable solvent such as alcohol or water, inwhich the desired concentration of the sulfating agent has been added.Suitable organic solvents include, but are not limited to, the one tothree carbon alcohols because of their volatility and low surfacetension.

In one aspect of the invention, the amount of sulfate ion present beforecalcining is generally from about 0.5 parts by weight to about 100 partsby weight sulfate ion to about 100 parts by weight solid oxide. Inanother aspect, the amount of sulfate ion present before calcining isgenerally from about 1 part by weight to about 50 parts by weightsulfate ion to about 100 parts by weight solid oxide, and in stillanother aspect, from about 5 parts by weight to about 30 parts by weightsulfate ion to about 100 parts by weight solid oxide. These weightratios are based on the weight of the solid oxide before calcining. Onceimpregnated with sulfate, the sulfated oxide may be dried by any methodknown in the art including, but not limited to, suction filtrationfollowed by evaporation, drying under vacuum, spray drying, and thelike, although it is also possible to initiate the calcining stepimmediately.

In addition to being treated with an electron-withdrawing component suchas halide or sulfate ion, the solid inorganic oxide of this inventionmay optionally be treated with a metal source, including metal salts ormetal-containing compounds. In one aspect of the invention, thesecompounds may be added to or impregnated onto the solid oxide insolution form, and subsequently converted into the supported metal uponcalcining. Accordingly, in one aspect, the solid inorganic oxide canfurther comprise a metal selected from zinc, titanium, nickel, vanadium,silver, copper, gallium, tin, tungsten, molybdenum, or a combinationthereof. For example, zinc may be used to impregnate the solid oxidebecause it provides good catalyst activity and low cost. The solid oxidemay be treated with metal salts or metal-containing compounds before,after, or at the same time that the solid oxide is treated with theelectron-withdrawing anion.

Further, any method of impregnating the solid oxide material with ametal may be used. The method by which the oxide is contacted with ametal source, typically a salt or metal-containing compound, includes,but is not limited to, gelling, co-gelling, impregnation of one compoundonto another, and the like. Following any contacting method, thecontacted mixture of oxide compound, electron-withdrawing anion, and themetal ion is typically calcined. Alternatively, a solid oxide material,an electron-withdrawing anion source, and the metal salt ormetal-containing compound are contacted and calcined simultaneously.

In another aspect, the first metallocene compound, the secondmetallocene compound, or a combination thereof, may be precontacted withan olefin monomer and an organoaluminum compound for a first period oftime prior to contacting this mixture with the chemically-treated solidoxide. Once the precontacted mixture of the first metallocene compound,the second metallocene compound, or a combination thereof, olefinmonomer, organoaluminum compound is contacted with thechemically-treated solid oxide, the composition further comprising thechemically-treated solid oxide is termed the “postcontacted” mixture.The postcontacted mixture may be allowed to remain in further contactfor a second period of time prior to being charged into the reactor inwhich the polymerization process will be carried out.

Various processes to prepare solid oxide activator-supports that can beemployed in this invention have been reported. For example, U.S. Pat.Nos. 6,107,230, 6,165,929, 6,294,494, 6,300,271, 6,316,553, 6,355,594,6,376,415, 6,391,816, 6,395,666, 6,524,987, and 6,548,441, describe suchmethods, each of which is incorporated by reference herein, in itsentirety.

The Organoaluminum Compound

In one aspect, this invention encompasses a catalyst compositioncomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. In this aspect, for example, organoaluminumcompounds that can be used in this invention include, but are notlimited to compound with the formula:Al(X⁹)_(n)(X¹⁰)_(3-n),wherein (X⁹) is a hydrocarbyl having from 1 to about 20 carbon atoms;(X¹⁰) is selected from alkoxide or aryloxide, any one of which havingfrom 1 to about 20 carbon atoms, halide, or hydride; and n is a numberfrom 1 to 3, inclusive. In one aspect, (X⁹) is an alkyl having from 1 toabout 10 carbon atoms. Examples of (X⁹) moieties include, but are notlimited to, ethyl, propyl, n-butyl, sec-butyl, isobutyl, hexyl, and thelike. In another aspect, (X¹⁰) may be independently selected from fluoroor chloro. In yet another aspect, (X¹⁰) may be chloro.

In the formula Al(X⁹)_(n)(X¹⁰)_(3-n), n is a number from 1 to 3inclusive, and typically, n is 3. The value of n is not restricted to bean integer, therefore this formula includes sesquihalide compounds orother organoaluminum cluster compounds.

In another aspect, examples of organoaluminum compounds that can be usedin this invention include, but are not limited to, trialkylaluminumcompounds, dialkylaluminium halide compounds, dialkylaluminum alkoxidecompounds, dialkylaluminum hydride compounds, and combinations thereof.Specific examples of organoaluminum compounds that are useful in thisinvention include, but are not limited to: trimethylaluminum (TMA);triethylaluminum (TEA); tripropylaluminum; diethylaluminum ethoxide;tributylaluminum; disobutylaluminum hydride; triisobutylaluminum; anddiethylaluminum chloride.

In one aspect, the present invention comprises precontacting theansa-metallocene with at least one organoaluminum compound and an olefinmonomer to form a precontacted mixture, prior to contact thisprecontacted mixture with the solid oxide activator-support to form theactive catalyst. When the catalyst composition is prepared in thismanner, typically, though not necessarily, a portion of theorganoaluminum compound is added to the precontacted mixture and anotherportion of the organoaluminum compound is added to the postcontactedmixture prepared when the precontacted mixture is contacted with thesolid oxide activator. However, all the organoaluminum compound may beused to prepare the catalyst in either the precontacting orpostcontacting step. Alternatively, all the catalyst components may becontacted in a single step.

Further, more than one organoaluminum compounds may be used, in eitherthe precontacting or the postcontacting step. When an organoaluminumcompound is added in multiple steps, the amounts of organoaluminumcompound disclosed herein include the total amount of organoaluminumcompound used in both the precontacted and postcontacted mixtures, andany additional organoaluminum compound added to the polymerizationreactor. Therefore, total amounts of organoaluminum compounds aredisclosed, regardless of whether a single organoaluminum compound isused, or more than one organoaluminum compound. In another aspect,triethylaluminum (TEA) or triisobutylaluminum are typical organoaluminumcompounds used in this invention.

The Optional Aluminoxane Cocatalyst

In one aspect, this invention encompasses a catalyst compositioncomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. In another aspect, the present inventionprovides a catalyst composition comprising an optional aluminoxanecocatalyst in addition to these other components.

Aluminoxanes are also referred to as poly(hydrocarbyl aluminum oxides)or organoaluminoxanes. The other catalyst components are typicallycontacted with the aluminoxane in a saturated hydrocarbon compoundsolvent, though any solvent which is substantially inert to thereactants, intermediates, and products of the activation step can beused. The catalyst composition formed in this manner may be collected bymethods known to those of skill in the art, including but not limited tofiltration, or the catalyst composition may be introduced into thepolymerization reactor without being isolated.

The aluminoxane compound of this invention is an oligomeric aluminumcompound, wherein the aluminoxane compound can comprise linearstructures, cyclic, or cage structures, or typically mixtures of allthree. Cyclic aluminoxane compounds having the formula:

R is a linear or branched alkyl having from 1 to 10 carbon atoms, and nis an integer from 3 to about 10 are encompassed by this invention. The(AlRO)_(n) moiety shown here also constitutes the repeating unit in alinear aluminoxane. Thus, linear aluminoxanes having the formula:

R is a linear or branched alkyl having from 1 to 10 carbon atoms, and nis an integer from 1 to about 50, are also encompassed by thisinvention.

Further, aluminoxanes may also have cage structures of the formula R^(t)_(5m+α)R^(b) _(m−α)Al_(4m)O_(3m), wherein m is 3 or 4 and αis=n_(Al(3))−n_(O(2))+n_(O(4)); wherein n_(Al(3)) is the number of threecoordinate aluminum atoms, n_(O(2)) is the number of two coordinateoxygen atoms, n_(O(4)) is the number of 4 coordinate oxygen atoms, R^(t)represents a terminal alkyl group, and R^(b) represents a bridging alkylgroup; wherein R is a linear or branched alkyl having from 1 to 10carbon atoms.

Thus, aluminoxanes that can serve as optional cocatalysts in thisinvention are generally represented by formulas such as (R—Al—O)_(n),R(R—Al—O)_(n)AlR₂, and the like, wherein the R group is typically alinear or branched C₁-C₆ alkyl such as methyl, ethyl, propyl, butyl,pentyl, or hexyl wherein n typically represents an integer from 1 toabout 50. In one embodiment, the aluminoxane compounds of this inventioninclude, but are not limited to, methylaluminoxane, ethylaluminoxane,n-propylaluminoxane, iso-propylaluminoxane, n-butylaluminoxane,t-butylaluminoxane, sec-butylaluminoxane, iso-butylaluminoxane,1-pentylaluminoxane, 2-pentylaluminoxane, 3-pentylaluminoxane,iso-pentylaluminoxane, neopentylaluminoxane, or combinations thereof.

While organoaluminoxanes with different types of R groups areencompassed by the present invention, methyl aluminoxane (MAO), ethylaluminoxane, or isobutyl aluminoxane are typical optional cocatalystsused in the catalyst compositions of this invention. These aluminoxanesare prepared from trimethylaluminum, triethylaluminum, ortriisobutylaluminum, respectively, and are sometimes referred to aspoly(methyl aluminum oxide), poly(ethyl aluminum oxide), andpoly(isobutyl aluminum oxide), respectively. It is also within the scopeof the invention to use an aluminoxane in combination with atrialkylaluminum, such as disclosed in U.S. Pat. No. 4,794,096, which isherein incorporated by reference in its entirety.

The present invention contemplates many values of n in the aluminoxaneformulas (R—Al—O)_(n) and R(R—Al—O)_(n)AlR₂, and preferably n is atleast about 3. However, depending upon how the organoaluminoxane isprepared, stored, and used, the value of n may be variable within asingle sample of aluminoxane, and such a combination oforganoaluminoxanes are comprised in the methods and compositions of thepresent invention.

In preparing the catalyst composition of this invention comprising anoptional aluminoxane, the molar ratio of the aluminum in the alumixoaneto the metallocene in the composition is usually from about 1:10 toabout 100,000:1. In one another aspect, the molar ratio of the aluminumin the alumixoane to the metallocene in the composition is usually fromabout 5:1 to about 15,000:1. The amount of optional aluminoxane added toa polymerization zone is an amount within a range of about 0.01 mg/L toabout 1000 mg/L, from about 0.1 mg/L to about 100 mg/L, or from about 1mg/L to about 50 mg/L.

Organoaluminoxanes can be prepared by various procedures which are wellknown in the art. Examples of organoaluminoxane preparations aredisclosed in U.S. Pat. Nos. 3,242,099 and 4,808,561, each of which isincorporated by reference herein, in its entirety. One example of how analuminoxane may be prepared is as follows. Water which is dissolved inan inert organic solvent may be reacted with an aluminum alkyl compoundsuch as AlR₃ to form the desired organoaluminoxane compound. While notintending to be bound by this statement, it is believed that thissynthetic method can afford a mixture of both linear and cyclic(R—Al—O)_(n) aluminoxane species, both of which are encompassed by thisinvention. Alternatively, organoaluminoxanes may be prepared by reactingan aluminum alkyl compound such as AlR₃ with a hydrated salt, such ashydrated copper sulfate, in an inert organic solvent.

The Optional Organoboron Cocatalyst

In one aspect, this invention encompasses a catalyst compositioncomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. In another aspect, the present inventionprovides a catalyst composition comprising an optional organoboroncocatalyst in addition to these other components.

In one aspect, the organoboron compound comprises neutral boroncompounds, borate salts, or combinations thereof. For example, theorganoboron compounds of this invention can comprise a fluoroorganoboron compound, a fluoroorgano borate compound, or a combinationthereof. Any fluoroorgano boron or fluoroorgano borate compound known inthe art can be utilized. The term fluoroorgano boron compounds has itsusual meaning to refer to neutral compounds of the form BY₃. The termfluoroorgano borate compound also has its usual meaning to refer to themonoanionic salts of a fluoroorgano boron compound of the form[cation]⁺[BY₄]⁻, where Y represents a fluorinated organic group. Forconvenience, fluoroorgano boron and fluoroorgano borate compounds aretypically referred to collectively by organoboron compounds, or byeither name as the context requires.

Examples of fluoroorgano borate compounds that can be used ascocatalysts in the present invention include, but are not limited to,fluorinated aryl borates such as, N,N-dimethylaniliniumtetrakis(pentafluorophenyl)borate, triphenylcarbeniumtetrakis(pentafluorophenyl)borate, lithiumtetrakis(pentafluorophenyl)borate, N,N-dimethylaniliniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbeniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, and the like, includingmixtures thereof. Examples of fluoroorgano boron compounds that can beused as cocatalysts in the present invention include, but are notlimited to, tris(pentafluorophenyl)boron,tris[3,5-bis(trifluoromethyl)phenyl]boron, and the like, includingmixtures thereof.

Although not intending to be bound by the following theory, theseexamples of fluoroorgano borate and fluoroorgano boron compounds, andrelated compounds, are thought to form “weakly-coordinating” anions whencombined with organometal compounds, as disclosed in U.S. Pat. No.5,919,983, which is incorporated herein by reference in its entirety.

Generally, any amount of organoboron compound can be utilized in thisinvention. In one aspect, the molar ratio of the organoboron compound tothe total of the first and second metallocene compounds in thecomposition is from about 0.1:1 to about 10:1. Typically, the amount ofthe fluoroorgano boron or fluoroorgano borate compound used as acocatalyst for the metallocenes is in a range of from about 0.5 mole toabout 10 moles of boron compound per total mole of first and secondmetallocene compounds combined. In one aspect, the amount offluoroorgano boron or fluoroorgano borate compound used as a cocatalystfor the metallocene is in a range of from about 0.8 mole to about 5moles of boron compound per total moles of first and second metallocenecompound.

The Optional Ionizing Ionic Compound Cocatalyst

In one aspect, this invention encompasses a catalyst compositioncomprising a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound. In another aspect, the present inventionprovides a catalyst composition comprising an optional ionizing ioniccompound cocatalyst in addition to these other components. Examples ofionizing ionic compound are disclosed in U.S. Pat. Nos. 5,576,259 and5,807,938, each of which is incorporated herein by reference, in itsentirety.

An ionizing ionic compound is an ionic compound which can function toenhance the activity of the catalyst composition. While not bound bytheory, it is believed that the ionizing ionic compound may be capableof reacting with the first, second, or both metallocene compounds andconverting the metallocenes into a cationic metallocene compounds, orincipient cationic metallocene compounds. Again, while not intending tobe bound by theory, it is believed that the ionizing ionic compound mayfunction as an ionizing compound by completely or partially extractingan anionic ligand, possibly a non-η⁵-alkadienyl ligand such as (X³) or(X⁴), from the metallocenes. However, the ionizing ionic compound is anactivator regardless of whether it is ionizes the metallocenes,abstracts an (X³) or (X⁴) ligand in a fashion as to form an ion pair,weakens the metal-(X³) or metal-(X⁴) bond in the metallocenes, simplycoordinates to an (X³) or (X⁴) ligand, or any other mechanisms by whichactivation may occur.

Further, it is not necessary that the ionizing ionic compound activatethe metallocenes only. The activation function of the ionizing ioniccompound is evident in the enhanced activity of catalyst composition asa whole, as compared to a catalyst composition containing catalystcomposition that does not comprise any ionizing ionic compound. It isalso not necessary that the ionizing ionic compound activate both firstand second metallocene compounds, nor is it necessary that it activatethe first metallocene compound and the second metallocene compounds tothe same extent.

Examples of ionizing ionic compounds include, but are not limited to,the following compounds: tri(n-butyl)ammonium tetrakis(p-tolyl)borate,tri(n-butyl)ammonium tetrakis(m-tolyl)borate, tri(n-butyl)ammoniumtetrakis(2,4-dimethyl)borate, tri(n-butyl)ammoniumtetrakis(3,5-dimethylphenyl)borate, tri(n-butyl)ammoniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tri(n-butyl)ammoniumtetrakis(pentafluorophenyl)borate, N,N-dimethylaniliniumtetrakis(p-tolyl)borate, N,N-dimethylanilinium tetrakis(m-tolyl)borate,N,N-dimethylanilinium tetrakis(2,4-dimethylphenyl)borate,N,N-dimethylanilinium tetrakis(3,5-dimethylphenyl)borate,N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate,N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate,triphenylcarbenium tetrakis(p-tolyl)borate, triphenylcarbeniumtetrakis(m-tolyl)borate, triphenylcarbeniumtetrakis(2,4-dimethylphenyl)borate, triphenylcarbeniumtetrakis(3,5-dimethylphenyl)borate, triphenylcarbeniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbeniumtetrakis(pentafluorophenyl)borate, tropylium tetrakis(p-tolyl)borate,tropylium tetrakis(m-tolyl)borate, tropyliumtetrakis(2,4-dimethylphenyl)borate, tropyliumtetrakis(3,5-dimethylphenyl)borate, tropyliumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tropyliumtetrakis(pentafluorophenyl)borate, lithiumtetrakis(pentafluorophenyl)borate, lithium tetrakis(phenyl)borate,lithium tetrakis(p-tolyl)borate, lithium tetrakis(m-tolyl)borate,lithium tetrakis(2,4-dimethylphenyl)borate, lithiumtetrakis(3,5-dimethylphenyl)borate, lithium tetrafluoroborate, sodiumtetrakis(pentafluorophenyl)borate, sodium tetrakis(phenyl) borate,sodium tetrakis(p-tolyl)borate, sodium tetrakis(m-tolyl)borate, sodiumtetrakis(2,4-dimethylphenyl)borate, sodiumtetrakis(3,5-dimethylphenyl)borate, sodium tetrafluoroborate, potassiumtetrakis(pentafluorophenyl)borate, potassium tetrakis(phenyl)borate,potassium tetrakis(p-tolyl)borate, potassium tetrakis(m-tolyl)borate,potassium tetrakis(2,4-dimethylphenyl)borate, potassiumtetrakis(3,5-dimethylphenyl)borate, potassium tetrafluoroborate,tri(n-butyl)ammonium tetrakis(p-tolyl)aluminate, tri(n-butyl)ammoniumtetrakis(m-tolyl)aluminate, tri(n-butyl)ammoniumtetrakis(2,4-dimethyl)aluminate, tri(n-butyl)ammoniumtetrakis(3,5-dimethylphenyl)aluminate, tri(n-butyl)ammoniumtetrakis(pentafluorophenyl)aluminate, N,N-dimethylaniliniumtetrakis(p-tolyl)aluminate, N,N-dimethylaniliniumtetrakis(m-tolyl)aluminate, N,N-dimethylaniliniumtetrakis(2,4-dimethylphenyl)aluminate, N,N-dimethylaniliniumtetrakis(3,5-dimethylphenyl)aluminate, N,N-dimethylaniliniumtetrakis(pentafluorophenyl)aluminate, triphenylcarbeniumtetrakis(p-tolyl)aluminate, triphenylcarbeniumtetrakis(m-tolyl)aluminate, triphenylcarbeniumtetrakis(2,4-dimethylphenyl)aluminate, triphenylcarbeniumtetrakis(3,5-dimethylphenyl)aluminate, triphenylcarbeniumtetrakis(pentafluorophenyl)aluminate, tropyliumtetrakis(p-tolyl)aluminate, tropylium tetrakis(m-tolyl)aluminate,tropylium tetrakis(2,4-dimethylphenyl)aluminate, tropyliumtetrakis(3,5-dimethylphenyl)aluminate, tropyliumtetrakis(pentafluorophenyl)aluminate, lithiumtetrakis(pentafluorophenyl)aluminate, lithium tetrakis(phenyl)aluminate,lithium tetrakis(p-tolyl)aluminate, lithium tetrakis(m-tolyl)aluminate,lithium tetrakis(2,4-dimethylphenyl)aluminate, lithiumtetrakis(3,5-dimethylphenyl)aluminate, lithium tetrafluoroaluminate,sodium tetrakis(pentafluorophenyl)aluminate, sodiumtetrakis(phenyl)aluminate, sodium tetrakis(p-tolyl)aluminate, sodiumtetrakis(m-tolyl)aluminate, sodiumtetrakis(2,4-dimethylphenyl)aluminate, sodiumtetrakis(3,5-dimethylphenyl)aluminate, sodium tetrafluoroaluminate,potassium tetrakis(pentafluorophenyl)aluminate, potassiumtetrakis(phenyl)aluminate, potassium tetrakis(p-tolyl)aluminate,potassium tetrakis(m-tolyl)aluminate, potassiumtetrakis(2,4-dimethylphenyl)aluminate, potassiumtetrakis(3,5-dimethylphenyl)aluminate, potassium tetrafluoroaluminate,and the like. However, the optional ionizing ionic compounds that areuseful in this invention are not limited to these.

The Olefin Monomer

In one aspect, unsaturated reactants that are useful in thepolymerization processes with catalyst compositions and processes ofthis invention typically include olefin compounds having from about 2 toabout 30 carbon atoms per molecule and having at least one olefinicdouble bond. This invention encompasses homopolymerization processesusing a single olefin such as ethylene or propylene, as well ascopolymerization reactions with at least one different olefiniccompound. In one aspect of a copolymerization reaction of ethylene,copolymers of ethylene comprise a major amount of ethylene (>50 molepercent) and a minor amount of comonomer <50 mole percent), though thisis not a requirement. The comonomers that can be copolymerized withethylene should have from three to about 20 carbon atoms in theirmolecular chain.

Acyclic, cyclic, polycyclic, terminal (α), internal, linear, branched,substituted, unsubstituted, functionalized, and non-functionalizedolefins may be employed in this invention. For example, typicalunsaturated compounds that may be polymerized with the catalysts of thisinvention include, but are not limited to, propylene, 1-butene,2-butene, 3-methyl-1-butene, isobutylene, 1-pentene, 2-pentene,3-methyl-1-pentene, 4-methyl-1-pentene, 1-hexene, 2-hexene, 3-hexene,3-ethyl-1-hexene, 1-heptene, 2-heptene, 3-heptene, the four normaloctenes, the four normal nonenes, the five normal decenes, and mixturesof any two or more thereof. Cyclic and bicyclic olefins, including butnot limited to, cyclopentene, cyclohexene, norbornylene, norbornadiene,and the like, may also be polymerized as described above.

In one aspect, when a copolymer is desired, the monomer ethylene may becopolymerized with a comonomer. In another aspect, examples of thecomonomer include, but are not limited to, propylene, 1-butene,2-butene, 3-methyl-1-butene, isobutylene, 1-pentene, 2-pentene,3-methyl-1-pentene, 4-methyl-1-pentene, 1-hexene, 2-hexene, 3-hexene,3-ethyl-1-hexene, 1-heptene, 2-heptene, 3-heptene, the four normaloctenes, the four normal nonenes, or the five normal decenes. In anotheraspect, the comonomer may be selected from 1-butene, 1-pentene,1-hexene, 1-octene, 1-decene, or styrene.

In one aspect, the amount of comonomer introduced into a reactor zone toproduce the copolymer is generally from about 0.01 to about 50 weightpercent comonomer based on the total weight of the monomer andcomonomer. In another aspect, the amount of comonomer introduced into areactor zone is from about 0.01 to about 40 weight percent comonomer,and in still another aspect, from about 0.1 to about 35 weight percentcomonomer based on the total weight of the monomer and comonomer.Alternatively, an amount sufficient to give the above describedconcentrations by weight, in the copolymer produced can be used.

While not intending to be bound by this theory, in the event thatbranched, substituted, or functionalized olefins are used as reactants,it is believed that steric hindrance may impede and/or slow thepolymerization process. Thus, branched and/or cyclic portion(s) of theolefin removed somewhat from the carbon-carbon double bond would not beexpected to hinder the reaction in the way that the same olefinsubstituents situated more proximate to the carbon-carbon double bondmight. In one aspect, at least one reactant for the catalystcompositions of this invention is ethylene, so the polymerizations areeither homopolymerizations or copolymerizations with a differentacyclic, cyclic, terminal, internal, linear, branched, substituted, orunsubstituted olefin. In addition, the catalyst compositions of thisinvention may be used in polymerization of diolefin compounds, includingbut are not limited to, 1,3-butadiene, isoprene, 1,4-pentadiene, and1,5-hexadiene.

Preparation of the Catalyst Composition

In one aspect, this invention encompasses a catalyst compositioncomprising the contact product of a first metallocene compound, a secondmetallocene compound, at least one chemically-treated solid oxide, andat least one organoaluminum compound. In another aspect, this inventionencompasses methods of making the catalyst composition encompassingcontacting a first metallocene compound, a second metallocene compound,at least one chemically-treated solid oxide, and at least oneorganoaluminum compound, in any order. In this aspect, an activecatalyst composition is obtained with the catalyst components arecontacted in any sequence or order.

In another aspect of this invention, the first metallocene compound, thesecond metallocene compound, or both can optionally be precontacted withan olefinic monomer, not necessarily the olefin monomer to bepolymerized, and an organoaluminum cocatalyst for a first period of timeprior to contacting this precontacted mixture with the chemicallytreated solid oxide. In one aspect, the first period of time forcontact, the precontact time, between the metallocene compound orcompounds, the olefinic monomer, and the organoaluminum compoundtypically range from time about 0.1 hour to about 24 hours, and fromabout 0.1 to about 1 hour is typical. Precontact times from about 10minutes to about 30 minutes are also typical.

In yet another aspect of this invention, once the precontacted mixtureof the first, second, or both metallocene compounds, olefin monomer, andorganoaluminum cocatalyst is contacted with the chemically treated solidoxide, this composition (further comprising the chemically treated solidoxide) is termed the postcontacted mixture. Typically, the postcontactedmixture may optionally be allowed to remain in contact for a secondperiod of time, the postcontact time, prior to being initiating thepolymerization process. In one aspect, postcontact times between theprecontacted mixture and the chemically treated solid oxide may range intime from about 0.1 hour to about 24 hours. In another aspect, forexample, postcontact times from about 0.1 hour to about 1 hour aretypical.

In one aspect, the precontacting, the postcontacting step, or both mayincrease the productivity of the polymer as compared to the samecatalyst composition that is prepared without precontacting orpostcontacting. However, neither a precontacting step nor apostcontacting step are required for this invention.

The postcontacted mixture may be heated at a temperature and for aduration sufficient to allow adsorption, impregnation, or interaction ofprecontacted mixture and the chemically treated solid oxide, such that aportion of the components of the precontacted mixture is immobilized,adsorbed, or deposited thereon. For example, the postcontacted mixturemay be heated from between about 0° F. to about 150° F. Temperaturesbetween about 40° F. to about 95° F. are typical if the mixture isheated at all.

In one aspect, the molar ratio of the total moles of first and secondmetallocene compounds combined to the organoaluminum compound may befrom about 1:1 to about 1:10,000. In another aspect, the molar ratio ofthe total moles of first and second metallocene compounds combined tothe organoaluminum compound may be from about 1:1 to about 1:1,000, andin another aspect, from about 1:1 to about 1:100. These molar ratiosreflect the ratio of the total moles of first and second metallocenecompounds combined to the total amount of organoaluminum compound inboth the precontacted mixture and the postcontacted mixture combined.

When a precontacting step is used, generally, the molar ratio of olefinmonomer to total moles of first and second metallocene compoundscombined in the precontacted mixture may be from about 1:10 to about100,000:1, or from about 10:1 to about 1,000:1.

In another aspect of this invention, the weight ratio of the chemicallytreated solid oxide to the organoaluminum compound may range from about1:5 to about 1,000:1. In another aspect, the weight ratio of thechemically treated solid oxide to the organoaluminum compound may befrom about 1:3 to about 100:1, and in yet another aspect, from about 1:1to about 50:1.

In a further aspect of this invention, the weight ratio of the first andsecond metallocene compounds combined to the chemically treated solidoxide may be from about 1:1 to about 1:1,000,000. In yet another aspectof this invention, the weight ratio of the total moles of first andsecond metallocene compounds combined to the chemically treated solidoxide which may be from about 1:10 to about 1:100,00, and in anotheraspect, from about 1:20 to about 1:1000.

One aspect of this invention is that aluminoxane is not required to formthe catalyst composition disclosed herein, a feature that allows lowerpolymer production costs. Accordingly, in one aspect, the presentinvention can use AlR₃-type organoaluminum compounds and a chemicallytreated solid oxide in the absence of aluminoxanes. While not intendingto be bound by theory, it is believed that the organoaluminum compoundslikely does not activate the metallocene catalyst in the same manner asan organoaluminoxane.

Additionally, no expensive borate compounds or MgCl₂ are required toform the catalyst composition of this invention, although aluminoxanes,organoboron compounds, ionizing ionic compounds, organozinc compounds,MgCl₂, or any combination thereof can optionally be used in the catalystcomposition of this invention. Further, in one aspect, cocatalysts suchas aluminoxanes, organoboron compounds, ionizing ionic compounds,organozinc compounds, or any combination thereof may be used ascocatalysts with the first and second metallocene compounds, either inthe presence or in the absence of the chemically treated solid oxide,and either in the presence or in the absence of the organoaluminumcompounds.

In one aspect, the catalyst activity of the catalyst of this inventionis typically greater than or equal to about 100 grams polyethylene pergram of chemically treated solid oxide per hour (abbreviatedgP/(gCTSO•hr)). In another aspect, the catalyst of this invention may becharacterized by an activity of greater than or equal to about 250gP/(gCTSO•hr), and in another aspect, an activity of greater than orequal to about 500 gP/(gCTSO•hr). In still another aspect, the catalystof this invention may be characterized by an activity of greater than orequal to about 1000 gP/(gCTSO•hr), and in another aspect, an activity ofgreater than or equal to about 2000 gP/(gCTSO•hr). This activity ismeasured under slurry polymerization conditions, using isobutane as thediluent, and with a polymerization temperature of about 90° C., and anethylene pressure of about 550 psig. The reactor should havesubstantially no indication of any wall scale, coating or other forms offouling upon making these measurements.

In still another aspect of this invention, any combination of the firstmetallocene compound, the second metallocene compound, thechemically-treated solid oxide, the organoaluminum compound, and theolefin monomer, can optionally be precontacted. In this aspect, when anyprecontacting occurs with an olefinic monomer, it is not necessary thatthe olefin monomer used in the precontacting step be the same as theolefin to be polymerized. Further, in one aspect, when a precontactingstep among any combination of the catalyst components is employed for afirst period of time prior, this precontacted mixture may be used in asubsequent, postcontacting step between any other combination ofcatalyst components for a second period of time. In one aspect, forexample, all the catalyst components and 1-hexene can be used in aprecontacting step for a first period of time, and this precontactedmixture can then be contacted with the chemically treated solid oxide toform a postcontacted mixture, that is contacted for a second period oftime prior to initiating the polymerization reaction. In one aspect, forexample, the first period of time for contact, the precontact time,between any combination of the first metallocene compound, the secondmetallocene compound, the olefinic monomer, the chemically-treated solidoxide, and the organoaluminum compound typically range from time about0.1 hour to about 24 hours, and from about 0.1 to about 1 hour istypical. Precontact times from about 10 minutes to about 30 minutes arealso typical. In this aspect, the postcontacted mixture may optionallybe allowed to remain in contact for a second period of time, thepostcontact time, prior to being initiating the polymerization process.In one aspect, postcontact times between the precontacted mixture andany remaining catalyst components may range in time from about 0.1 hourto about 24 hours. In another aspect, for example, postcontact timesfrom about 0.1 hour to about 1 hour are typical.

Utility of the Catalyst Composition in Polymerization Processes

Polymerizations using the catalysts of this invention can be carried outin any manner known in the art. Such polymerization processes include,but are not limited to slurry polymerizations, gas phasepolymerizations, solution polymerizations, and the like, includingmulti-reactor combinations thereof. Thus, any polymerization zone knownin the art to produce ethylene-containing polymers can be utilized. Forexample, a stirred reactor can be utilized for a batch process, or thereaction can be carried out continuously in a loop reactor or in acontinuous stirred reactor. In one aspect, for example, thepolymerization reaction of this invention is carried out in a loopreactor.

After catalyst activation, a catalyst composition is used tohomopolymerize ethylene, or copolymerize ethylene with a comonomer. Inone aspect, a typical polymerization method is a slurry polymerizationprocess (also known as the particle form process), which is well knownin the art and is disclosed, for example in U.S. Pat. No. 3,248,179,which is incorporated by reference herein, in its entirety. Otherpolymerization methods of the present invention for slurry processes arethose employing a loop reactor of the type disclosed in U.S. Pat. No.3,248,179, and those utilized in a plurality of stirred reactors eitherin series, parallel, or combinations thereof, wherein the reactionconditions are different in the different reactors, which is alsoincorporated by reference herein, in its entirety.

In one aspect, polymerization temperature for this invention may rangefrom about 60° C. to about 280° C., and in another aspect,polymerization reaction temperature may range from about 70° C. to about110° C.

The polymerization reaction typically occurs in an inert atmosphere,that is, in an atmosphere substantial free of oxygen and undersubstantially anhydrous conditions, thus, in the absence of water as thereaction begins. Therefore a dry, inert atmosphere, for example, drynitrogen or dry argon, is typically employed in the polymerizationreactor.

The polymerization reaction pressure can be any pressure that does notterminate the polymerization reaction, and is typically conducted at apressure higher than the pretreatment pressures. In one aspect,polymerization pressures may be from about atmospheric pressure to about1000 psig. In another aspect, polymerization pressures may be from about50 psig to about 800 psig. Further, hydrogen can be used in thepolymerization process of this invention to control polymer molecularweight.

Polymerizations using the catalysts of this invention can be carried outin any manner known in the art. Such processes that can polymerizemonomers into polymers include, but are not limited to slurrypolymerizations, gas phase polymerizations, solution polymerizations,and multi-reactor combinations thereof. Thus, any polymerization zoneknown in the art to produce olefin-containing polymers can be utilized.For example, a stirred reactor can be utilized for a batch process, orthe reaction can be carried out continuously in a loop reactor or in acontinuous stirred reactor. Typically, the polymerizations disclosedherein are carried out using a slurry polymerization process in a loopreaction zone. Suitable diluents used in slurry polymerization are wellknown in the art and include hydrocarbons which are liquid underreaction conditions. The term “diluent” as used in this disclosure doesnot necessarily mean an inert material, as this term is meant to includecompounds and compositions that may contribute to polymerizationprocess. Examples of hydrocarbons that can be used as diluents include,but are not limited to, cyclohexane, isobutane, n-butane, propane,n-pentane, isopentane, neopentane, and n-hexane. Typically, isobutane isused as the diluent in a slurry polymerization. Examples of thistechnology are found in U.S. Pat. Nos. 4,424,341; 4,501,885; 4,613,484;4,737,280; and 5,597,892; each of which is incorporated by referenceherein, in its entirety.

For purposes of the invention, the term polymerization reactor includesany polymerization reactor or polymerization reactor system known in theart that is capable of polymerizing olefin monomers to producehomopolymers or copolymers of the present invention. Such reactors cancomprise slurry reactors, gas-phase reactors, solution reactors, or anycombination thereof. Gas phase reactors can comprise fluidized bedreactors or tubular reactors. Slurry reactors can comprise verticalloops or horizontal loops. Solution reactors can comprise stirred tankor autoclave reactors.

Polymerization reactors suitable for the present invention can compriseat least one raw material feed system, at least one feed system forcatalyst or catalyst components, at least one reactor system, at leastone polymer recovery system or any suitable combination thereof.Suitable reactors for the present invention can further comprise anyone, or combination of, a catalyst storage system, an extrusion system,a cooling system, a diluent recycling system, or a control system. Suchreactors can comprise continuous take-off and direct recycling ofcatalyst, diluent, and polymer. Generally, continuous processes cancomprise the continuous introduction of a monomer, a catalyst, and adiluent into a polymerization reactor and the continuous removal fromthis reactor of a suspension comprising polymer particles and thediluent.

Polymerization reactor systems of the present invention can comprise onetype of reactor per system or multiple reactor systems comprising two ormore types of reactors operated in parallel or in series. Multiplereactor systems can comprise reactors connected together to performpolymerization, or reactors that are not connected. The polymer can bepolymerized in one reactor under one set of conditions, and then thepolymer can be transferred to a second reactor for polymerization undera different set of conditions.

In one aspect of the invention, the polymerization reactor system cancomprise at least one loop slurry reactor. Such reactors are known inthe art and can comprise vertical or horizontal loops. Such loops cancomprise a single loop or a series of loops. Multiple loop reactors cancomprise both vertical and horizontal loops. The slurry polymerizationcan be performed in an organic solvent that can disperse the catalystand polymer. Examples of suitable solvents include butane, hexane,cyclohexane, octane, and isobutane. Monomer, solvent, catalyst and anycomonomer are continuously fed to a loop reactor where polymerizationoccurs. Polymerization can occur at low temperatures and pressures.Reactor effluent can be flashed to remove the solid resin.

In yet another aspect of this invention, the polymerization reactor cancomprise at least one gas phase reactor. Such systems can employ acontinuous recycle stream containing one or more monomers continuouslycycled through the fluidized bed in the presence of the catalyst underpolymerization conditions. The recycle stream can be withdrawn from thefluidized bed and recycled back into the reactor. Simultaneously,polymer product can be withdrawn from the reactor and new or freshmonomer can be added to replace the polymerized monomer. Such gas phasereactors can comprise a process for multi-step gas-phase polymerizationof olefins, in which olefins are polymerized in the gaseous phase in atleast two independent gas-phase polymerization zones while feeding acatalyst-containing polymer formed in a first polymerization zone to asecond polymerization zone.

In still another aspect of the invention, the polymerization reactor cancomprise a tubular reactor. Tubular reactors can make polymers by freeradical initiation, or by employing the catalysts typically used forcoordination polymerization. Tubular reactors can have several zoneswhere fresh monomer, initiators, or catalysts are added. Monomer can beentrained in an inert gaseous stream and introduced at one zone of thereactor. Initiators, catalysts, and/or catalyst components can beentrained in a gaseous stream and introduced at another zone of thereactor. The gas streams are intermixed for polymerization. Heat andpressure can be employed appropriately to obtain optimal polymerizationreaction conditions.

In another aspect of the invention, the polymerization reactor cancomprise a solution polymerization reactor. During solutionpolymerization, the monomer is contacted with the catalyst compositionby suitable stirring or other means. A carrier comprising an inertorganic diluent or excess monomer can be employed. If desired, themonomer can be brought in the vapor phase into contact with thecatalytic reaction product, in the presence or absence of liquidmaterial. The polymerization zone is maintained at temperatures andpressures that will result in the formation of a solution of the polymerin a reaction medium. Agitation can be employed during polymerization toobtain better temperature control and to maintain uniform polymerizationmixtures throughout the polymerization zone. Adequate means are utilizedfor dissipating the exothermic heat of polymerization. Thepolymerization can be effected in a batch manner, or in a continuousmanner. The reactor can comprise a series of at least one separator thatemploys high pressure and low pressure to separate the desired polymer.

In a further aspect of the invention, the polymerization reactor systemcan comprise the combination of two or more reactors. Production ofpolymers in multiple reactors can include several stages in at least twoseparate polymerization reactors interconnected by a transfer devicemaking it possible to transfer the polymers resulting from the firstpolymerization reactor into the second reactor. The desiredpolymerization conditions in one of the reactors can be different fromthe operating conditions of the other reactors. Alternatively,polymerization in multiple reactors can include the manual transfer ofpolymer from one reactor to subsequent reactors for continuedpolymerization. Such reactors can include any combination including, butnot limited to, multiple loop reactors, multiple gas reactors, acombination of loop and gas reactors, a combination of autoclavereactors or solution reactors with gas or loop reactors, multiplesolution reactors, or multiple autoclave reactors.

After the polymers are produced, they can be formed into variousarticles, including but not limited to, household containers, utensils,film products, drums, fuel tanks, pipes, geomembranes, and liners.Various processes can form these articles. Usually, additives andmodifiers are added to the polymer in order to provide desired effects.By using the invention described herein, articles can likely be producedat a lower cost, while maintaining most or all of the unique propertiesof polymers produced with metallocene catalysts.

Ethylene Polymers Prepared According to this Invention

Tables 1 through 8 and the Examples provide data for the polyethyleneresins produced using the catalyst compositions of this invention, andfor polyethylene resins produced using standard or comparative catalystcompositions. Table 1 provides a summary of catalyst pretreatments,while Table 2 provides a listing of components used for theprecontacting step in the precontactor.

A polymerization run using a first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A) alone was conducted because (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ is used as afirst metallocene in many of the Examples provided herein. These dataappear in Tables 3A and 3B and provide a baseline or control by which tocompare the dual metallocene catalyst compositions.

A polymerization using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ (A)combined with the tightly-bridged second metallocene,methyl-3-butenylmethylidene(η⁵-cyclopentadienyl)(η⁵-9-fluorenyl)zirconiumdichloride (B) was also conducted. Tables 4A and 4B provide the resinand film properties for polyethylene prepared using this dualmetallocene catalyst. Thus, when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ was combinedwith a metallocene that is tightly-bridged by a single carbon atom, theresulting resin was characterized by a lower MI as compared to using(η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ alone, but also substantially decreases MD tear.

A polymerization run using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A) combined with a tightly-bridged second metallocene, either compoundC or D as shown in Tables 5A and 5B, was also conducted. Tables 5A and5B provide the resin and film properties for polyethylene prepared usingthis dual metallocene catalyst. Thus, when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ wascombined with a tightly-bridged metallocene, specifically, a metallocenebridged by a single silicon atom, the resulting resin was characterizedby a lower MI as compared to using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ alone, butalso a substantially decreased MD tear.

A polymerization run using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A) combined with a second, loosely-bridged metallocene, either compoundE, F, or G as shown in Tables 6A and 6B was also conducted. Tables 6Aand 6B provide the resin and film properties for polyethylene preparedusing this dual metallocene catalyst. Thus, when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂was combined with a loosely-bridged metallocene, specifically, a 3- or4-carbon atom bridged metallocene, the resulting resin was characterizedby a lower MI as compared to using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ alone, withoutdecreasing MD tear, and with generally decreasing haze.

A polymerization run using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A) combined with a second, more highly-substituted metallocene,compound (η⁵-C₅H₃ ^(n)BuMe)₂ZrCl₂ (H), as shown in Tables 7A and 7B, wasalso conducted. Tables 7A and 7B provide the resin and film propertiesfor polyethylene prepared using this dual metallocene catalyst. Thus,when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ was combined with a more highly-substitutedmetallocene such as (η⁵-C₅H₃ ^(n)BuMe)₂ZrCl₂, specifically, ametallocene wherein the cyclopentadienyl-type ligand is morehighly-substituted, the resulting resin was characterized by a lower MIas compared to using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ alone, without substantiallydecreasing MD tear.

A polymerization run using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A) combined with the second hafnium metallocene (η⁵-C₅H₄ ^(n)Bu)₂HfCl₂(I) was also conducted. Tables 8A and 8B provides the resin and filmproperties for polyethylene prepared using this dual metallocenecatalyst. Thus, when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ was combined with a hafniummetallocene (η⁵-C₅H₄ ^(n)Bu)₂HfCl₂, the resulting resin wascharacterized by a lower MI as compared to using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂alone, without substantially decreasing MD tear.

In one aspect, for example, the data disclosed herein indicate that,among other things, under the practical conditions of a loop reactor, acatalyst in which (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ (A) is the only metalloceneemployed affords polymer which is generally too high in MI to affordadequate melt strength for blowing film. Additionally, given the high MIand narrow molecular weight distribution of such polymers, (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ (A) provides a polymer with too much haze for many LLDPEfilm applications. However, upon adding the second metallocene whichproduces higher molecular weight polymer to the catalyst compositionprovides a polymer with a lower MI, and hence, increased melt strengthfor blowing film, without sacrificing useful polymer film propertiessuch as MD tear. In this aspect, the second metallocene compounds, whenemployed in the catalyst compositions without a first metallocenecompound, possess sufficient activity, the addition of hydrogen tocontrol MI may not be necessary in the dual metallocene catalystcompositions of this invention.

In one aspect, for example, the resins and films of this invention maybe characterized by polymer properties that can fall in these ranges:melt index from about 0.3 to about 2.0 dg/min; density from about 0.94to about 0.91 g/cm³; CY-a parameter from about 0.45 to about 0.70;polydispersity index (M_(w)/M_(n)) from about 2 to about 6; HLMI/MIratio is from about 16.5 to about 25; Elmendorf MD tear resistancegreater than about 150 g for a 1 mil blown film; Elmendorf TD tearresistance is greater than about 350 g for a 1 mil blown film; film hazeof less than about 25% for a 1 mil blown film; Dart impact strengthgreater than about 600 g for a 1 mil blown film; and Spencer impactstrength greater than about 0.7 J for a 1 mil blown film.

In another aspect, for example, the resins and films of this inventionmay be characterized by polymer properties that can fall in theseranges: melt index from about 0.5 to about 1.5 dg/min; density fromabout 0.935 to about 0.915 g/cm³; CY-a parameter from about 0.50 toabout 0.65; polydispersity index (M_(w)/M_(n)) from about 2.2 to about5.0; HLMI/MI ratio is from about 17 to about 24; Elmendorf MD tearresistance greater than about 200 g for a 1 mil blown film; Elmendorf TDtear resistance greater than about 380 g for a 1 mil blown film; filmhaze of less than about 15% for a 1 mil blown film; Dart impact strengthgreater than about 800 g for a 1 mil blown film; and Spencer impactstrength greater than about 0.9 J for a 1 mil blown film.

In yet another aspect, for example, the resins and films of thisinvention may be characterized by polymer properties that can fall inthese ranges: melt index from about 0.8 to about 1.3 dg/min; densityfrom about 0.925 to about 0.915 g/cm³; CY-a parameter from about 0.53 toabout 0.62; polydispersity index (M_(w)/M_(n)) from about 2.6 to about4.0; HLMI/MI ratio from about 17.5 to about 23; Elmendorf MD tearresistance greater than about 250 g for a 1 mil blown film; Elmendorf TDtear resistance greater than about 450 g for a 1 mil blown film; filmhaze less than about 10% for a 1 mil blown film; Dart impact strengthgreater than about 1200 g for a 1 mil blown film; and Spencer impactstrength greater than about 1.00 J for a 1 mil blown film.

In a further aspect of this invention, the polymer of this invention ischaracterized by a melt index (MI) from about 0.3 to about 2.0 dg/min.In another aspect, the MI is from about 0.5 to about 1.5 dg/min, and instill another aspect, the MI is from about 0.8 to about 1.3 dg/min.

In yet another aspect of this invention, the polymer of this inventionis characterized by a density from about 0.94 to about 0.91 g/cm³. Instill another aspect, the density is from about 0.935 to about 0.915g/cm³, and in another aspect, the density is from about 0.925 to about0.915 g/cm³.

In yet another aspect of this invention, the polymer of this inventionis characterized by a CY-a parameter from about 0.45 to about 0.70. Instill another aspect, the CY-a parameter is from about 0.50 to about0.65, and in another aspect, the CY-a parameter is from about 0.53 toabout 0.62.

In yet another aspect of this invention, the polymer of this inventionis characterized by a polydispersity index (M_(w)/M_(n)) from about 2 toabout 6. In still another aspect, the polydispersity index (M_(w)/M_(n))is from about 2.2 to about 5.0, and in another aspect, thepolydispersity index (M_(w)/M_(n)) is from about 2.6 to about 4.0.

In yet another aspect of this invention, the polymer of this inventionis characterized by a HLMI/MI ratio from about 16.5 to about 25. Instill another aspect, the HLMI/MI ratio is from about 17 to about 24,and in another aspect, the HLMI/MI ratio is from about 17.5 to about 23.

In yet another aspect of this invention, the polymer of this inventionis characterized by an Elmendorf MD tear resistance greater than about150 g for a 1 mil blown film. In still another aspect, the Elmendorf MDtear resistance is greater than about 200 g for a 1 mil blown film, andin another aspect, the Elmendorf MD tear resistance is greater thanabout 250 g for a 1 mil blown film.

In yet another aspect of this invention, the polymer of this inventionis characterized by an Elmendorf TD tear resistance greater than about350 g for a 1 mil blown film. In still another aspect, the Elmendorf TDtear resistance is greater than about 380 g for a 1 mil blown film, andin another aspect, the Elmendorf TD tear resistance is greater thanabout 450 g for a 1 mil blown film.

In yet another aspect of this invention, the polymer of this inventionis characterized by a film haze of less than about 25% for a 1 mil blownfilm. In still another aspect, the film haze) is less than about 15% fora 1 mil blown film, and in another aspect, the film haze is less thanabout 10% for a 1 mil blown film.

In yet another aspect of this invention, the polymer of this inventionis characterized by a Dart impact strength greater than about 600 g fora 1 mil blown film. In still another aspect, the Dart impact strength isgreater than about 800 g for a 1 mil blown film, and in another aspect,the Dart impact strength is greater than about 1200 g for a 1 mil blownfilm.

In yet another aspect of this invention, the polymer of this inventionis characterized by a Spencer impact strength greater than about 0.7 Jfor a 1 mil blown film. In still another aspect, the Spencer impactstrength is greater than about 0.9 J for a 1 mil blown film, and inanother aspect, the Spencer impact strength is greater than about 1.00 Jfor a 1 mil blown film.

Definitions

In order to more clearly define the terms used herein, the followingdefinitions are provided. To the extent that any definition or usageprovided by any document incorporated herein by reference conflicts withthe definition or usage provided herein, the definition or usageprovided herein controls.

The term “polymer” is used herein to mean homopolymers comprisingethylene and copolymers of ethylene and another olefinic comonomer.Polymer is also used herein to mean homopolymers and copolymers of anyother polymerizable monomer disclosed herein.

The term “cocatalyst” is generally used herein to refer to theorganoaluminum compounds that may constitute one component of thecatalyst composition, but also refers to the optional components of thecatalyst composition including, but not limited to, aluminoxanes,organoboron compounds, organozinc compounds, or ionizing ioniccompounds, as disclosed herein. The term cocatalyst may be usedregardless of the actual function of the compound or any chemicalmechanism by which the compound may operate. In one aspect, the termcocatalyst is used to distinguish that component of the catalystcomposition from the first and second metallocene compounds.

The term “precontacted” mixture is used herein to describe a firstmixture of catalyst components that are contacted for a first period oftime prior to the first mixture being used to form a “postcontacted” orsecond mixture of catalyst components that are contacted for a secondperiod of time. Typically, the precontacted mixture describes a mixtureof metallocene compound (first, second, or both), olefin monomer, andorganoaluminum compound, before this mixture is contacted with thechemically treated solid oxide and optionally additional organoaluminumcompound. Thus, “precontacted” describes components that are used tocontact each other, but prior to contacting the components in thesecond, postcontacted mixture. Accordingly, this invention mayoccasionally distinguish between a component used to prepare theprecontacted mixture and that component after the mixture has beenprepared. For example, according to this description, it is possible forthe precontacted organoaluminum compound, once it is contacted with themetallocene and the olefin monomer, to have reacted to form at least onedifferent chemical compound, formulation, or structure from the distinctorganoaluminum compound used to prepare the precontacted mixture. Inthis case, the precontacted organoaluminum compound or component isdescribed as comprising an organoaluminum compound that was used toprepare the precontacted mixture.

Similarly, the term “postcontacted” mixture is used herein to describe asecond mixture of catalyst components that are contacted for a secondperiod of time, and one constituent of which is the “precontacted” orfirst mixture of catalyst components that were contacted for a firstperiod of time. Typically, the term “postcontacted” mixture is usedherein to describe the mixture of first metallocene compound, firstmetallocene compound, olefin monomer, organoaluminum compound, andchemically treated solid oxide, formed from contacting the precontactedmixture of a portion of these components with any additional componentsadded to make up the postcontacted mixture. Generally, the additionalcomponent added to make up the postcontacted mixture is the chemicallytreated solid oxide, and optionally may include an organoaluminumcompound the same or different from the organoaluminum compound used toprepare the precontacted mixture, as described herein. Accordingly, thisinvention may also occasionally distinguish between a component used toprepare the postcontacted mixture and that component after the mixturehas been prepared.

The term metallocene, as used herein, describes a compound comprisingtwo η⁵-cycloalkadienyl-type ligands in the molecule. Thus, themetallocenes of this invention are bis(η⁵-cyclopentadienyl-type ligand)compounds, wherein the η⁵-cycloalkadienyl portions includecyclopentadienyl ligands, indenyl ligands, fluorenyl ligands, and thelike, including partially saturated or substituted derivatives oranalogs of any of these. Possible substituents on these ligands includehydrogen, therefore the description “substituted derivatives thereof” inthis invention comprises partially saturated ligands such astetrahydroindenyl, tetrahydrofluorenyl, octahydrofluorenyl, partiallysaturated indenyl, partially saturated fluorenyl, substituted partiallysaturated indenyl, substituted partially saturated fluorenyl, and thelike. In some contexts, the metallocene is referred to simply as the“catalyst”, in much the same way the term “cocatalyst” is used herein torefer to the organoaluminum compound. Unless otherwise specified, thefollowing abbreviations are used: Cp for cyclopentadienyl; Ind forindenyl; and Flu for fluorenyl.

The terms “catalyst composition,” “catalyst mixture,” and the like donot depend upon the actual product resulting from the contact orreaction of the components of the mixtures, the nature of the activecatalytic site, or the fate of the aluminum cocatalyst, the firstmetallocene compound, the second metallocene compound, any olefinmonomer used to prepare a precontacted mixture, or the chemicallytreated solid oxide after combining these components. Therefore, theterms catalyst composition, catalyst mixture, and the like may includeboth heterogeneous compositions and homogenous compositions.

The term “hydrocarbyl” is used herein to specify a hydrocarbon radicalgroup that includes, but is not limited to aryl, alkyl, cycloalkyl,alkenyl, cycloalkenyl, cycloalkadienyl, alkynyl, aralkyl, aralkenyl,aralkynyl, and the like, and includes all substituted, unsubstituted,branched, linear, heteroatom substituted derivatives thereof.

The terms chemically treated solid oxide, solid oxide activator-support,acidic activator-support, activator-support, treated solid oxidecompound, or simply activator, and the like are used herein to indicatea solid, inorganic oxide of relatively high porosity, which exhibitsLewis acidic or Brønsted acidic behavior, and which has been treatedwith an electron-withdrawing component, typically an anion, and which iscalcined. The electron-withdrawing component is typically anelectron-withdrawing anion source compound. Thus, the chemically treatedsolid oxide compound comprises the calcined contact product of at leastone solid oxide compound with at least one electron-withdrawing anionsource compound. Typically, the chemically treated solid oxide comprisesat least one ionizing, acidic solid oxide compound. The terms support oractivator-support are not used to imply these components are inert, andthis component should not be construed as an inert component of thecatalyst composition.

Although any methods, devices, and materials similar or equivalent tothose described herein can be used in the practice or testing of theinvention, the typical methods, devices and materials are hereindescribed.

All publications and patents mentioned herein are incorporated herein byreference for the purpose of describing and disclosing, for example, theconstructs and methodologies that are described in the publications,which might be used in connection with the presently describedinvention. The publications discussed above and throughout the text areprovided solely for their disclosure prior to the filing date of thepresent application. Nothing herein is to be construed as an admissionthat the inventors are not entitled to antedate such disclosure byvirtue of prior invention.

For any particular compound disclosed herein, any general structurepresented also encompasses all conformational isomers, regioisomers, andstereoisomers that may arise from a particular set of substituents. Thegeneral structure also encompasses all enantiomers, diastereomers, andother optical isomers whether in enantiomeric or racemic forms, as wellas mixtures of stereoisomers, as the context requires.

The present invention is further illustrated by the following examples,which are not to be construed in any way as imposing limitations uponthe scope thereof. On the contrary, it is to be clearly understood thatresort may be had to various other aspects, embodiments, modifications,and equivalents thereof which, after reading the description herein, maysuggest themselves to one of ordinary skill in the art without departingfrom the spirit of the present invention or the scope of the appendedclaims.

EXAMPLE 1 General Testing Procedures

Melt index (MI, g/10 min) was determined in accordance with ASTM D1238condition F at 190° C. with a 2,160 gram weight.

High load melt index (HLMI, g/10 min) was determined in accordance withASTM D1238 condition E at 190° C. with a 21,600 gram weight.

Polymer density was determined in grams per cubic centimeter (g/cc) on acompression molded sample, cooled at about 15° C. per hour, andconditioned for about 40 hours at room temperature in accordance withASTM D1505 and ASTM D1928, procedure C.

Molecular weights and molecular weight distributions were obtained usinga Waters 150 CV gel permeation chromatograph with trichlorobenzene (TCB)as the solvent, with a flow rate of 1 milliliter/minute at a temperatureof 140° C. 2,6-Di-t-butyl-4-methylphenol (BHT) at a concentration of 1.0gram per liter was used as a stabilizer in the TCB. An injection volumeof 220 liters was used with a nominal polymer concentration of 0.3gram/liter at room temperature. Dissolution of the sample in stabilizedTCB was carried out by heating at about 160-170° C. for 20 hours withoccasional, gentle agitation. The column was two Waters HT-6E columns(7.8 mm×300 mm). The columns were calibrated with a broad linearpolyethylene standard (Phillips Marlex.RTM. BHB 5003) for which themolecular weight had been determined.

All the blown film samples were made on a laboratory-scale blown filmline using typical linear low-density (LLDPE) conditions as follows: 100mm (4 inch) die diameter, 1.5 mm (0.060 inch) die gap, 37.5 mm (1.5inch) diameter single-screw extruder fitted with a barrier screw with aMaddock mixing section at the end (L/D=24, 2.2:1 compression ratio), 115RPM screw speed [about 27 kg/h (60 lb/h) output rate], 2.5:1 blow upratio (BUR), “in-pocket” bubble with a “freeze line height” (FLH)between 20-28 cm (8-11 inch), 190° C. (375° F.) barrel and die settemperatures and 1 mil (25 micron) thick film. Cooling was accomplishedwith a Dual Lip air ring using ambient (laboratory) air at about 25° C.(75-80° F.). These particular processing conditions were chosen sincethe film properties so obtained are typically representative of thoseobtained from larger, commercial scale film blowing conditions.

The haze (%) was measured in accordance with the procedures specified inASTM D 1003-97, using a Haze Gard Plus™ instrument (Model 4725) made bythe BYK-Gardner® Company.

Dart impact strength was measured in accordance with ASTM D-1709 (methodA).

Pendulum impact strength (more commonly known as Spencer impact)strength was measured in accordance with ASTM D-3420. However, a special(more severe) pendulum head, which was manufactured in-house, was usedfor these samples since they did not fail with the standard pendulumusing the maximum pendulum weight.

Machine (MD) and transverse (TD) direction Elmendorf tear strengths weremeasured on a Testing Machines Inc. tear tester (Model 83-11-00) inaccordance with ASTM D-1922.

Melt rheological characterizations were performed as follows.Small-strain (10%) oscillatory shear measurements were performed on aRheometrics cientific, Inc. ARES rheometer using parallel-plategeometry. All rheological tests were performed at 190° C. The complexviscosity |η*| versus frequency (ω) data were then curve fitted usingthe modified three parameter Carreau-Yasuda (CY) empirical model toobtain the zero shear viscosity—η₀, characteristic viscous relaxationtime—τ_(η), and the breadth parameter—α. The simplified Carreau-Yasuda(CY) empirical model is as follows.${{{\eta^{*}(\omega)}} = \frac{\eta_{0}}{\left\lbrack {1 + \left( {\tau_{\eta}\omega} \right)^{a}} \right\rbrack^{{({1 - n})}/a}}},$wherein:

-   -   |η*(ω)|=magnitude of complex shear viscosity;    -   η₀=zero shear viscosity    -   τ_(η)=viscous relaxation time    -   α=“breadth” parameter    -   n=fixes the final power law slope, fixed at 2/11; and    -   ω=angular frequency of oscillatory shearing deformation.        Details of the significance and interpretation of the CY model        and derived parameters may be found in: C. A. Hieber and H. H.        Chiang, Rheol. Acta, 28, 321 (1989); C. A. Hieber and H. H.        Chiang, Polym. Eng. Sci., 32, 931 (1992); and R. B. Bird, R. C.        Armstrong and O. Hasseger, Dynamics of Polymeric Liquids, Volume        1, Fluid Mechanics, 2nd Edition, John Wiley & Sons (1987); each        of which is incorporated herein by reference in its entirety.        The CY “a” parameter is reported in the tables for the resins        disclosed herein.

A “Quantachrome Autosorb-6 Nitrogen Pore Size Distribution Instrument”was used to determined specific surface area (“surface area”) andspecific pore volume (“pore volume”). This instrument was acquired fromthe Quantachrome Corporation, Syosset, N.Y.

EXAMPLE 2 Preparation of a Fluorided Silica-Alumina Activator-Support

The silica-alumina used to prepare the fluorided silica-alumina acidicactivator-support in this Example was obtained from W. R. Grace as GradeMS 13-110, containing 13% alumina, having a pore volume of about 1.2cc/g and a surface area of about 400 m²/g. This material was fluoridedby impregnation to incipient wetness with a solution containing ammoniumbifluoride in an amount sufficient to equal 10 wt % of the weight of thesilica-alumina. This impregnated material was then dried in a vacuumoven for 8 hours at 100° C. The fluorided silica-alumina samplesobtained in this manner were then calcined as follows. About 10 grams ofthe alumina were placed in a 1.75-inch quartz tube fitted with asintered quartz disk at the bottom. While the silica was supported onthe disk, dry air was blown up through the disk at the linear rate ofabout 1.6 to 1.8 standard cubic feet per hour. An electric furnacearound the quartz tube was used to increase the temperature of the tubeat the rate of about 400° C. per hour to a final temperature of about450° C. At this temperature, the silica-alumina was allowed to fluidizefor about three hours in the dry air. Afterward, the silica-alumina wascollected and stored under dry nitrogen, and was used without exposureto the atmosphere.

EXAMPLE 3 General and Specific Preparations of the Metallocenes

General Methods

General preparative methods for forming the first metallocene compoundsand the second metallocene compounds can be found in a variousreferences, including: U.S. Pat. Nos. 4,939,217; 5,191,132; 5,210,352;5,347,026; 5,399,636; 5,401,817; 5,420,320; 5,436,305; 5,451,649;5,496,781; 5,498,581; 5,541,272; 5,554,795; 5,563,284; 5,565,592;5,571,880; 5,594,078; 5,631,203; 5,631,335; 5,654,454; 5,668,230;5,705,579; 6,509,427; 5,705,579; and 6,509,427; and in Köppl, A. Alt, H.G. J. Mol. Catal A. 2001, 165, 23-32; Kajigaeshi, S.; Kadowaki, T.;Nishida, A.; Fujisaki, S. The Chemical Society of Japan, 1986, 59, 97;Alt, H. G.; Jung, M.; Kehr, G. J. Organomet. Chem. 1998, 562, 153-181;Alt, H. G.; Jung, M. J. Organomet. Chem. 1998, 568, 87-112; Journal ofOrganometallic Chemistry, 1996, 522, 39-54; and Wailes, P. C.; Coutts,R. S. P.; Weigold, H. in Organometallic Chemistry of Titanium, Zironium,and Hafnium, Academic; New York, 1974; and Cardin, D. J.; Lappert, M.F.; and Raston, C. L.; Chemistry of Organo-Zirconium and -HafniumCompounds; Halstead Press; New York, 1986.

Specific Preparations

All manipulations involving air-sensitive reagents and materials wereperformed under nitrogen by using Schlenk line or dry box techniques.THF was distilled from potassium. Anhydrous diethyl ether, methylenechloride, pentane and toluene were obtained from Fisher ScientificCompany and stored over activated alumina. All solvents were degassedand stored under nitrogen. Zirconium(IV) chloride (99.5%) andn-butyllithium were purchased from Aldrich and used as received.Products were analyzed by ¹H NMR (300 MHz, CDCl₃, referenced against thepeak of residual CHCl₃ at 7.24 ppm) or ¹³C NMR (75 MHz, CDCl₃,referenced against central line of CDCl₃ at 77.00 ppm).

Preparation of rac-C₃H₆(Ind)₂ZrCl₂ (E)

a. Synthesis of 1,3-bis(3-indenyl)propane. Technical grade indene (92%GC purity) (200 mL) was mixed with 1 liter of dry THF under nitrogen.The solution was cooled with dry ice and n-BuLi (640 mL, 2.5 M inhexanes, 1.6 mols) was added over a period of 45 minutes. The dry icebath was removed allowing the mixture to warm while stirring for 2 hoursat room temperature. The resulting red solution was gradually added to1,3-dibromopropane (75 mL, 0.74 moles) in 100 mL of dry THF at 0° C.over a period of 45 minutes, and the resulting mixture was stirred for14 hours at room temperature. The final resulting solution was cooled tobelow 5° C. and held below 6° C. while adding 600 mL of 3 M HCl aqueoussolution. After the ice bath was removed, the yellow mixture was stirredfor 1 hour. This mixture was extracted with 200 mL of diethyl ether, andthe resulting organic layer was washed with 3×300 mL of water and 100 mLof brine and then dried over anhydrous sodium sulfate and filtered. Asthe solvent was removed under vacuum a white solid began to form. Themixture was cooled to −15° C. in a freezer overnight. The solid wasbroken up, filtered off, and washed with cold methanol. After air dryingand breaking up further and drying further, a slightly yellow solid(167.3 g, 83% yield) was obtained. ¹H NMR (300 MHz, CDCl₃) δ 7.53 (d,J=7.2 Hz, 2H), 7.43 (d, J=7.2 Hz, 2H), 7.36 (t, J=7.2 Hz, 2H), 7.26 (t,J=7.2 Hz, 2H), 6.31 (broad s, 2H), 3.39 (d, J=1.8 Hz, 4H), 2.65-2.80(dt, J=7.2 Hz, 1.2 Hz, 4H), 2.17 (quin, J=7.2 Hz, 2H); ¹³C NMR (75 MHz,CDCl₃) δ 145.5, 144.5, 144.2, 127.9, 126.0, 124.5, 123.7, 118.9, 37.7,27.6, 26.2.

b. Synthesis of rac-C₃H₆(Ind)₂ZrCl₂. The ligand 1,3-bis(indenyl)propane(10.88 g, 40 mmol) was dissolved in 400 mL of dry THF and cooled to −78°C. under nitrogen. A portion of n-BuLi (33.6 mL, 2.5 M in hexanes, 84mmol) was added dropwise over 30 minutes to the solution. The resultingmixture was warmed to room temperature and stirred for an additional 3hours, giving rise to a red brown solution. Into a separate flask cooledto −78° C. and containing ZrCl₄ (9.8 g, 42 mmol) was added 20 mL ofpentane followed by a slow addition of 410 mL of THF, giving rise to awhite suspension. After warming to room temperature and stirring for anadditional 2 hours, the suspension fully dissolved to yield a clear,colorless solution. Both solutions were simultaneously added, viacannula, over 4 hours to a third flask containing 50 mL of rapidlystirred THF at room temperature. After the addition was completed, thesolution was stirred overnight at room temperature, giving rise to anorange solution. Removal of the solvent gave an orange solid (a crudeproduct). According to the ¹H NMR spectrum of the crude product, theratio of racemic isomer to meso isomer is about 10 to 1. Toluene (800mL) was added to the crude product to give an off yellow solid and anorange yellow solution. The solid was removed by centrifuge. Afterreducing the volume of the filtrate to about 250 mL, pentane was addedslowly until the solution just started to turn cloudy. The mixture wasstored at −15° C. The yellow racemic isomer was crystallized out fromthe mixture at −15° C. The combined first two crops gave 5.8 g (33.5%yield) of the titled product. ¹H NMR (300 MHz, CDCl₃) δ 7.64 (d, J=8.4Hz, 2H), 7.58 (d, J=8.4 Hz, 2H), 7.29-7.34 (m, 2H), 7.14-7.20 (m, 2H),6.20 (d, J=4.2 Hz, 2H), 6.08 (d, J=4.2 Hz, 2H), 3.06-3.16 (m, 2H),2.86-2.97 (m, 2H), 2.36-2.45 (m, 2H); ¹³C NMR (75 MHz, CDCl₃) δ 127.6,126.8, 126.5, 126.2, 125.4, 122.9, 122.4, 114.8, 105.8, 30.3, 25.4.

Preparation of rac-C₄H₈(Ind)₂ZrCl₂ (G)

a. Synthesis of 1,4-bis(3-indenyl)butane. Technical grade indene (92% GCpurity) (54.4 mL) was mixed with 720 mL of dry THF under nitrogen. Thesolution was cooled with dry ice and n-BuLi (184 mL, 2.5 M in hexanes,0.46 moles) was added dropwise. The dry ice bath was removed allowingthe mixture to warm while stirring for 4 hours at room temperature. Theresulting red solution was added dropwise to 1,4-dibromobutane (43.2 g,0.2 moles) in 80 mL of dry THF at 0° C. The resulting mixture wasstirred overnight at room temperature. The final resulting solution wasquenched with 5 wt % HCl in ice bath. The mixture from above wasextracted with diethyl ether. The resulting organic layer was washedwith water and then dried over anhydrous sodium sulfate and filtered.Removal of the solvent gave a pale yellow solid. The solid was washedwith hot pentane to afford the product as a pale yellow solid (45 g,78.7% yield). ¹H NMR (300 MHz, CDCl₃) δ 7.49 (d, J=7.4 Hz, 2H), 7.36 (d,J=7.4 Hz, 2H), 7.29 (t, J=7.3 Hz, 2H), 7.19 (dt, J=7.3 Hz, 1.4 Hz, 2H),6.20 (quin, J=1.9 Hz, 2H), 3.31 (q, J=1.9 Hz, 4H), 2.66-2.56 (m, 4H),1.85-1.78 (m, 4H); ¹³C NMR (75 MHz, CDCl₃) δ 145.5, 144.5, 144.4, 127.7,125.9, 124.4, 123.7, 118.9, 37.6, 27.9, 27.6 (Interpolated PeakListing).

b. Synthesis of rac-C₄H₈(Ind)₂ZrCl₂. The ligand 1,4-bis(3-indenyl)butane(6.66 g, 23.2 mmol) was dissolved in 250 mL of dry THF and cooled to−78° C. under nitrogen. A portion of n-BuLi (19.5 mL, 2.5 M in hexanes,48.7 mmol) was added dropwise to the ligand solution. The resultingmixture was warmed to room temperature and stirred for an additional 3.5hours. Into a separate flask cooled to −78° C. and containing ZrCl₄ (5.7g, 24.5 mmol) was added 15 mL of pentane followed by a slow addition of255 mL of THF, giving rise to a white suspension. After warming to roomtemperature and stirring for an additional 3 hours, the suspension fullydissolved to yield a clear, colorless solution. Both solutions weresimultaneously added, via cannula, over 4 hours to a third flaskcontaining 40 mL of rapidly stirred THF at room temperature. After theaddition was completed, the solution was stirred overnight at roomtemperature. Removal of the solvent gave an orange-yellow solid (crudeproduct). Toluene (700 mL) was added to the crude product to give an offyellow solid and a yellow solution. The solid was removed by centrifuge.After reducing the volume of the filtrate to about 250 mL, pentane wasadded slowly until the solution just started to turn cloudy. The mixturewas stored at −10 to −15° C. The yellow racemic isomer was crystallizedout from the mixture. The combined first two crops gave 2.18 g (21%yield) of the titled product. ¹H NMR (300 MHz, CDCl₃) δ 7.69 (d, J=8.6Hz, 2H), 7.52 (d, J=8.6 Hz, 2H), 7.31 (t, J=7.3 Hz, 2H), 7.21 (t, J=7.3Hz, 2H), 6.59 (d, J=3.3 Hz, 2H), 5.55 (d, J=3.3 Hz, 2H), 3.35-3.20 (dd,J=16.1 Hz, 10.5 Hz, 2H), 3.17-3.05 (dd, J=16.4 Hz, 5.6 Hz, 2H),2.33-2.18 (m, 2H), 2.13-1.97 (m, 2H); ¹³C NMR (75 MHz, CDCl₃) δ 128.4,126.7, 125.8, 125.3, 122.7, 121.3, 118.0, 103.3, 27.6, 26.7.

Rac-Me₂Si(2-Me-4-PhInd)₂ZrCl₂ (D), rac-Me₂Si(2-MeInd)₂ZrCl₂ (C),meso-C₃H₆(Ind)₂ZrCl₂ (F), (η⁵-3-Me,1-n-BuC₅H₃)₂ZrCl₂ (H), (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ (A) and (η⁵-C₅H₄ ^(n)Bu)₂HfCl₂ (I) were purchased fromBoulder Scientific and used as received.

Methyl-3-butenylmethylidene(η⁵-cyclopentadienyl)(η⁵-9-fluorenyl)zirconiumdichloride (B) was prepared as described in U.S. Pat. No. 5,498,581.

EXAMPLE 4 Preparation of Metallocene Solutions and Precontactor Feeds

Metallocene solutions and precontactor feeds were prepared as describedbelow using one of Methods A, B, C, D or E as detailed herein. Theamounts of metallocenes, solvents, organoaluminum compounds, and1-hexene (when appropriate) are indicated in Table 1, along with theExample number associated with each of the runs shown.

Method A. The appropriate amount of metallocene was dissolved in dry,degassed solvent under nitrogen at room temperature. The solution wastransferred to a steel vessel and diluted with isobutane to give a totalof 40 pounds. This solution was fed to the precontactor.

Method B. The appropriate amount of metallocene was dissolved in dry,degassed solvent under nitrogen at room temperature. In some cases1-hexene was also added as indicated in Table 1. While stirring at roomtemperature, 93 wt % (neat) triethylaluminum (amount as indicated inTable 1) was added. The solution was stirred for 30 to 60 minutes andthen diluted with additional solvent. The solution was transferred to asteel vessel and diluted with isobutane to give a total of 40 pounds.This solution was fed to the precontactor.

Method C. The appropriate amounts of metallocenes were dissolved in dry,degassed solvent under nitrogen. This solution was transferred to asteel vessel and diluted with isobutane to give a total of 40 pounds.This solution was fed to the precontactor.

Method D. About 150 mL of toluene was added to the flask containing theappropriate amounts of metallocenes followed by addition of TEA(triethylaluminum) and 1-hexene at room temperature. The mixture wasstirred for 2 hr at room temperature, then charged into a steel vessel.The rest of toluene was then added and the contents were diluted withisobutane to a total of 40 pounds. This solution was fed to theprecontactor.

Method E. Solution A: rac-C₃H₆(Ind)₂ZrCl₂ (E) was suspended in 1-hexene,TEA was added to the suspension followed by addition of some heptane(250-500 g) at room temperature. The mixture was heated at 50-55° C.overnight, then cooled to room temperature. Solution B: (n-BuCp)₂ZrCl₂(A) was dissolved in heptane (ca. 500 g) followed by addition of TEA,the mixture was stirred for several hours. Solutions A and B werepremixed, then charged into a steel vessel followed by adding the restof heptane. Finally, the contents were diluted to a total of 40 poundswith isobutane.

Precontactor Feeds. The catalyst and co-catalyst feed ratios to theprecontactor are shown in Table 2. TABLE 1 Summary of CatalystPretreatments Table Example Solution Metallocene Metallocene TEA (93%)1-Hexene Solvent Solvent No No. Method Type Amount (g) Amount (g) Amount(g) Type (g) 3 6.1 A A 1.1 0 0 Toluene 584.2 3 6.2 B A 1.009 25.0 0Heptane 1196.4 3 6.3^(a) A A 0.256 0 Toluene 384.0 4 7.1 A A 0.516 0 0Heptane 561 B B 4.0 34.0 92.0 Heptane 2195 4 7.2 A A 0.516 0 0 Heptane561 B B 4 34.0 92.0 Heptane 2195 5 8.1 B C 1.0 28.4 0 Toluene 2790 A A1.026 0 0 Toluene 833.9 5 8.2 B C 1.0 28.4 0 Toluene 2790 A A 1.07 0 0Toluene 697.6 5 8.3 B D 1.00 29.0 0 Toluene 2792 A A 1.07 0 Toluene697.6 6 9.1 D G 0.497 12.5 137 Toluene 3049.6 A A 1.14 0 0 Toluene 544.76 9.2 D G 0.497 12.5 137 Toluene 3049.6 A A 1.14 0 0 Toluene 544.7 6 9.3D E 0.25 12.5 113 Toluene 2999.2 A A 1.1 0 0 Toluene 584.2 6 9.4 D E0.57 12.5 123 Toluene 3092 A A 1.1 0 0 Toluene 584.2 6 9.5 D E 0.57 12.5123 Toluene 3092 A A 1.1 0 0 Toluene 561.0 6 9.6 D E 0.57 12.5 123Toluene 3092 A A 1.1 0 0 Toluene 561.0 6 9.7 E E/A 1.0/0.937 21.3 112heptane 2222 6 9.8 E E/A 1.0/0.936 21.3 193.5 heptane 2883.6 6 9.9 E E/A2.0/0.93  38.1 366 heptane 3001.9 6 9.10 A A 1.00 0 Heptane 2278 B F1.017 26.3 40.3 Heptane 2137 6 9.11 A A 1.0 0 0 Heptane 635 B F 1.01726.3 40.3 Heptane 2137 6 9.12 A A 1.0 0 0 Heptane 635 B F 1.017 26.340.3 Heptane 2137 6 9.13 A A 1.0 0 0 Heptane 635 B F 1.017 26.3 40.3Heptane 2137 6 9.14 A A 1.0 0 0 Heptane 635 B F 1.017 26.3 40.3 Heptane2137 7 10.1 C A/H 0.40, 1.20 0 0 Heptane 262 7 10.2 C A/H 0.25, 0.50 0 0Hexene 1419 7 10.3 C A/H 0.25, 0.50 0 0 Hexene 1009 7 10.4 C A/H 0.50,1.0  0 0 Hexene 1163 7 10.5 C A/H 0.40, 1.20 0 0 Heptane 262 8 11.1 A A0.50 0 0 Heptane 320 A I 0.505 0 0 Heptane 929 8 11.2 A A 0.50 0 0Heptane 320 A I 0.505 0 0 Heptane 929^(a)This vessel was dilutedto 40 pounds using hexene-1 rather thanisobutane.

TABLE 2 Precontactor Feeds Precontactor Precontactor PrecontactorPrecontactor Precontactor Metallocene Metallocene Hexen 0.1% TEAIsobutane Precontactor Resin Solution 1 Solution 2^(a) Feed Feed FeedVolume Number (lbs/hr) (lbs/hr) (lbs/hr) (lbs/hr) (lbs/hr) (Liters)Table 3 6.1 0.21 None 0 0.71 2.58 0.5 6.2 0.26 None 0 0.71 2.32 0.5 6.30.55 None 0 0.61 2.73 0.5 Table 4 7.1 0.32 0.24 0 0.75 1.86 0.5 7.2 0.310.43 0 0.85 1.73 0.5 Table 5 8.1 0.2 0.53 0 0.79 3.72 0.5 8.2 0.21 0.410 0.59 3.79 0.5 8.3 0.33 0.41 0 0.61 2.61 0.5 Table 6 9.1 0.22 0.43 00.71 2.59 0.5 9.2 0.22 0.35 0 0.69 2.6 0.5 9.3 0.76 0.18 0 0.63 2.67 0.59.4 0.82 0.16 0 0.62 2.72 0.5 9.5 0.39 0.10 0 0.62 2.68 0.5 9.6 0.390.10 0 0.62 2.68 0.5 9.7 0.41 a 0 0.68 1.94 0.5 9.8 0.32 a 0 0.62 2 0.59.9 0.45 a 0 0.67 1.96 0.5 9.10 0.21 0.19 0 1.01 2 0.5 9.11 0.17 0.39 01 2.02 0.5 9.12 0.33 0.10 0 0.99 1.99 0.5 9.13 0.37 0.11 0 1.01 2 0.59.14 0.29 0.10 0 1 2 0.5 Table 7 10.1 0.48 a 0 0.95 1.59 0.5 10.2 0.48 a0 0.49 4.94 2 10.3 0.86 a 0 0.48 4.63 2 10.4 0.32 a 0 0.51 4.95 2 10.50.27 a 0 0.98 1.59 0.5 Table 8 11.1 0.2 0.48 0 0.69 1.43 0.5 11.2 0.210.68 0 0.75 1.37 0.5^(a) In examples where only one metallocene feed is listed themetallocenes were feed in a premixed solution.

EXAMPLE 5 Description of a Typical Polymerization Run

Ethylene copolymers were prepared in a continuous particle form process(also known as a slurry process) by contacting the catalyst of thepresent invention with ethylene and 1-hexene comonomer. Thepolymerization medium and polymerization temperature are thus selectedsuch that the copolymer is produced in the form of solid particles andis recovered in that form. General polymerization reaction details areas follows.

Ethylene was dried over activated alumina was used as the monomer.Isobutane that had been degassed by fractionation and dried overactivated alumina was used as the diluent.

The polymerization reactor was a liquid-full 15.2 cm diameter pipe loophaving a volume of 23 (87 liters) or 27 gallons (102 liters). Thefluorided silica-alumina, the 0.1 wt % triethylaluminum solution inisobutane, the metallocene solution or solutions prepared as above and aportion of the total isobutane diluent were all fed to the reactorthrough a precontacting vessel (0.5 or 2.0 Liters), where the threeingredients contacted each other at room temperature for about 10 to 30minutes, before entering the reaction zone. The precontactor consistedof a stirred Autoclave Engineers Magnadrive reactor with a volume ofeither 0.5 or 2.0 Liters as indicated in the tables below, which feddirectly into the loop reactor. The chemically treated solid oxide(CTSO) was added to the precontactor through a 0.35 cc circulatingball-check feeder using a small isobutane flow, as indicated above.Occasionally some hydrogen was added to the reactor to regulate themolecular weight of the polymer product. The reactor pressure was about4 Mpa (about 580 psi). The reactor temperature was varied over a range,from about 65° C. to about 110° C., as indicated. The polymerizationreactor was operated to have a residence time of 1.25 hours. Atsteady-state conditions the total isobutane feed rate was about 46liters per hour, the ethylene feed rate was about 30 lbs/hr, and the1-hexene feed rate was varied to control the density of the polymerproduct. Ethylene concentration in the diluent was from about 14 toabout 20 mole percent. Catalyst concentrations in the reactor are suchthat the CTSO system content typically ranges from 0.001 to about 1weight percent based on the weight of the reactor contents. Polymer wasremoved from the reactor at the rate of about 25 lbs per hour andrecovered in a flash chamber. A Vulcan dryer was used to dry the polymerunder nitrogen from about 60° C. to about 80° C.

To prevent static buildup in the reactor, a small amount (<5 ppmrelative to diluent) of a commercial antistatic agent sold as Stadis 450was typically added.

EXAMPLE 6 Ethylene Polymerization Using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂

Polymerization runs using the single metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A), fluorided silica-alumina, and triethylaluminum were conducted usingthe methods as described herein and in Tables 3A and 3B. Only fluoridedCTSO and TEA were used in these Examples. See Table 1 for metallocenesolution preparation, Table 2 for catalyst feeds to the precontactor,and Table 3A for reactor conditions.

Table 3B provides the resin and film properties for polyethyleneprepared using the single metallocene catalyst comprising (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ (A) as shown. Because the metallocene compound (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ (A) is used as a first metallocene in many of the Examplesprovided herein, these data provide a baseline or control by which tocompare the dual metallocene catalyst compositions.

EXAMPLE 7 Ethylene Polymerization Using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ and aTightly-Bridged Metallocene

Polymerization runs using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A), and the tightly-bridged second metallocene,methyl-3-butenylmethylidene(η⁵-cyclopentadienyl)(η⁵-9-fluorenyl)zirconiumdichloride (B), shown in Tables 4A and 4B, fluorided silica-alumina, andtriethylaluminum were conducted using the methods as described herein.See Table 1 for metallocene solution preparation and Table 2 forcatalyst feeds to the precontactor.

Table 4A illustrates typical polymerization and reactor conditions forpolyethylene prepared using a dual metallocene catalyst comprisingcompounds A+B as shown, while Table 4B provides the resin and filmproperties for polyethylene prepared using the dual metallocene catalystcomprising compounds A+B. Thus, when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ is combinedwith a metallocene that is tightly-bridged by a single carbon atom, theresulting resin is characterized by a lower MI as compared to using(η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ alone, but also substantially decreases MD tear.

EXAMPLE 8 Ethylene Polymerization Using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ and aMetallocene Tightly-Bridged with a SiMe₂ Group

Polymerization runs using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A), the second metallocene, either compound C or D as shown in Tables5A and 5B, fluorided silica-alumina, and triethylaluminum were conductedusing the methods as described herein. See Table 1 for metallocenesolution preparation and Table 2 for catalyst feeds to the precontactor.

Table 5A illustrates the polymerization and reactor conditions forpolyethylene prepared using a dual metallocene catalyst comprisingcompounds A+C or A+D, as shown, while Table 5B provides the resin andfilm properties for polyethylene prepared using the dual metallocenecatalyst comprising compounds A+C or A+D. Thus, when (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ (A) is combined with a tightly-bridged metallocene,specifically, a metallocene bridged by a single silicon atom, theresulting resin is characterized by a lower MI as compared to using(η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ alone, but also a substantially decreased MDtear.

EXAMPLE 9 Ethylene Polymerization Using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ and aLoosely-Bridged Metallocene

Polymerization runs using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A), the second, loosely-bridged metallocene, either compound E, F, or Gas shown in Tables 6A and 6B, fluorided silica-alumina, andtriethylaluminum were conducted using the methods as described herein.See Table 1 for metallocene solution preparation and Table 2 forcatalyst feeds to the precontactor.

Table 6A illustrates the polymerization and reactor conditions forpolyethylene prepared using a dual metallocene catalyst comprisingcompounds A+E, A+F, or A+G, as shown, while Table 6B provides the resinand film properties for polyethylene prepared using the dual metallocenecatalyst comprising compounds A+E, A+F, or A+G. Thus, when (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ (A) is combined with a loosely-bridged metallocene,specifically, a 3- or 4-carbon atom bridged metallocene, the resultingresin is characterized by a lower MI as compared to using (η⁵-C₅H₄^(n)Bu)₂ZrCl₂ alone, without decreasing MD tear, and with generallydecreasing haze.

This Example helps demonstrate, among other things, that under thepractical conditions of a loop reactor, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ (A) byitself affords polymer which is too high in MI to give adequate meltstrength for blowing film. Additionally, given its high MI and narrowmolecular weight distribution, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ (A) provides apolymer with too much haze for many LLDPE film applications. Adding thesecond metallocene which produces higher molecular weight polymerprovides a polymer with lower MI, and hence, increased melt strength forblowing film, without sacrificing useful polymer film properties such asMD tear.

EXAMPLE 10 Ethylene Polymerization Using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ and aMore Highly-Substituted Zirconium Metallocene (η⁵-C₅H₃ ^(n)BuMe)₂ZrCl₂(H)

Polymerization runs using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A), the second, more highly-substituted metallocene, compound (η⁵-C₅H₃^(n)BuMe)₂ZrCl₂ (H), as shown in Tables 7A and 7B, fluoridedsilica-alumina, and triethylaluminum were conducted using the methods asdescribed herein. See Table 1 for metallocene solution preparation andTable 2 for catalyst feeds to the precontactor.

Table 7A illustrates the polymerization and reactor conditions forpolyethylene prepared using a dual metallocene catalyst comprisingcompounds A+H, while Table 7B provides the resin and film properties forpolyethylene prepared using the dual metallocene catalyst comprisingcompounds A+H. Thus, when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ (A) is combined with amore highly substituted metallocene, compound (η⁵-C₅H₃ ^(n)BuMe)₂ZrCl₂(H), specifically, a metallocene wherein the cyclopentadienyl-typeligand is more highly substituted, the resulting resin is characterizedby a lower MI as compared to using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ alone, withoutsubstantially decreasing MD tear.

EXAMPLE 11 Ethylene Polymerization Using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ and itsHafnium Analog (η⁵-C₅H₄ ^(n)BU)₂HfCl₂ (I)

Polymerization runs using the first metallocene, (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂(A), the second hafnium metallocene (η⁵-C₅H₄ ^(n)Bu)₂HfCl₂ (I)comprising substituted cyclopentadienyl ligands as shown in Table 8A and8B, fluorided silica-alumina, and triethylaluminum were conducted usingthe methods as described herein. See Table 1 for metallocene solutionpreparation and Table 2 for catalyst feeds to the precontactor.

Table 8A illustrates the polymerization and reactor conditions forpolyethylene prepared using a dual metallocene catalyst comprisingcompounds A+I, while Table 8B provides the resin and film properties forpolyethylene prepared using the dual metallocene catalyst comprisingcompounds A+I. Thus, when (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ (A) is combined with ahafnium metallocene (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂ (I), the resulting resin ischaracterized by a lower MI as compared to using (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂alone, without substantially decreasing MD tear. TABLE 3A Polymerizationand Reactor Conditions for Polyethylene Prepared Using a SingleMetallocene Catalyst Comprising Compound A as Shown.

Example No. 6.1 6.2 6.3 Chemically-Treated F—Si/AL F—Si/AL F—Si/AL SolidOxide Metallocene A A A in 1-hexene Metallocene to Reactor 0.23 0.260.13 (ppm) Autoclave Residence 10.19 10.89 9.17 Time (Mm) CocatalystType TEA TEA TEA Cocatalyst (ppm) 13.5 13.2 10 Rx Temp (° F.) 181.7178.1 172.8 Ethylene (C2) (mol %) 14.38 14.02 14.05 1-hexene (C6) (mol%)5.04 9.80 8.36 C6═/C2═ (Mole Ratio) 0.35 0.70 0.6 H₂ 0 0 0 C2═ Feed Rate(lb/hr) 28.61 19.07 24.5 1-Hexene (C6) Feed Rate 8.89 12.62 11.44(lb/hr) Total iC4 Flow Rate (lb/hr) 51.05 53.84 60.6 Solids Conc. wt. %28.80 28.4 26.69 Polymer Production (lb/hr) 26.00 24.75 20.8 Density(pellets) (g/cc) 0.9196 0.9166 0.9173 CTSO (RPH) 10 16 22 Mass BalanceProductivity 2774 2286 2240 (lb/lb) Ash Productivity (lb/lb) 2381 27251538 Ash (wt %) 0.042 0.0367 0.065 Mw 78,910 87,630 86,180 Mn 35,90038,100 34,400 Mw/Mn 2.2 2.3 2.51 Precontactor Feed 0.0055 0.0056 0.0014Metallocene Conc (Wt %)

TABLE 3B Resin and Film Properties for Polyethylene Prepared Using aSingle Metallocene Catalyst Comprising Compound A as Shown.

Ex. HLMI/ Dart Spencer MD TD No. Metallocene MI HLMI MI Density ImpactImpact tear tear Haze CY-a 6.1 A 2.48 37.1 14.9 0.918 762 0.63 252 39617.2 0.763 6.2 A 1.93 30.8 16.0 0.916 1316 0.87 317 412 27.3 0.776 6.3 A1.45 26.4 18.2 0.9173 >1400 1.29 269 353 19.3 0.727

TABLE 4A Polymerization and Reactor Conditions for Polyethylene PreparedUsing a Dual Metallocene Catalyst Comprising Compounds A + B as Shown.

Example No. 7.1 7.2 Chemically-Treated Solid Oxide F—Si/AL F—Si/ALMetallocene A + B A + B Metallocene B/A to Reactor 1.24 + 0.11  1.2 +0.21 (ppm) Autoclave Residence Time 11.5 10.96 (Mm) Cocatalyst Type TEATEA Cocatalyst (ppm) 13.16 14.73 Rx Temp (° F.) 175.1 175.4 Ethylene(mol %) 14.61 15.34 1-hexene (mol %) 2.27 2.92 C6═/C2═ (Mole Ratio) 0.160.19 H₂ C2═ Feed Rate (lb/hr) 28.57 29.22 1-Hexene Feed Rate (lb/hr)4.16 4.62 Total iC4 Flow Rate (lb/hr) 57.1 57.2 Solids Conc. wt. % 27.227.3 Polymer Production (lb/hr) 24.92 25.33 Density (pellets) (g/cc) 0.9193 0.9240 CTSO (RPH) 34 24 Mass Balance Productivity 2373. 2373 (lb/lb)Ash Productivity (lb/lb) 2381 2703 Ash (wt %) 0.042 0.037 Mw Mn Mw/MnPrecontactor Feed Metallocene  0.022/0.0028  0.022/0.0028 B/A Conc (Wt%)

TABLE 4B Resin and Film Properties for Polyethylene Prepared Using aDual Metallocene Catalyst Comprising Compounds A + B as Shown.

Ex. HLMI/ Dart Spencer MD TD No. Metallocene MI HLMI MI Density ImpactImpact tear tear Haze CY-a 7.1 A + B 0.46 11.5 25.1 0.919 754 0.56 78419 10.3 0.189 7.2 A + B 0.96 29.4 30.6 0.924 278 0.34 112 540 8.0 0.312

TABLE 5A Polymerization and Reactor Conditions for Polyethylene PreparedUsing a Dual Metallocene Catalyst Comprising Compounds A + C or A + D,as Shown.

Example No. 8.1 8.2 8.3 Chemically-Treated Solid Oxide F—Si/AL F—Si/ALF—Si/AL Metallocene A + C A + C A + D Metallocene to Reactor A + C or0.21 + 0.55 0.22 + 0.43 0.39 + 0.48 A + D (ppm) Autoclave Residence Time(Min) 7.57 7.77 10.05 Cocatalyst Type TEA TEA TEA Cocatalyst (ppm) 15.2111.02 12.95 Rx Temp (° F.) 180.1 180 180.2 Ethylene (mol %) 13.2 13.6214.61 1-hexene (mol %) 5.71 7.48 7.03 C6═ /C2═ (Mole Ratio) 0.43 0.550.48 H₂ C2═ Feed Rate (lb/hr) 25 25 25 1-Hexene Feed Rate (lb/hr) 7.5210.17 9.56 Total iC4 Flow Rate (lb/hr) 52.07 53.11 47.14 Solids Conc.wt. % 25.32 26.15 26.20 Polymer Production (lb/hr) 21.8 23.4 21.8Density (pellets) (g/cc) 0.9238 0.9167 0.9185 CTSO (RPH) 14 13 20 MassBalance Productivity (lb/lb) 3827 3827 2422 Ash Productivity (lb/lb)2174 1515 2128 Ash (wt%) 0.046 0.066 0.047 Mw 112,900 138,380 Mn 37,20037,200 Mw/Mn 3.03 3.72 Precontactor Feed Metallocene 0.005510.00550.0055/0.0055 0.0055/0.0055 A/C or A/D Conc (Wt %)

TABLE 5B Resin and Film Properties for Polyethylene Prepared Using aDual Metallocene Catalyst Comprising Compounds A + C or A + D, as Shown.

Ex. HLMI/ Dart Spencer MD TD No. Example MI HLMI MI Density ImpactImpact tear tear Haze CY-a 8.1 A + C 1.04 24.3 23.4 0.923 154 0.36 68347 21.1 0.079 8.2 A + C 1.10 25.3 23.0 0.916 456 0.44 104 372 9.4 0.0988.3 A + D 1.10 22.6 20.5 0.918 168 0.36 80 409 25.1 0.06

TABLE 6A Polymerization and Reactor Conditions for Polyethylene PreparedUsing a Dual Metallocene Catalyst Comprising Compounds A + E, A + F, orA + G, as Shown.

Example No. 9.1 9.2 9.3 9.4 9.5 9.6 9.7 Chemically-Treated Solid OxideF—Si/Al F—Si/AL F—Si/AL F—Si/AL F—Si/AL F—Si/AL F—Si/AL Metallocene G +A G + A E + A E + A E + A E + A E + A Metallocene G + A, E + A, 0.18 +0.23  0.2 + 0.24 0.45 + 0.16  0.2 + 0.18 0.38 + 0.11 0.38 + 0.11 0.86 orA + F to Reactor (ppm) Autoclave Residence Time (Min) 9.24 9.03 8.268.41 9.41 9.41 11.32 Cocatalyst Type TEA TEA TEA TEA TEA TEA TEACocatalyst (ppm) 13.08 13.25 11.17 11.88 11.42 11.42 13.58 Rx Temp (°F.) 181.6 181.6 182.8 180 182.8 182.8 180 Ethylene (mol %) 13.31 14.3512.79 12.28 13.9 13.9 14.54 1-hexene (mol %) 5.73 5.44 4.82 7.13 7.557.55 7.63 C6═/C2═ (Mole Ratio) 0.43 0.38 0.38 0.58 0.54 0.54 0.52 H₂ C2═Feed Rate (lb/hr) 29 29.01 22.55 24.12 24.31 24.31 26.97 1-Hexene FeedRate (lb/hr) 10.65 10.47 10.92 10.84 11.13 11.13 11.42 Total iC4 FlowRate (lb/hr) 53.03 53.25 55.7 53.09 54.84 54.84 50.87 Solids Conc. wt. %28.3 28.4 28.7 30 30 30 26.5 Polymer Production (lb/br) 26.67 26.83 2626.83 27.5 27.5 24.13 Density (pellets) (g/cc) 0.9182 0.9198 0.9180.9176 0.9183 0.9183 0.9228 CTSO (RPH) 21 22 22 42 23 23 17 Mass BalanceProductivity (lb/lb) 2774 2774 3224 3224 3224 3224 2373 Ash Productivity(lb/lb) 1923 1887 1957 1250 1946 1946 3704 Ash (wt %) 0.052 0.053 0.05110.08 0.0514 0.0514 0.027 Mw 105,230 105,560 108,190 107,120 107,120 Mn47,000 44,000 35,000 42,300 42,300 Mw/Mn 2.4 2.42 3.09 2.53 2.53Precontactor Feed G/A, E/A, or A/F 0.0055/0.0028 0.0055/0.00280.0031/0.0055 0.0014/0.0055 0.0031/0.0055 0.0031/0.0055 0.0107^(a)Metallocene Conc (Wt %) Example No. 9.8 9.9 9.10 9.11 9.12 9.13 9.14Chemically-Treated Solid Oxide F—Si/AL F—Si/AL F—Si/AL F—Si/AL F—Si/ALF—Si/AL F—Si/AL Metallocene E + A E + A E + A A + F A + F A + F A + FMetallocene G + A, E + A, 0.67 1.43 0.24 + 0.24 0.19 + 0.45 0.39 + 0.110.43 + 0.13 0.33 + 0.12 or A + F to Reactor (ppm) Autoclave ResidenceTime (Min) 12.24 11.41 10.86 9.87 10.66 10.39 10.67 Cocatalyst Type TEATEA TEA TEA TEA TEA TEA Cocatalyst (ppm) 13.06 12.84 20.92 20.24 20.3921.26 20.69 Rx Temp (° F.) 179.8 180 177.5 177.6 177.7 177.9 178Ethylene (mol %) 9.95 10.16 12.95 12.86 12.64 13.06 12.11 1-hexene (mol%) 6.17 7.53 20.44 16.82 13.58 14.12 14.24 C6═/C2═ (Mole Ratio) 0.620.74 1.58 1.31 1.07 1.08 1.18 H₂ C2═ Feed Rate (lb/hr) 27.65 29.35 29.7129.79 29.7 29.72 29.69 1-Hexene Feed Rate (lb/hr) 8.29 10.35 13.61 12.7510.48 11.31 11.19 Total iC4 Flow Rate (lb/hr) 52.7 52.14 48.57 48.7148.44 47.63 48.52 Solids Conc. wt. % 30.4 28.7 29.3 29 30.7 30.3 31.1Polymer Production (lb/br) 27.42 26.89 27.5 27 27.83 27.5 28.5 Density(pellets) (g/cc) 0.9197 0.9175 0.9154 0.9215 0.9155 0.9165 0.9166 CTSO(RPH) 35 25 28 30 22 21 22 Mass Balance Productivity (lb/lb) 2373 33073307 3307 3307 3307 Ash Productivity (lb/lb) 3333 3125 3401 2203 23872160 2342 Ash (wt %) 0.03 0.032 0.0294 0.0454 0.0419 0.0463 0.0427 Mw107,040 99,200 106,170 Mn 32,700 30,900 29,700 Mw/Mn 3.27 3.21 3.57Precontactor Feed G/A, E/A, or A/F 0.0107^(a) 0.0162^(a) 0.0055/0.00550.0055/0.0055 0.0055/0.0055 0.0055/0.0055 0.0055/0.0055 Metallocene Conc(Wt %)^(a)For these examples the metallocenes were premixed during thepreparation of the solutions.

TABLE 6B Resin and Film Properties for Polyethylene Prepared Using aDual Metallocene Catalyst Comprising Compounds A + E, A + F, or A + G,as Shown.

Ex. HLMI/ Dart Spencer MD TD No. Example MI HLMl MI Density ImpactImpact tear tear Haze CY-a 9.1 A + G 0.85 14.9 17.5 0.918 >1400 1.34 209398 7.6 0.672 9.2 A + G 0.83 14.5 17.4 0.920 823 1.11 275 470 8.4 0.669.3 A + E 0.81 18.4 22.7 0.918 >1400 1.07 241 451 6.9 0.576 9.4 A + E0.84 16.8 20.0 0.918 >1400 0.91 229 477 7.9 0.509 9.5 A + E 0.77 15.720.4 0.918 >1400 1.00 309 471 6.4 0.566 9.6 A + E 0.77 15.7 20.4 0.9181039 1.21 273 436 7.0 0.566 9.7 A + E 0.76 15 20.1 0.923 191 0.42 264454 6.4 0.549 9.8 A + E 1.01 22 20.3 0.920 391 0.62 274 428 7.4 0.6189.9 A + E 1.00 25 21.3 0.918 1400 1.02 246 383 8.3 9.10 A + F 0.58 13.523.3 0.917 >1400 1.72 194 467 10.1 0.345 9.11 A + F 0.6 15.1 25.2 0.922437 0.36 274 747 7.4 0.569 9.12 A + F 1.03 18.6 18.1 0.916 >1400 1.11215.5 414 17.3 0.646 9.13 A + F 1.11 19.1 17.2 0.916 >1400 1.23 271 4419.7 0.648 9.14 A + F 0.95 16.9 17.8 0.917 >1400 1.68 209 339 14.4 0.652

TABLE 7A Polymerization and Reactor Conditions for Polyethylene PreparedUsing a Dual Metallocene Catalyst Comprising Compounds A + H, as Shown.

Example No. 10.1 10.2 10.3 10.4 10.5 Chemically-Treated Solid OxideF—Si/AL F—Si/AL F—Si/AL F—Si/AL F—Si/AL Metallocene A + H A + H A + HA + H A + H Metallocene to Reactor (ppm) 0.84 0.41 0.6 0.5 0.46Autoclave Residence Time (Min) 12.43 24.96 24.09 24.97 13.3 CacatalystType TEA TEA TEA TEA TEA Cocatalyst (ppm) 19.07 10.03 9.7 9.69 19.68 RxTemp (° F.) 179.3 174.8 174.8 174.8 179.2 Ethylene (mol %) 14.23 13.3512.79 13.41 15.66 1-hexene (mol %) 12.55 2.44 2.55 2.59 15.52 C6═/C2═(Mole Ratio) 0.88 0.18 0.2 0.19 0.99 H2 (mole %) 0.003 C2═ Feed Rate(lb/hr) 19.8 25.87 25.88 25.9 29.8 1-Hexene Feed Rate (lb/hr) 11.2 9.5511.22 12.49 11.84 Total iC4 Flow Rate (lb/hr) 54.2 48.89 48.34 52.38 54Solids Conc. wt. % 28.1 25.3 24.6 21.7 29.5 Polymer Production (lb/hr)26.17 21.67 21.44 20 27.67 Density (pellets) (g/cc) 0.9189 0.9183 0.91790.9177 0.916 CTSO (RPH) 28 60 56 57 22 Mass Balance Productivity (lb/lb)2825 1966 2405 2405 2854 Ash Productivity (lb/lb) 2703 3846 2222 25643030 Ash (wt %) 0.037 0.026 0.045 0.039 0.033 Mw 134,760 124,640 124,060101,110 Mn 55,950 49,760 51.130 35,600 Mw/Mn 2.41 2.5 2.43 2.84Precontactor Feed 0.0088 0.0042 0.0034 0.0083 0.0088 Metallocene Conc(Wt %) Metallocene Mixed Feed A/H 3:1 2:1 2:1 2:1 3:1 Wt. RatioPrecontactor Metallocene 0.48 0.48 0.86 0.32 0.27 Feed (lbs/hr)

TABLE 7B Resin and Film Properties for Polyethylene Prepared Using aDual Metallocene Catalyst Comprising Compounds A + H, as Shown.

Ex. HLMI/ Dart Spencer MD TD No. Metallocene MI HLMI MI Density ImpactImpact tear tear Haze CY-a 10.1 A + H 0.89 15 16.9 0.918 >1400 0.72 216367 1.4 0.585 10.2 A + H 1.03 17.46 17.0 0.9183 1292 1 243 413 16.40.629 10.3 A + H 1.31 23.16 17.7 0.9179 1268 0.99 279 446 22.6 0.61410.4 A + H 1.33 23.39 17.6 0.9177 1007 0.7 297 472 29.9 0.623 10.5 A + H0.98 16.53 16.9 0.9160 1400 1.66 217 402 13.3 0.655

TABLE 8A Polymerization and Reactor Conditions for Polyethylene PreparedUsing a Dual Metallocene Catalyst Comprising Compounds A + I, as Shown.

Example No. 11.1 11.2 Chemically-Treated Solid F—Si/AL F—Si/AL OxideMetallocene A + I A + I Metallocene to Reactor 0.11 + 0.26 0.11 + 0.38(ppm) Autoclave Residence Time 13.57 12.76 (Min) Cocatalyst Type TEA TEACocatalyst (ppm) 13.73 14.11 Rx Temp (° F.) 176.3 176.2 Ethylene (mol %)15.14 14.82 1-hexene (mol %) 11.79 11.3 C6=/C2= (Mole Ratio) 0.78 0.76H₂ C2= Feed Rate (lb/hr) 29.3 29.3 1-Hexene Feed Rate (lb/hr) 9.61 9.75Total iC4 Flow Rate (lb/hr) 50.27 50.52 Solids Conc. wt. % 28.1 27.7Polymer Production (lb/hr) 25.5 25.27 Density (pellets) (g/cc) 0.91850.9181 CTSO (RPH) 29 35 Mass Balance Productivity 2222 2222 (lb/lb) AshProductivity (lb/lb) 2941 2941 Ash (wt %) 0.034 0.049 Mw 102,610 118,520Mn 36,800 39,200 Mw/Mn 2.79 3.02 Precontactor Feed All 0.0028/0.00280.0028/0.0028 Metallocene Conc (Wt %) Metallocene Mixed Feed Wt. 0.4230.289 Ratio Precontactor Metallocene 0.2 0.21 A/I Feed (lbs/hr)Metallocene Feed (lbs/hr) 0.48 0.68

TABLE 8B Resin and Film Properties for Polyethylene Prepared Using aDual Metallocene Catalyst Comprising Compounds A + I, as Shown.

Ex. HLMI/ Dart Spencer MD TD No. Metallocene MI HLMI MI Density ImpactImpact tear tear Haze CY-a 11.1 A + I 1.09 20.8 19.1 0.917 688 0.65 242413 20.6 0.534 11.2 A + I 0.84 16.2 19.3 0.917 727 0.85 196 447 11.60.499

1. A catalyst composition comprising a first metallocene compound, asecond metallocene compound, at least one chemically-treated solidoxide, and at least one organoaluminum compound, wherein: a) the firstmetallocene compound has the following formula:(X¹)(X²)(X³)(X⁴)Zr; wherein (X¹) and (X²) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; wherein each substituent on (X¹) and (X²) isindependently selected from a linear or branched aliphatic group,wherein the aliphatic group is unsubstituted or substituted, any one ofwhich having from 1 to about 20 carbon atoms; wherein (X³), (X⁴), andany substituent on the substituted aliphatic group on (X¹) and (X²) areindependently selected from an aliphatic group, an aromatic group, acyclic group, a combination of aliphatic and cyclic groups, an oxygengroup, a sulfur group, a nitrogen group, a phosphorus group, an arsenicgroup, a carbon group, a silicon group, a germanium group, a tin group,a lead group, a boron group, an aluminum group, an inorganic group, anorganometallic group, or a substituted derivative thereof, any one ofwhich having from 1 to about 20 carbon atoms; a halide; or hydrogen; b)wherein the second metallocene compound has the following formula:(X¹)(X⁶)(X⁷)(X⁸)M;  wherein 1) M is Zr; (X⁵) and (X⁶) are independentlyselected from a substituted cyclopentadienyl, a substituted indenyl, asubstituted fluorenyl, or a substituted, partially saturated analogthereof, wherein at least one of (X⁵) and (X⁶) is at leastdisubstituted; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; 2) M is Zr; (X⁵) and (X⁶ ) areindependently selected from a cyclopentadienyl, an indenyl, a fluorenyl,a partially saturated analog thereof, or a substituted analog thereof;and (X⁵) and (X⁶) are connected by a substituted or unsubstitutedbridging group comprising from 3 to 5 contiguous ansa carbon atoms in achain, one end of which is bonded to (X⁵) and the other end of which isbonded to (X⁶); or 3) M is Hf; (X⁵) and (X⁶) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; and each substituent on (X⁵ ) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; and wherein (X⁷), (X⁸), any substituenton (X⁵), any substituent on (X⁶), any substituent on the substitutedaliphatic group on (X⁵) and (X⁶), and any substituent on the substitutedbridging group connecting (X⁵) and (X⁶) are independently selected froman aliphatic group, an aromatic group, a cyclic group, a combination ofaliphatic and cyclic groups, an oxygen group, a sulfur group, a nitrogengroup, a phosphorus group, an arsenic group, a carbon group, a silicongroup, a germanium group, a tin group, a lead group, a boron group, analuminum group, an inorganic group, an organometallic group, or asubstituted derivative thereof, any one of which having from 1 to about20 carbon atoms; a halide; or hydrogen; c) the chemically-treated solidoxide comprises a solid oxide treated with an electron-withdrawinganion; and d) the organoaluminum compound has the following formula:Al(X⁹)_(n)(X¹⁰)_(3-n); wherein (X⁹) is a hydrocarbyl having from 1 toabout 20 carbon atoms; (X¹⁰) is selected from alkoxide or aryloxidehaving from 1 to about 20 carbon atoms, halide, or hydride; and n is anumber from 1 to 3, inclusive.
 2. The catalyst composition of claim 1,wherein the second metallocene compound has the following formula:(X⁵)(X⁶)(X⁷)(X⁸)Zr;wherein (X⁵) and (X⁶) are independently selected froma substituted cyclopentadienyl, a substituted indenyl, a substitutedfluorenyl, or a substituted, partially saturated analog thereof, whereinat least one of (X⁵) and (X⁶) is at least disubstituted; wherein eachsubstituent on (X⁵) and (X⁶) is independently selected from a linear orbranched aliphatic group, wherein the aliphatic group is unsubstitutedor substituted, any one of which having from 1 to about 20 carbon atoms;wherein (X⁷), (X⁸), and any substituent on the substituted aliphaticgroup on (X⁵) and (X⁶) are independently selected from an aliphaticgroup, an aromatic group, a cyclic group, a combination of aliphatic andcyclic groups, an oxygen group, a sulfur group, a nitrogen group, aphosphorus group, an arsenic group, a carbon group, a silicon group, agermanium group, a tin group, a lead group, a boron group, an aluminumgroup, an inorganic group, an organometallic group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen.
 3. The catalyst composition of claim 2,wherein both (X⁵) and (X⁶) are at least disubstituted.
 4. The catalystcomposition of claim 2, wherein: a) the first metallocene compound hasthe formula (η⁵-C₅H₄R¹)₂ZrX¹¹ ₂, wherein R¹ in each instance isindependently selected from a linear or branched aliphatic group havingfrom 1 to about 20 carbon atoms, and wherein X¹¹ in each instance isindependently selected from F, Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr,O-n-Bu, O-t-Bu, NMe₂, or NEt₂; b) the second metallocene compound hasthe formula (η⁵-C₅H₃R¹ ₂)₂ZrX¹¹ ₂, wherein R¹ in each instance isindependently selected from a linear or branched aliphatic group havingfrom 1 to about 20 carbon atoms, and X¹¹ in each instance isindependently selected from F, Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr,O-n-Bu, O-t-Bu, NMe₂, or NEt₂; c) the chemically-treated solid oxide isselected from fluorided alumina, chlorided alumina, bromided alumina,sulfated alumina, fluorided silica-alumina, chlorided silica-alumina,bromided silica-alumina, sulfated silica-alumina, fluoridedsilica-zirconia, chlorided silica-zirconia, bromided silica-zirconia,sulfated silica-zirconia, or any combination thereof; and d) theorganoaluminum compound is selected from trimethylaluminum,triethylaluminum, tri-n-propylaluminum, diethylaluminum ethoxide,tri-n-butylaluminum, disobutylaluminum hydride, triisobutylaluminum,diethylaluminum chloride, or any combination thereof.
 5. The catalystcomposition of claim 2, wherein: a) the first metallocene compound hasthe formula (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂; b) the second metallocene compoundhas the formula (η⁵-C₅H₃ ^(n)BuR²)₂ZrCl₂, wherein R² is selected fromMe, Et, n-Pr, i-Pr, n-Bu, s-Bu, i-Bu, or t-Bu; c) the chemically-treatedsolid oxide is selected from fluorided alumina, chlorided alumina,sulfated alumina, fluorided silica-alumina, or any combination thereof;and d) the organoaluminum compound is selected from trimethylaluminum,triethylaluminum, tri-n-propylaluminum, diethylaluminum ethoxide,tri-n-butylaluminum, disobutylaluminum hydride, triisobutylaluminum,diethylaluminum chloride, or any combination thereof.
 6. The catalystcomposition of claim 2, wherein: a) the first metallocene compound hasthe formula (η⁵-C₅H₄ ^(n)Bu)₂ZrCl₂; b) the second metallocene compoundhas the formula (η⁵-C₅H₃ ^(n)BuMe)₂ZrCl₂; c) the chemically-treatedsolid oxide is selected from fluorided alumina, chlorided alumina,sulfated alumina, fluorided silica-alumina, or any combination thereof;and d) the organoaluminum compound is selected from triethylaluminum ortriisobutylaluminum.
 7. The catalyst composition of claim 1, wherein thesecond metallocene compound is an ansa-metallocene having the followingformula:(X⁵)(X⁶) (X⁷)(X⁸)Zr;wherein (X⁵) and (X⁶) are independently selectedfrom a cyclopentadienyl, an indenyl, a fluorenyl, a partially saturatedanalog thereof, or a substituted analog thereof; wherein (X⁵) and (X⁶)are connected by a substituted or unsubstituted bridging groupcomprising from 3 to 5 contiguous ansa carbon atoms in a chain, one endof which is bonded to (X⁵) and the other end of which is bonded to (X⁶);wherein (X⁷), (X⁸), any substituent on the substituted bridging groupconnecting (X⁵) and (X⁶), any substituent on (X⁵ ), and any substituenton (X⁶ ) are independently selected from an aliphatic group, an aromaticgroup, a cyclic group, a combination of aliphatic and cyclic groups, anoxygen group, a sulfur group, a nitrogen group, a phosphorus group, anarsenic group, a carbon group, a silicon group, a germanium group, a tingroup, a lead group, a boron group, an aluminum group, an inorganicgroup, an organometallic group, or a substituted derivative thereof, anyone of which having from 1 to about 20 carbon atoms; a halide; orhydrogen.
 8. The catalyst composition of claim 7, wherein a) the firstmetallocene compound has the formula (η⁵-C₅H₄R¹)₂ZrCl₂, wherein R¹ ineach instance is independently selected from a linear or branchedaliphatic group having from 1 to about 20 carbon atoms; b) the secondmetallocene compound is selected from[μ-CH₂(CH₂)_(n)CH₂](η⁵-9-C₁₃H₈)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-9-C₁₃H₁₆)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-1-C₉H₆)₂ZrX¹² ₂,[μ-CH₂(CH₂)_(n)CH₂](η⁵-1-C₉H₁₀)₂ZrX¹² ₂, or any combination thereof,wherein n is from 1 to 3, and wherein X¹², in each occurrence, isindependently selected from an aliphatic group, an aromatic group, analkoxide group, an aryloxide group, an alkylamide group, an arylamidegroup, a dialkylamide group, a diarylamide group, an alkyl arylamidegroup, an alkylthiolate group, an arylthiolate group, or a substitutedderivative thereof, any one of which having from 1 to about 20 carbonatoms; a halide; or hydrogen; c) the chemically-treated solid oxide isselected from fluorided alumina, chlorided alumina, bromided alumina,sulfated alumina, fluorided silica-alumina, chlorided silica-alumina,bromided silica-alumina, sulfated silica-alumina, fluoridedsilica-zirconia, chlorided silica-zirconia, bromided silica-zirconia,sulfated silica-zirconia, or any combination thereof; and d) theorganoaluminum compound is selected from trimethylaluminum,triethylaluminum, tri-n-propylaluminum, diethylaluminum ethoxide,tri-n-butylaluminum, disobutylaluminum hydride, triisobutylaluminum,diethylaluminum chloride, or any combination thereof.
 9. The catalystcomposition of claim 8, wherein X¹² is independently selected from F,Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr, O-n-Bu, O-t-Bu, NMe₂, or NEt₂. 10.The catalyst composition of claim 7, wherein: a) the first metallocenecompound has the following formula (η⁵-C₅H₄R¹)₂ZrCl₂, wherein R¹ in eachinstance is independently selected from a linear or branched aliphatichaving from 1 to about 20 carbon atoms; and b) the second metallocenecompound is selected from: 1,3-propanediylbis(η⁵-9-fluorenyl)zirconiumdichloride; 1,4-butanediylbis(η⁵-9-fluorenyl)zirconium dichloride;1,5-pentanediylbis(η⁵-9-fluorenyl)zirconium dichloride;1,3-propanediylbis(η⁵-1-indenyl)zirconium dichloride;1,4-butanediylbis(η⁵-1-indenyl)zirconium dichloride;1,5-pentanediylbis(η⁵-1-indenyl)zirconium dichloride;1,3-propanediylbis(η⁵-9-fluorenyl)di-n-butoxyzirconium;1,4-butanediylbis(η⁵-9-fluorenyl)di-n-butoxyzirconium;1,5-pentanediylbis(η⁵-9-fluorenyl)di-n-butoxyzirconium;1,3-propanediylbis(η⁵-1-indenyl)di-n-butoxyzirconium;1,4-butanediylbis(η⁵-1-indenyl)di-n-butoxyzirconium;1,5-pentanediylbis(η⁵-1-indenyl)di-n-butoxyzirconium;1,3-propanediylbis(η⁵-9-fluorenyl)zirconium dimethyl;1,4-butanediylbis(η⁵-9-fluorenyl)zirconium dimethyl;1,5-pentanediylbis(η⁵-9-fluorenyl)zirconium dimethyl;1,3-propanediylbis(η⁵-1-indenyl)zirconium dimethyl;1,4-butanediylbis(η⁵-1-indenyl)zirconium dimethyl;1,5-pentanediylbis(η⁵-1-indenyl)zirconium dimethyl; or any combinationthereof; c) the chemically-treated solid oxide is selected fromfluorided alumina, chlorided alumina, sulfated alumina, fluoridedsilica-alumina, or any combination thereof; and d) the organoaluminumcompound is selected from triethylaluminum or triisobutylaluminum. 11.The catalyst composition of claim 1, wherein the second metallocenecompound has the following formula:(X⁵)(X⁶)(X⁷)(X⁸)Hf;wherein (X⁵) and (X⁶) are independently selected froma monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; wherein each substituent on (X⁵) and (X⁶) isindependently selected from a linear or branched aliphatic group,wherein the aliphatic group is unsubstituted or substituted, any one ofwhich having from 1 to about 20 carbon atoms; wherein (X⁷), (X⁸), andany substituent on the substituted aliphatic group on (X⁵) and (X⁶) areindependently selected from an aliphatic group, an aromatic group, acyclic group, a combination of aliphatic and cyclic groups, an oxygengroup, a sulfur group, a nitrogen group, a phosphorus group, an arsenicgroup, a carbon group, a silicon group, a germanium group, a tin group,a lead group, a boron group, an aluminum group, an inorganic group, anorganometallic group, or a substituted derivative thereof, any one ofwhich having from 1 to about 20 carbon atoms; a halide; or hydrogen. 12.The catalyst composition of claim 11, wherein: a) the first metallocenecompound has the following formula (η⁵-C₅H₄R¹)₂ZrX¹¹ ₂, wherein R¹ ineach instance is independently selected from a linear or branchedaliphatic group having from 1 to about 20 carbon atoms, and X¹¹ isindependently selected from F, Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr,O-n-Bu, O-t-Bu, NMe₂, or NEt₂; b) the second metallocene compound hasthe following formula (η⁵-C₅H₄R¹)₂HfX¹¹ ₂, wherein R¹ in each instanceis independently selected from a linear or branched aliphatic grouphaving from 1 to about 20 carbon atoms, and X¹¹ is independentlyselected from F, Cl, Br, I, OMe, OEt, O-n-Pr, O-i-Pr, O-n-Bu, O-t-Bu,NMe₂, or NEt₂; c) the chemically-treated solid oxide is selected fromfluorided alumina, chlorided alumina, sulfated alumina, fluoridedsilica-alumina, chlorided silica-alumina, sulfated silica-alumina, orany combination thereof; and d) the organoaluminum compound is selectedfrom trimethylaluminum, triethylaluminum, tri-n-propylaluminum,diethylaluminum ethoxide, tri-n-butylaluminum, disobutylaluminumhydride, triisobutylaluminum, diethylaluminum chloride, or anycombination thereof.
 13. The catalyst composition of claim 11, wherein:a) the first metallocene compound has the formula (η⁵-C₅H₄^(n)Bu)₂ZrCl₂; b) the second metallocene compound has the formula(η⁵-C₅H₄ ^(n)Bu)₂HfCl₂; c) the chemically-treated solid oxide isselected from fluorided alumina, chlorided alumina, sulfated alumina,fluorided silica-alumina, or any combination thereof; and d) theorganoaluminum compound is selected from trimethylaluminum,triethylaluminum, tri-n-propylaluminum, diethylaluminum ethoxide,tri-n-butylaluminum, disobutylaluminum hydride, triisobutylaluminum,diethylaluminum chloride, or any combination thereof.
 14. The catalystcomposition of claim 1, wherein the chemically-treated solid oxidecomprises a solid oxide treated with an electron-withdrawing anion,wherein the solid oxide is selected from silica, alumina,silica-alumina, aluminum phosphate, heteropolytungstates, titania,zirconia, magnesia, boria, zinc oxide, mixed oxides thereof, or mixturesthereof; and the electron-withdrawing anion is selected from fluoride,chloride, bromide, phosphate, triflate, bisulfate, sulfate, or anycombination thereof.
 15. The catalyst composition of claim 1, whereinthe chemically-treated solid oxide is selected from fluorided alumina,chlorided alumina, bromided alumina, sulfated alumina, fluoridedsilica-alumina, chlorided silica-alumina, bromided silica-alumina,sulfated silica-alumina, fluorided silica-zirconia, chloridedsilica-zirconia, bromided silica-zirconia, sulfated silica-zirconia, orany combination thereof.
 16. The catalyst composition of claim 1,wherein the chemically-treated solid oxide further comprises a metal ormetal ion selected from zinc, nickel, vanadium, silver, copper, gallium,tin, tungsten, molybdenum, or any combination thereof.
 17. The catalystcomposition of claim 1, wherein the chemically-treated solid oxidefurther comprises a metal or metal ion and is selected fromzinc-impregnated chlorided alumina, zinc-impregnated fluorided alumina,zinc-impregnated chlorided silica-alumina, zinc-impregnated fluoridedsilica-alumina, zinc-impregnated sulfated alumina, or any combinationthereof.
 18. The catalyst composition of claim 1, wherein the weightratio of the organoalumium compound to the chemically-treated solidoxide is from about 10:1 to about 1:1,000.
 19. The catalyst compositionof claim 1, wherein the organoaluminum compound is selected fromtrimethylaluminum, triethylaluminum, tripropylaluminum, diethylaluminumethoxide, tributylaluminum, disobutylaluminum hydride,triisobutylaluminum, or diethylaluminum chloride.
 20. The catalystcomposition of claim 1, further comprising an optional cocatalystselected from at least one aluminoxane, at least one organozinccompound, at least one organoboron compound, at least one ionizing ioniccompound, or any combination thereof.
 21. The catalyst composition ofclaim 1, further comprising an optional cocatalyst selected from atleast one aluminoxane compound, wherein the aluminoxane comprises acyclic aluminoxane having the formula:

R is a linear or branched alkyl having from 1 to 10 carbon atoms, and nis an integer from 3 to about 10; a linear aluminoxane having theformula:

R is a linear or branched alkyl having from 1 to 10 carbon atoms, and nis an integer from 1 to about 50; a cage aluminoxane having the formulaR^(t) _(5m+α)R^(b) _(m−α)Al_(4m)O_(3m), wherein m is 3 or 4 and α is=n_(Al(3))−n_(O(2))+n_(O(4)); wherein n_(Al(3)) is the number of threecoordinate aluminum atoms, n_(O(2)) is the number of two coordinateoxygen atoms, n_(O(4)) is the number of 4 coordinate oxygen atoms, R^(t)represents a terminal alkyl group, and R^(b) represents a bridging alkylgroup; wherein R is a linear or branched alkyl having from 1 to 10carbon atoms; or any combination thereof.
 22. The catalyst compositionof claim 21, wherein the molar ratio of the aluminum in the aluminoxaneto the combined first metallocene compound and second metallocenecompound in the catalyst composition is from about 1:10 to about100,000:1.
 23. The catalyst composition of claim 21, wherein thealuminoxane compound is selected from methylaluminoxane,ethylaluminoxane, n-propylaluminoxane, iso-propylaluminoxane,n-butylaluminoxane, t-butyl-aluminoxane, sec-butylaluminoxane,iso-butylaluminoxane, 1-pentylaluminoxane, 2-pentylaluminoxane,3-pentylaluminoxane, iso-pentylaluminoxane, neopentylaluminoxane, or acombination thereof.
 24. The catalyst composition of claim 1, furthercomprising an optional cocatalyst selected from at least one organozinccompound, wherein the organozinc compound has the following formula:Zn(X¹³)(X¹⁴); wherein (X¹³) is a hydrocarbyl having from 1 to about 20carbon atoms; (X¹⁴) is selected from a hydrocarbyl, an alkoxide or anaryloxide having from 1 to about 20 carbon atoms, halide, or hydride;25. The catalyst composition of claim 1, further comprising an optionalcocatalyst selected from at least one organozinc compound, wherein theorganozinc compound is selected from dimethylzinc, diethylzinc,dipropylzinc, dibutylzinc, dineopentylzinc,di(trimethylsilylmethyl)zinc, or any combination thereof.
 26. Thecatalyst composition of claim 1, further comprising an optionalcocatalyst selected from at least one organoboron compound, wherein theorganoboron compound is selected from tris(pentafluorophenyl)boron,tris[3,5-bis(trifluoromethyl)phenyl]boron, N,N-dimethylaniliniumtetrakis(pentafluorophenyl)borate, triphenylcarbeniumtetrakis(pentafluorophenyl)borate, lithiumtetrakis(pentafluorophenyl)borate, N,N-dimethylaniliniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbeniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, or a combinationthereof.
 27. The catalyst composition of claim 26, wherein the molarratio of the organoboron compound to the combined first metallocenecompound and second metallocene compound in the catalyst composition isfrom about 0.1:1 to about 10:1.
 28. The catalyst composition of claim 1,further comprising an optional cocatalyst selected from at least oneionizing ionic compound, wherein the ionizing ionic compound is selectedfrom tri(n-butyl)ammonium tetrakis(p-tolyl)borate, tri(n-butyl)ammoniumtetrakis(m-tolyl)borate, tri(n-butyl)ammoniumtetrakis(2,4-dimethyl)borate, tri(n-butyl)ammoniumtetrakis(3,5-dimethylphenyl)borate, tri(n-butyl)ammoniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tri(n-butyl)ammoniumtetrakis(pentafluorophenyl)borate, N,N-dimethylaniliniumtetrakis(p-tolyl)borate, N,N-dimethylanilinium tetrakis(m-tolyl)borate,N,N-dimethylanilinium tetrakis(2,4-dimethylphenyl)borate,N,N-dimethylanilinium tetrakis(3,5-dimethylphenyl)borate,N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate,N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate,triphenylcarbenium tetrakis(p-tolyl)borate, triphenylcarbeniumtetrakis(m-tolyl)borate, triphenylcarbeniumtetrakis(2,4-dimethylphenyl)borate, triphenylcarbeniumtetrakis(3,5-dimethylphenyl)borate, triphenylcarbeniumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, triphenylcarbeniumtetrakis(pentafluorophenyl)borate, tropylium tetrakis(p-tolyl)borate,tropylium tetrakis(m-tolyl)borate, tropyliumtetrakis(2,4-dimethylphenyl)borate, tropyliumtetrakis(3,5-dimethylphenyl)borate, tropyliumtetrakis[3,5-bis(trifluoromethyl)phenyl]borate, tropyliumtetrakis(pentafluorophenyl)borate, lithiumtetrakis(pentafluorophenyl)borate, lithium tetrakis(phenyl)borate,lithium tetrakis(p-tolyl)borate, lithium tetrakis(m-tolyl)borate,lithium tetrakis(2,4-dimethylphenyl)borate, lithiumtetrakis(3,5-dimethylphenyl)borate, lithium tetrafluoroborate, sodiumtetrakis(pentafluorophenyl)borate, sodium tetrakis(phenyl) borate,sodium tetrakis(p-tolyl)borate, sodium tetrakis(m-tolyl)borate, sodiumtetrakis(2,4-dimethylphenyl)borate, sodiumtetrakis(3,5-dimethylphenyl)borate, sodium tetrafluoroborate, potassiumtetrakis(pentafluorophenyl)borate, potassium tetrakis(phenyl)borate,potassium tetrakis(p-tolyl)borate, potassium tetrakis(m-tolyl)borate,potassium tetrakis(2,4-dimethylphenyl)borate, potassiumtetrakis(3,5-dimethylphenyl)borate, potassium tetrafluoroborate,tri(n-butyl)ammonium tetrakis(p-tolyl)aluminate, tri(n-butyl)ammoniumtetrakis(m-tolyl)aluminate, tri(n-butyl)ammoniumtetrakis(2,4-dimethyl)aluminate, tri(n-butyl)ammoniumtetrakis(3,5-dimethylphenyl)aluminate, tri(n-butyl)ammoniumtetrakis(pentafluorophenyl)aluminate, N,N-dimethylaniliniumtetrakis(p-tolyl)aluminate, N,N-dimethylaniliniumtetrakis(m-tolyl)aluminate, N,N-dimethylaniliniumtetrakis(2,4-dimethylphenyl)aluminate, N,N-dimethylaniliniumtetrakis(3,5-dimethylphenyl)aluminate, N,N-dimethylanilinium tetrakis(pentafluorophenyl)aluminate, triphenylcarbeniumtetrakis(p-tolyl)aluminate, triphenylcarbeniumtetrakis(m-tolyl)aluminate, triphenylcarbeniumtetrakis(2,4-dimethylphenyl)aluminate, triphenylcarbeniumtetrakis(3,5-dimethylphenyl)aluminate, triphenylcarbeniumtetrakis(pentafluorophenyl)aluminate, tropyliumtetrakis(p-tolyl)aluminate, tropylium tetrakis(m-tolyl)aluminate,tropylium tetrakis(2,4-dimethylphenyl)aluminate, tropyliumtetrakis(3,5-dimethylphenyl)aluminate, tropyliumtetrakis(pentafluorophenyl)aluminate, lithiumtetrakis(pentafluorophenyl)aluminate, lithium tetrakis(phenyl)aluminate,lithium tetrakis(p-tolyl)aluminate, lithium tetrakis(m-tolyl)aluminate,lithium tetrakis(2,4-dimethylphenyl)aluminate, lithiumtetrakis(3,5-dimethylphenyl)aluminate, lithium tetrafluoroaluminate,sodium tetrakis(pentafluorophenyl)aluminate, sodiumtetrakis(phenyl)aluminate, sodium tetrakis(p-tolyl)aluminate, sodiumtetrakis(m-tolyl)aluminate, sodiumtetrakis(2,4-dimethylphenyl)aluminate, sodiumtetrakis(3,5-dimethylphenyl)aluminate, sodium tetrafluoroaluminate,potassium tetrakis(pentafluorophenyl)aluminate, potassiumtetrakis(phenyl)aluminate, potassium tetrakis(p-tolyl)aluminate,potassium tetrakis(m-tolyl)aluminate, potassiumtetrakis(2,4-dimethylphenyl)aluminate, potassium tetrakis(3,5-dimethylphenyl)aluminate, potassium tetrafluoroaluminate, or anycombination thereof.
 29. A catalyst composition consisting essentiallyof a first metallocene compound, a second metallocene compound, at leastone chemically-treated solid oxide, and at least one organoaluminumcompound, wherein: a) the first metallocene compound has the followingformula:(X¹)(X²)(X³)(X⁴ )Zr; wherein (X¹) and (X²) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; wherein each substituent on (X¹) and (X²) isindependently selected from a linear or branched aliphatic group,wherein the aliphatic group is unsubstituted or substituted, any one ofwhich having from 1 to about 20 carbon atoms; wherein (X³), (X⁴), andany substituent on the substituted aliphatic group on (X¹) and (X²) areindependently selected from an aliphatic group, an aromatic group, acyclic group, a combination of aliphatic and cyclic groups, an oxygengroup, a sulfur group, a nitrogen group, a phosphorus group, an arsenicgroup, a carbon group, a silicon group, a germanium group, a tin group,a lead group, a boron group, an aluminum group, an inorganic group, anorganometallic group, or a substituted derivative thereof, any one ofwhich having from 1 to about 20 carbon atoms; a halide; or hydrogen; b)wherein the second metallocene compound has the following formula:(X⁵)(X⁶)(X⁷)(X⁸)M;  wherein 1) M is Zr; (X⁵) and (X⁶) are independentlyselected from a substituted cyclopentadienyl, a substituted indenyl, asubstituted fluorenyl, or a substituted, partially saturated analogthereof, wherein at least one of (X⁵) and (X⁶) is at leastdisubstituted; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; 2) M is Zr; (X⁵) and (X⁶) areindependently selected from a cyclopentadienyl, an indenyl, a fluorenyl,a partially saturated analog thereof, or a substituted analog thereofand (X⁵) and (X⁶) are connected by a substituted or unsubstitutedbridging group comprising from 3 to 5 contiguous ansa carbon atoms in achain, one end of which is bonded to (X⁵) and the other end of which isbonded to (X⁶); or 3) M is Hf; (X⁵) and (X⁶) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; and wherein (X⁷), (X⁸), any substituenton (X⁵), any substituent on (X⁶), any substituent on the substitutedaliphatic group on (X⁵) and (X⁶), and any substituent on the substitutedbridging group connecting (X⁵) and (X⁶) are independently selected froman aliphatic group, an aromatic group, a cyclic group, a combination ofaliphatic and cyclic groups, an oxygen group, a sulfur group, a nitrogengroup, a phosphorus group, an arsenic group, a carbon group, a silicongroup, a germanium group, a tin group, a lead group, a boron group, analuminum group, an inorganic group, an organometallic group, or asubstituted derivative thereof, any one of which having from 1 to about20 carbon atoms; a halide; or hydrogen; c) the chemically-treated solidoxide comprises a solid oxide treated with an electron-withdrawinganion; and d) the organoaluminum compound has the following formula:Al(X⁹)_(n)(X¹⁰)_(3-n); wherein (X⁹) is a hydrocarbyl having from 1 toabout 20 carbon atoms; (X¹⁰) is selected from alkoxide or aryloxidehaving from 1 to about 20 carbon atoms, halide, or hydride; and n is anumber from 1 to 3, inclusive.
 30. A catalyst composition comprising thecontact product of a first metallocene compound, a second metallocenecompound, at least one chemically-treated solid oxide, and at least oneorganoaluminum compound, wherein: a) the first metallocene compound hasthe following formula:(X¹)(X²)(X³)(X⁴)Zr; wherein (X¹) and (X²) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; wherein each substituent on (X¹) and (X²) isindependently selected from a linear or branched aliphatic group,wherein the aliphatic group is unsubstituted or substituted, any one ofwhich having from 1 to about 20 carbon atoms; wherein (X³), (X⁴), andany substituent on the substituted aliphatic group on (X¹) and (X²) areindependently selected from an aliphatic group, an aromatic group, acyclic group, a combination of aliphatic and cyclic groups, an oxygengroup, a sulfur group, a nitrogen group, a phosphorus group, an arsenicgroup, a carbon group, a silicon group, a germanium group, a tin group,a lead group, a boron group, an aluminum group, an inorganic group, anorganometallic group, or a substituted derivative thereof, any one ofwhich having from 1 to about 20 carbon atoms; a halide; or hydrogen; b)wherein the second metallocene compound has the following formula:(X⁵)(X⁶)(X⁷)(X⁸)M;  wherein 1) M is Zr; (X⁵) and (X⁶) are independentlyselected from a substituted cyclopentadienyl, a substituted indenyl, asubstituted fluorenyl, or a substituted, partially saturated analogthereof, wherein at least one of (X⁵) and (X⁶) is at leastdisubstituted; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; 2) M is Zr; (X⁵) and (X⁶ ) areindependently selected from a cyclopentadienyl, an indenyl, a fluorenyl,a partially saturated analog thereof, or a substituted analog thereof;and (X⁵) and (X⁶) are connected by a substituted or unsubstitutedbridging group comprising from 3 to 5 contiguous ansa carbon atoms in achain, one end of which is bonded to (X⁵) and the other end of which isbonded to (X⁶); or 3) M is Hf; (X⁵) and (X⁶) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; and wherein (X⁷), (X⁸), any substituenton (X⁵), any substituent on (X⁶), any substituent on the substitutedaliphatic group on (X⁵) and (X⁶), and any substituent on the substitutedbridging group connecting (X⁵) and (X⁶) are independently selected froman aliphatic group, an aromatic group, a cyclic group, a combination ofaliphatic and cyclic groups, an oxygen group, a sulfur group, a nitrogengroup, a phosphorus group, an arsenic group, a carbon group, a silicongroup, a germanium group, a tin group, a lead group, a boron group, analuminum group, an inorganic group, an organometallic group, or asubstituted derivative thereof, any one of which having from 1 to about20 carbon atoms; a halide; or hydrogen; c) the chemically-treated solidoxide comprises a solid oxide treated with an electron-withdrawinganion; and d) the organoaluminum compound has the following formula:Al(X⁹)_(n)(X¹⁰)_(3-n); wherein (X⁹) is a hydrocarbyl having from 1 toabout 20 carbon atoms; (X¹⁰) is selected from alkoxide or aryloxidehaving from 1 to about 20 carbon atoms, halide, or hydride; and n is anumber from 1 to 3, inclusive.
 31. A process to produce a catalystcomposition comprising contacting a first metallocene compound, a secondmetallocene compound, at least one chemically-treated solid oxide, andat least one organoaluminum compound, wherein: a) the first metallocenecompound has the following formula:(X¹)(X²)(X³)(X⁴)Zr; wherein (X¹) and (X²) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; wherein each substituent on (X¹) and (X²) isindependently selected from a linear or branched aliphatic group,wherein the aliphatic group is unsubstituted or substituted, any one ofwhich having from 1 to about 20 carbon atoms; wherein (X³), (X⁴), andany substituent on the substituted aliphatic group on (X¹) and (X²) areindependently selected from an aliphatic group, an aromatic group, acyclic group, a combination of aliphatic and cyclic groups, an oxygengroup, a sulfur group, a nitrogen group, a phosphorus group, an arsenicgroup, a carbon group, a silicon group, a germanium group, a tin group,a lead group, a boron group, an aluminum group, an inorganic group, anorganometallic group, or a substituted derivative thereof, any one ofwhich having from 1 to about 20 carbon atoms; a halide; or hydrogen; b)wherein the second metallocene compound has the following formula:(X⁵)(X⁶)(X⁷)(X⁸)M;  wherein 1) M is Zr; (X⁵) and (X⁶ ) are independentlyselected from a substituted cyclopentadienyl, a substituted indenyl, asubstituted fluorenyl, or a substituted, partially saturated analogthereof, wherein at least one of (X⁵) and (X⁶) is at leastdisubstituted; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; 2) M is Zr; (X⁵) and (X⁶) areindependently selected from a cyclopentadienyl, an indenyl, a fluorenyl,a partially saturated analog thereof, or a substituted analog thereof;and (X⁵) and (X⁶) are connected by a substituted or unsubstitutedbridging group comprising from 3 to 5 contiguous ansa carbon atoms in achain, one end of which is bonded to (X⁵) and the other end of which isbonded to (X⁶); or 3) M is Hf; (X⁵) and (X⁶ ) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; and wherein (X⁷), (X⁸), any substituenton (X⁵), any substituent on (X⁶), any substituent on the substitutedaliphatic group on (X⁵) and (X⁶), and any substituent on the substitutedbridging group connecting (X⁵) and (X⁶) are independently selected froman aliphatic group, an aromatic group, a cyclic group, a combination ofaliphatic and cyclic groups, an oxygen group, a sulfur group, a nitrogengroup, a phosphorus group, an arsenic group, a carbon group, a silicongroup, a germanium group, a tin group, a lead group, a boron group, analuminum group, an inorganic group, an organometallic group, or asubstituted derivative thereof, any one of which having from 1 to about20 carbon atoms; a halide; or hydrogen; c) the chemically-treated solidoxide comprises a solid oxide treated with an electron-withdrawinganion; and d) the organoaluminum compound has the following formula:Al(X⁹)_(n)(X¹⁰)_(3-n); wherein (X⁹) is a hydrocarbyl having from 1 toabout 20 carbon atoms; (X¹⁰) is selected from alkoxide or aryloxidehaving from 1 to about 20 carbon atoms, halide, or hydride; and n is anumber from 1 to 3, inclusive.
 32. A process for polymerizing olefins inthe presence of a catalyst composition, comprising contacting thecatalyst composition with at least one type of olefin monomer, whereinthe catalyst composition comprises a first metallocene compound, asecond metallocene compound, at least one chemically-treated solidoxide, and at least one organoaluminum compound, wherein: a) the firstmetallocene compound has the following formula:(X¹)(X²)(X³)(X⁴)Zr; wherein (X¹) and (X²) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; wherein each substituent on (X¹) and (X²) isindependently selected from a linear or branched aliphatic group,wherein the aliphatic group is unsubstituted or substituted, any one ofwhich having from 1 to about 20 carbon atoms; wherein (X³), (X⁴), andany substituent on the substituted aliphatic group on (X¹) and (X²) areindependently selected from an aliphatic group, an aromatic group, acyclic group, a combination of aliphatic and cyclic groups, an oxygengroup, a sulfur group, a nitrogen group, a phosphorus group, an arsenicgroup, a carbon group, a silicon group, a germanium group, a tin group,a lead group, a boron group, an aluminum group, an inorganic group, anorganometallic group, or a substituted derivative thereof, any one ofwhich having from 1 to about 20 carbon atoms; a halide; or hydrogen; b)wherein the second metallocene compound has the following formula:(X⁵)(X⁶)(X⁷)(X⁹)M;  wherein 1) M is Zr; (X⁵) and (X⁶ ) are independentlyselected from a substituted cyclopentadienyl, a substituted indenyl, asubstituted fluorenyl, or a substituted, partially saturated analogthereof, wherein at least one of (X⁵) and (X⁶) is at leastdisubstituted; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; 2) M is Zr; (X⁵) and (X⁶) areindependently selected from a cyclopentadienyl, an indenyl, a fluorenyl,a partially saturated analog thereof, or a substituted analog thereof;and (X⁵) and (X⁶ ) are connected by a substituted or unsubstitutedbridging group comprising from 3 to 5 contiguous ansa carbon atoms in achain, one end of which is bonded to (X⁵) and the other end of which isbonded to (X⁶); or 3) M is Hf; (X⁵) and (X⁶) are independently selectedfrom a monosubstituted cyclopentadienyl, a monosubstituted indenyl, amonosubstituted fluorenyl, or a monosubstituted, partially saturatedanalog thereof; and each substituent on (X⁵) and (X⁶) is independentlyselected from a linear or branched aliphatic group, wherein thealiphatic group is unsubstituted or substituted, any one of which havingfrom 1 to about 20 carbon atoms; and wherein (X⁷), (X⁸), any substituenton (X⁵), any substituent on (X⁶), any substituent on the substitutedaliphatic group on (X⁵) and (X⁶), and any substituent on the substitutedbridging group connecting (X⁵) and (X⁶) are independently selected froman aliphatic group, an aromatic group, a cyclic group, a combination ofaliphatic and cyclic groups, an oxygen group, a sulfur group, a nitrogengroup, a phosphorus group, an arsenic group, a carbon group, a silicongroup, a germanium group, a tin group, a lead group, a boron group, analuminum group, an inorganic group, an organometallic group, or asubstituted derivative thereof, any one of which having from 1 to about20 carbon atoms; a halide; or hydrogen; c) the chemically-treated solidoxide comprises a solid oxide treated with an electron-withdrawinganion; and d) the organoaluminum compound has the following formula:Al(X⁹)_(n)(X¹⁰)_(3-n); wherein (X⁹) is a hydrocarbyl having from 1 toabout 20 carbon atoms; (X¹⁰) is selected from alkoxide or aryloxidehaving from 1 to about 20 carbon atoms, halide, or hydride; and n is anumber from 1 to 3, inclusive.
 33. The process of claim 32, wherein thecatalyst composition is contacted with ethylene and at least one otherolefin selected from 1-butene, 2-butene, 3-methyl-1-butene, isobutylene,1-pentene, 2-pentene, 3-methyl-1-pentene, 4-methyl-1-pentene, 1-hexene,2-hexene, 3-hexene, 3-ethyl-1-hexene, 1-heptene, 2-heptene, or3-heptene.
 34. The process of claim 32, wherein the catalyst compositionis contacted with ethylene and 1 -hexene.
 35. The process of claim 32,wherein the catalyst composition is contacted with ethylene.
 36. Apolymer or copolymer of ethylene, wherein the melt index is from about0.3 to about 2.0 dg/min; the density from about 0.94 to about 0.91g/cm³; the CY-a parameter is from about 0.45 to about 0.70; thepolydispersity index (M_(w)/M_(n)) is from about 2 to about 6; theHLMI/MI ratio is from about 16.5 to about 25; the Elmendorf MD tearresistance is greater than about 150 g for 1 mil blown film; theElmendorf TD tear resistance is greater than about 350 g for a 1 milblown film; the film haze is less than about 25% for a 1 mil blown film;the Dart impact strength is greater than about 600 g for a 1 mil blownfilm; and the Spencer impact strength is greater than about 0.7 J for a1 mil blown film.
 37. A polymer or copolymer of ethylene, wherein themelt index is from about 0.5 to about 1.5 dg/min; the density is fromabout 0.935 to about 0.915 g/cm³; the CY-a parameter is from about 0.50to about 0.65; the polydispersity index (M_(w)/M_(n)) is from about 2.2to about 5.0; the HLMI/MI ratio is from about 17 to about 24; theElmendorf MD tear resistance is greater than about 200 g for a 1 milblown film; the Elmendorf TD tear resistance is greater than about 380 gfor a 1 mil blown film; the film haze is less than about 15% for a 1 milblown film; the Dart impact strength is greater than about 800 g for a 1mil blown film; and the Spencer impact strength is greater than about0.9 J for a 1 mil blown film.
 38. A polymer or copolymer of ethylene,wherein the melt index is from about 0.8 to about 1.3 dg/min; thedensity is from about 0.925 to about 0.915 g/cm³; the CY-a parameter isfrom about 0.55 to about 0.62; the polydispersity index (M_(w)/M_(n)) isfrom about 2.6 to about 4.0; the HLMI/MI ratio is from about 17.5 toabout 23; the Elmendorf MD tear resistance is greater than about 250 gfor a 1 mil blown film; the Elmendorf TD tear resistance is greater thanabout 450 g for a 1 mil blown film; the film haze is less than about 10%for a 1 mil blown film; the Dart impact strength is greater than about1200 g for a 1 mil blown film; and the Spencer impact strength isgreater than about 1.00 J for a 1 mil blown film.